Metal treatment – Process of modifying or maintaining internal physical... – With casting or solidifying from melt
Reexamination Certificate
2002-07-22
2004-12-28
Yee, Deborah (Department: 1742)
Metal treatment
Process of modifying or maintaining internal physical...
With casting or solidifying from melt
C148S541000, C148S602000, C148S603000, C148S598000, C148S599000
Reexamination Certificate
active
06835253
ABSTRACT:
BACKGROUND OF THE INVENTION
The invention relates to a method for producing a hot strip, in particular for producing a hot strip intended for the production of a cold strip with good deep-drawing characteristics, made of a low-carbon low alloyed steel, in which thin slabs are produced by continuous strand casting; in which the strand emerging from a permanent casting mould during continuous strand casting passes along a cooling line; and in which the cast strand itself or thin slabs divided off the strand are reheated in a soaking furnace before they are hot rolled to form hot strip.
In a known method of the above-mentioned type, which has become known as the “CSP method”, thin slabs are divided off a steel strand produced in a continuous strand casting plant and after temperature equalisation in a tunnel furnace, are subjected to rolling in a multistand mill train so as to form hot strip. In the known method, as a rule the thin slabs enter the soaking furnace at a temperature between 950° C. and 1100° C. and are reheated therein to a temperature between 1100° C. and 1200° C.
By using the heat present in the strand after casting, the known method makes it possible to produce hot strip with reduced energy expenditure when compared to other conventional methods of this type. However, with this method, the soaking furnace must be operated at very high temperatures. Such high temperatures cause rapid wear of the furnace so that the cost of furnace maintenance negates the benefit of energy gains achieved. Nonetheless the high temperatures in the soaking furnace are required in the state of the art so as to keep in, or bring to, solution, the alloying constituents in the steel strand, said constituents during subsequent process steps in the production of the hot strip or of the cold strip made from said hot strip, causing precipitation which has a decisive influence on the formation of a particular microstructure in the finished hot strip or in the cold strip produced therefrom.
From EP 0 686 702 A1 a modification of the above-mentioned method is known in which the surface temperature of the slab between the permanent casting mould and the soaking furnace is lowered in an adequate way to such an extent that a microstructural transformation from austenite to ferrite/pearlite takes place in the slab. It is further stated that the temperature attained during this process at a depth of 2 mm below the slab surface is preferably below 600° C.
It is the aim of the measures described in EP 0 686 702 A1 to achieve a situation in which even such slabs which as a result of the addition of substantial quantities of secondary scrap to the melt contain significant amounts of copper, enter the soaking furnace in a state by which excessive accumulation of copper in the region of the grain boundaries of the primary austenite is prevented. Otherwise such accumulation causes very considerable scale formation and in further stages of hot strip production can cause so-called soldering fractures. By cooling the slabs to a temperature below the A
r3
temperature (the temperature below which transformation of austenite to ferrite takes place), a microstructure transformation with re-orientation of the austenite grain boundaries is enforced during reheating in the soaking furnace.
Slabs which are cooled in this way are reheated in the soaking furnace to the high temperature to which the soaking furnace is usually set. In order to expend as little energy as possible for reheating, in the method known from EP 0 686 702 A1, the depth of cooling and the time intended for cooling are reduced to a minimum so that the temperature in the interior of the slab is as high as possible when the slab enters the soaking furnace.
Attempts to minimise both the wear of the soaking furnace and the energy expenditure required for its operation, by reducing the furnace temperature have shown that such a reduction in temperature in particular during processing of low-alloyed low-carbon steels has a negative influence on the formation of precipitation in the subsequent process of hot strip production and cold strip production.
SUMMARY OF THE INVENTION
It is thus the object of the invention, in a process of the type mentioned above, during processing of low-alloyed low-carbon steels to reduce the required temperature in the soaking furnace such that the stress on the furnace is reduced without there being any reduction in the quality of the hot strip produced, or of the cold strip made from said hot strip.
According to the invention this object is met by a method for producing a hot strip, in particular for producing a hot strip intended for the production of a cold strip with good deep-drawing characteristics; in which a steel melt comprising (in % by weight) C:≦0.07%, Si:≦0.5%, Mn:≦2.5%, Al:≦0.1%, N:≦0.01%, P:≦0.025, B:≦0.05, if need be up to a total of 0.35% of Nb, Ti and V, with the remainder being iron and the usual impurities; in which the steel melt is continually output from a permanent casting mould; in which the cast strand immediately after discharging from the permanent casting mould is led along a cooling line; in which the strand is intensively cooled down to a temperature of A
r1
±25 K at a cooling rate of at least 3 K/s; in which, following its intensive cooling, the strand is cooled by exposure to air for at least 30 seconds; and in which the strand itself or thin slabs divided off the strand is/are reheated in a soaking furnace before the strand or the thin slabs are hot rolled to form hot strip.
Since according to the invention the strand emerging from the permanent casting mould is subjected to intensive cooling at cooling rates of at least 3 K/s, during which cooling the strand is cooled to a temperature of A
r1
±25 K (the temperature at which the transformation from austenite to ferrite is completed), the precipitation required to achieve the desired material characteristics of the hot strip, is in a targeted way already introduced in the region in front of the soaking furnace. Thus, during cooling by exposure to air, which cooling follows intensive cooling, there is sufficient time available for the precipitation processes to be essentially complete at the time of entry into the soaking furnace. At the same time, homogenisation of the temperature in the strand takes place so that there is an even temperature distribution at the time of entry into the furnace.
Since the formation of precipitation has essentially been completed prior to entry into the soaking furnace, the furnace temperature can be limited to a temperature which is below the reheating temperature applied in the conventional approach. Advantageously, the soaking furnace temperature to be adhered to according to the invention is in a range whose lower limit is determined by the A
r3
temperature and whose upper limit is 1150° C.
A reheating temperature of max. 1050° C. is sufficient if the hot strip produced according to the invention is used for the production of a cold strip which after cold rolling is annealed in a continuous annealing furnace. In this case, preferably no precipitation processes take place during any reheating connected with the production of the hot strip and cold strip, such process steps following reheating, so that it is no longer necessary to bring to solution any alloying constituents which take part in the formation of precipitation.
By contrast, if from the hot strip produced according to the invention, a cold strip is rolled which after cold rolling is annealed in a hood-type annealing furnace, then the temperature in the soaking furnace, during heating of the strand or the thin slabs, should be in the range from 1100° C. to 1150° C. If the heating temperature exceeds 1100° C., sufficient Al nitride will become soluble to produce a desirable “pancake” microstructure during hood-type annealing.
It has been found that a strip produced according to the invention has a fine-grained microstructure which has a favourable effect on the deep-drawability of a cold strip made from the hot st
Engl Bernhard
Heller Thomas
Kawalla Rudlof
Rasim Wolfgang
Sowka Eberhard
Proskauer Rose LLP
Thyssen-Krupp Stahl AG
Yee Deborah
LandOfFree
Method for producing a hot strip does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for producing a hot strip, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for producing a hot strip will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3327754