ABSTRACT:
BACKGROUND OF THE INVENTION
(1) Field of the Invention
This invention relates to a method for producing a tin-nickel alloy film, particularly a method for producing a tin-nickel alloy film for decorative purposes.
(2) Description of the prior art
Recently, attention has been paid to a tin-nickel alloy film to replace a decorative chromium plating film. Although the chromium plating film has some excellent properties such as wear-resistance and corrosion-resistance, it is strictly restricted in use because it has harmful element, Cr for environment. The use of the chromium plating film would be more severely restricted in future. Therefore, the tin-nickel alloy film would play very important roles in the future instead of the chromium plating film.
In the past, the tin-nickel film would be produced from a given water solution by alloy-electroplating, and thus, two different metals, tin and nickel, must be electroplated at the same voltage. Then, all kinds of things to perform the electroplating at the same voltage have been carried out. Moreover, chemical species to be used have been restricted, and anti-environmental additives have been used.
Furthermore, the above electroplated tin-nickel film from the water solution always has a non-equilibrium NiSn phase which is not recognized in its equilibrium diagram. The NiSn phase often shifts to another stable phase due to the wear or the heating in the use of the tin-nickel alloy film, and thus, the properties of the tin-nickel alloy film often change. Therefore, the functions given to the tin-nickel alloy film for predetermined purposes may change during the use of the film, so that it may be that the tin-nickel alloy film can not exhibit the predetermined functions.
In the above case, various modifications in electroplating condition and additives have been performed for preventing the occurrence of the unstable NiSn phase, but can not generate another stable phase except the unstable NiSn phase.
SUMMERY OF THE INVENTION
It is an object of the present invention to provide a method for producing a stable tin-nickel alloy film not including the non-equilibrium NiSn phase.
For achieving the above object, this invention relates to a method for producing a tin-nickel alloy film comprising the steps of:
depositing a tin layer and a nickel layer on a given substrate sequentially, thereby to form a multilayered film composed of the tin layer and the nickel layer, and
irradiating laser beams onto the multilayered film to form the tin-nickel alloy film.
The inventors have intensely studied to obtain the tin-nickel alloy film not including the non-equilibrium NiSn phase. As a result, they have found out a new method for producing the above tin-nickel alloy film in which films made of tin and nickel, which are the component in the tin-nickel alloy film, are stacked to form a multilayered film, and then, laser beams are irradiated to the multilayered film to diffuse the tin elements and the nickel element into the respective opposite layers, and thus, obtain the tin-nickel alloy film.
According to the present invention, the tin-nickel alloy film is produced in short time through the rapid diffusion of the tin element to constitute the tin-film and the nickel element to constitute the nickel film. Therefore, it can maintain its original properties in use, and the original functions given to the tin-nickel alloy film can be maintained for a long time.
REFERENCES:
patent: 4495255 (1985-01-01), Draper et al.
Matsuyoshi, H.,Development of Sn-Ni alloy film having large oxidation resistance at higher temperature,The Surface Finishing Society of Japan, Sep., 2000.
Sonoda, T., et al.,Structure and Properties of Bright Tin-Nickel Alloy Films Formed By Thermal Diffusion Method,The Surface Finishing Society of Japan, vol. 45, No. 2, 1994, pp. 197-201.
Yoshimura, S., et al.,Corrosion Resistance of Tin-Nickel Alloy Films Formed by Heating Diffusion Treatment,The Surface Finishing Society of Japan, vol. 44, No. 2, 1993, pp. 176-178.
Alloying of a Ni-Sn multiplayer on an iron plate through thermal process,May, 2000.
Kanematsu, H., et al.,Thermal Alloying of Tin/Nickel Films as Substitutes for Chromium Plating,Proceedings AEST SUR/FIN® 2000, Annual International Technical Conference, Jun., 2000, pp. 842-847.
Hino, M., et al.,Optimum Conditions for the Alloying of Zn/Ni Double-Coated Film by YAG Laser Irradiation,vol. 44, No. 11, 1993, pp. 933-937.
Kanematsu Hideyuki
Masuo Yoshihiko
Oki Takeo
Burns Doane , Swecker, Mathis LLP
Suzuka National College of Technology
Yee Deborah
LandOfFree
Method for producing a tin-nickel alloy film does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for producing a tin-nickel alloy film, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for producing a tin-nickel alloy film will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3069908