ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a stacked piezoelectric element and a producing method therefor.
2. Related Background Art
Conventionally there has been proposed a stacked piezoelectric element in which an electro-mechanical energy converting material such as piezoelectric ceramics having electro-mechanical energy converting function and an electrode material are alternately stacked. Such stacked piezoelectric element, in comparison for example with plate like single piezoelectric ceramics of a same thickness, can provide a larger distortion for deforming or a larger generated force with a lower applied voltage, and is therefore investigated and employed for use in the driving portion of a vibration element constituting a vibration driving device such as a piezoelectric actuator or a vibration wave motor.
The stacked piezoelectric element is produced principally in the following two methods.
The first producing method consists of forming electrode layers on both surfaces of a sintered single piezoelectric ceramic plate, stacking a plurality of such ceramic plate and adhering, for example with adhesive material, the ceramic plates.
The second producing method is an integral sintering method consisting of superposing and thermally pressing layers of unsintered sheet-shaped molded member (green sheet) containing piezoelectric ceramics and an organic binder and unsintered layers of electrode paste and sintering thus superposed layers.
For connecting the electrode layers in thus produced stacked piezoelectric element with the outside, there is proposed a method of forming electric connection between the layers by a through hole (via hole) electrode, which is a penetrating electrode obtained by forming a through hole in each piezoelectric ceramic layer and filling such through hole with an electrode material.
Particularly in the second producing method for the stacked piezoelectric element, the through hole (via hole) electrode is obtained by forming a hole in the green sheet of the piezoelectric ceramics and filling the holes with conductive paste before stacking, and then sintering the green sheets after stacking.
A stacked piezoelectric element, in which such through hole (via hole) electrode is exposed on the surface layer of the stacked piezoelectric element and is used as the electric conductive means to the external circuit such as a printed wiring board, is proposed for example in the Japanese Patent Application Laid-open No. 8-213664.
When such proposed stacked piezoelectric element is employed in rod or Langevin type of a vibration wave actuator or motor, the reference shows that the smoothness of the upper and lower surfaces of the element affects the mechanical quality coefficient (Qm) of the entire device.
It is therefore proposed to apply surface processing (lapping, polishing, grinding etc.) to the upper and lower surfaces of the stacked piezoelectric element after sintering, thereby obtaining the element of high flatness.
The through hole (via hole) electrode of the stacked piezoelectric element may be provided at a position arbitrarily selected for forming electrical conduction between the layers.
For example in
FIG. 6A
, in a piezoelectric ceramic
2
-
1
of a first layer, constituting the surface layer of the stacked piezoelectric element
1
, a through hole electrode
4
-
1
is formed in a position suitable for external connection.
In a piezoelectric ceramic
2
-
2
of a second layer, a through hole electrode
4
-
2
is provided in a position suitable for connecting the piezoelectric ceramic
2
-
1
of the first layer to a piezoelectric element
2
-
3
of a third layer so as to be made an electrical connection by an electrode film
3
-
2
.
In the third and lower layers, a through hole electrode
4
-
3
and further through hole electrodes are provided in positions having relatively little contribution to the mechanical force generation, in order to achieve effective force generation of the stacked piezoelectric element
1
.
However, the surface processing on the upper and lower surfaces of the stacked piezoelectric element of the above-described configuration has revealed the necessity for further improvement as will be explained in the following.
In the piezoelectric ceramics
2
constituting the stacked piezoelectric element
1
and the conductive member constituting the through hole electrodes
4
for the different layers, the green sheet and the conductive paste containing the conductive material show mutually different contraction rates at the sintering operation, because of the characteristics of each material and the different mixing ratios of the organic binder present prior to the sintering.
For this reason, there is generated a residual stress in a hatched area a shown in
FIG. 6A. A
defect from the falling off is easily generated in such area &agr;, and it is confirmed that, if the smoothing surface processing is applied to the upper and lower surfaces of such stacked piezoelectric element
1
, a part of the piezoelectric ceramic drops off in an area &bgr; shown in FIG.
6
B.
Such dropping off of the piezoelectric ceramic exposes the through hole electrode
4
-
2
, leading to a drawback such as shortcircuiting with the wiring on the printing wiring board.
On the other hand, the electrode material employed in the above-described process is generally composed of a precious metal (platinum, palladium, silver etc.) having high melting temperature or a mixture thereof because it has to be sintered together with the piezoelectric ceramic material. The electrode material is most commonly composed of a mixture of silver and palladium with a weight ratio of 5:5 to 8:2 though it is dependent also on the sintering temperature of the piezoelectric ceramic.
Such precious metals are expensive and constitute the largest proportion in the material cost of the stacked piezoelectric element. For this reason, the electrode layers are formed as thin as possible within the manufacturable range of the stacked piezoelectric element and within the acceptable performance range thereof, by the improvement in the electrode paste consisting of the electrode material, organic binder, solvent and other additives and the layer forming method such as screen printing.
The piezoelectric element thus formed is then subjected to a polarization process for enabling elongation and contraction for the actual use. The uppermost surface electrode layer is used as a contact electrode in such polarization process but is removed after the polarization process, thereby enabling connection of the individual through hole (through hole filled with conductive material being often called a through hole electrode or a via hole) exposed on the surface with the driving circuit.
Prior to the actual use, the stacked piezoelectric element is subjected to the polarization process of applying a voltage to the piezoelectric ceramic layers. This process is executed by applying a voltage of 3 to 1 kV/mm for a period of 30 to 60 minutes under a high temperature (80° C. to 200° C.).
In this process, the current generated after the voltage application becomes very large in case of the stacked piezoelectric element because of the significantly larger electrostatic capacitance in comparison with the conventional single-plate piezoelectric element. Consequently a large current is generated in the thin electrode layers of the stacked piezoelectric element, particularly in the connecting portion between the surface electrode layer in direct contact with the DC power source for the polarization process and the conductive electrode connecting the surface electrode to the internal electrode layers, whereby sparks are often generated to induce fused breakage of the connecting portion, thus inhibiting the polarization process or eventually resulting in the destruction of the element by the shock of the sparks.
The stacked piezoelectric element utilizes, in the conductive electrode for connecting the internal electrode layers, the through hole commonly employed in the p
Ezaki Toru
Kojima Nobuyuki
Maruyama Yutaka
Yamakawa Takahiro
Arbes Carl J.
Nguyen Tai
LandOfFree
Method for producing a stacked piezoelectric element does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for producing a stacked piezoelectric element, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for producing a stacked piezoelectric element will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3146471