DESCRIPTION:
BRIEF SUMMARY
The present invention relates to a method for producing decorative glass objects in which the decoration is created by clear pearls formed by air bubbles within solid glass and/or by a pattern essentially formed by streaks on the outer surface of the glass.
Glass with bubbles has previously been produced either by using sodium carbonate or by boiling molten glass in a furnace before starting the production in order to produce blisters. However, when using these methods, the outcome has not been controllable but has been rather random, which has resulted in an extremely high waste percentage. Moreover, these methods have only been applicable to manual glass-making.
The use of sodium carbonate has resulted in too big bubbles or too small bubbles appearing as a dim impurity in the glass. Bubbles produced during boiling as well as by using sodium carbonate remain on the outer and inner surfaces of the objects, which thus become fragile.
The accompanying drawing illustrates some applications of the invention.
FIG. 1 is a front view of a length cut off from a cylindrical, solid glass object.
FIG. 2 shows the same in cross-section. Inside the glass object there are blisters or pearls 1 of different sizes and on the surface streaks 2 to a small extent.
FIG. 3 illustrates a stem glass provided with a solid stem 3 made by means of the method according to the invention and having blisters 4 inside and streaks 5 on the outer surface. To this stem 3 has been secured by blowing a bowl 6 made simultaneously therewith.
FIG. 4 is a front view of a drinking glass provided with a solid stem portion 7 made by means of the method according to the invention and with a bowl portion 8 produced simultaneously therewith and secured thereto by blowing. The stem portion is provided with blisters 9 and streaks 10.
By means of the method according to the invention fully clear pearls can be produced within the glass. The variable size of the pearls and their "arbitrary" grouping create a strong impression of beauty resembling the overall impression given by the Archipelago Sea, for which reason the method according to the invention is called the "Arkipelago" method.
By means of the method it is also possible to provide the outer surface of glass with a pattern mainly consisting of streaks. Both the pattern and the blisters formed by pearls are fully controllable. The proportions of both the pattern and the blisters can each be separately increased or reduced, the extreme cases essentially comprising blisters only or essentially pattern only (blisters always appear to some extent).
According to the invention, molten glass is poured in the shape of a band either mechanically or manually from above into a hot mould whereby the glass is spread into the mould in layers between which microscopic air bubbles remain. The temperature of the mould is lower than the temperature of the glass melt poured whereby, as the glass surface cools, the core still remains hot and the air enclosed within the bubbles expands in the still molten glass which, while slowly cooling, leaves the bubbles as clear pearls inside the glass. As the molten glass is spread in layers towards the wall of the mould, a pattern (for example, comprising streaks) is formed as the glass surface cools.
In connection with the invention, it has been found that, in order to produce satisfactory blisters and a satisfactory pattern, the molten glass must be poured in the shape of a band into the moulds from a relatively high level. A level of about 50 to 70 cm has proved to be advantageous. Within this range, a wide control of both the blisters and the pattern is possible. If a lower level is used, there will be less blisters and less pattern and, when pouring the molten glass from a level right above the mould, the effect according to the invention will no longer be obtained.
In addition to the pouring level, the blisters and the pattern can also be controlled by means of the quantity of molten glass poured. The bigger the quantity of molten glass poured per unit of time is, the smalle
REFERENCES:
patent: 1311474 (1919-07-01), Wadsworth
patent: 1715130 (1929-05-01), Haley
patent: 1816045 (1931-07-01), Haley
patent: 2596990 (1952-05-01), Doyle
patent: 3245770 (1966-04-01), Cortright et al.
LandOfFree
Method for producing decorative glass objects does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for producing decorative glass objects, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for producing decorative glass objects will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-1580887