Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – From carboxylic acid or derivative thereof
Reexamination Certificate
2002-01-24
2003-05-06
Acquah, Samuel A. (Department: 1711)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
From carboxylic acid or derivative thereof
C528S283000, C528S286000, C528S302000, C528S307000, C528S308000, C528S308600, C524S706000, C524S783000, C524S789000
Reexamination Certificate
active
06559272
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the invention
The present invention relates, in general, to a method for preparing polyester resins copolymerized with glycol for modification such as 1,4-cyclohexanedimethanol. More particularly, the present invention pertains to a method for preparing polyester resins, in which polycondensation in the presence of titanium dioxide/silicon dioxide coprecipitate in the form of a suspension in glycol as a polycondensation catalyst is carried out.
2. Description of the Prior Art
Recently, polyester resin found many important applications in packing, molding and film industries. However, polyesters consisting merely of terephthalic acid and ethylene glycol do not show good moldability. For this reason, various glycols and/or dicarboxylic acids have been employed to modify the above polyesters and such modified polyester resins are prevalent in such industries. Conventionally, these polyester resins were prepared in the presence of antiomony catalysts. However, recent research has been directed to the preparation of polyester resins in the presence of titanium catalysts, instead of parts or all antimony catalysts which are required in large quantities owing to their relatively low catalytic activity, with the aim of improving reactivity and product transparency and avoiding the gray coloration attributable to antimony catalysts.
In this regard, U.S. Pat. Nos. 5,681,918 and 5,744,571 disclose the preparation of polyester in the presence of titanium alkoxide-based catalysts. Over antinomy-based catalysts, the titanium alkoxide-based catalysts certainly have advantages in the quantity used and in reactivity. However, the high sensitivity of the titanium alkoxide-based catalysts to moisture results in undesirable problems. For example, these catalysts are difficult to store and handle because, when coming into contact with moisture, they become low in reactivity and are deposited as precipitates. In addition, the titanium alkoxide-based catalysts should be added in amounts larger than necessary because moisture is generated upon ester exchange, adversely affecting the activity of the catalysts. Further, the polyester or copolyester resins, which are prepared in the presence of the titanium-alkoxide catalysts, are not improved in color or transparency to desirable extents.
Furthermore, U.S. Pat. Nos. 5,684,116 and 5,789,528 propose titanium dioxide/silicon dioxide coprecipitates and/or titanium dioxide/zirconium dioxide coprecipitates as polycondensation catalysts for the preparation of polyesters and copolyesters. However, nowhere are there mentioned copolyester resins comprising diols in a copolymerization ratio of more than 20%, nor the possibility to achieve such resins are disclosed.
SUMMARY OF THE INVENTION
The intensive and thorough research into the preparation of polyester resin copolymerized with glycol such as 1,4-cyclohexanedimethanol, conducted by the present inventors aiming to overcome the above problems encountered in prior arts, resulted in the finding that the polycondensation of esterification products in the presence of certain titanium-based compounds brings about a significant improvement in the transparency and coloration of the final products, leading to the present invention.
Therefore, it is an object of the present invention to provide a method for preparing polyester resins copolymerized with glycol ingredient for modification such as 1,4-cyclohexanedimethanol, which have excellent transparency and color properties as well as good processability.
Based on the present invention, the above object may be accomplished by a provision of a method for preparing copolyester resins comprising the following steps of: esterifying dicarboxylic acid with ethylene glycol and other glycol for modification; and polycondensing said esterification product in the presence of a titanium dioxide/silicon dioxide coprecipitate catalyst, said catalyst being in the form of 4% or less strength by weight suspension in glycol, in which the copolyester resins have said other glycol content ranging from 20 to 80 mol % of the total glycol content.
DETAILED DESCRIPTION OF THE INVENTION
In accordance with the present invention, polyester or copolyester is prepared in a two-stage process, that is, esterification and polycondensation.
In the first stage, the esterification is carried out using dicaboxylic acid, ethylene glycol and other glycol for modification such as 1,4-cyclohexanedimethanol, where the molar ratio of total glycols (ethylene glycol+other glycol for modification) to dicarboxylic acid is within the range of 1.05:1 to 3.0:1.
The dicarboxylic acid useful in the present invention may be exemplified by terephthalic acid, isophthalic acid, 1,4-cyclohexanedicarboxylc acid, 1,3-cyclohexnaedicarboxylic acid, succinic acid, glutaric acid, adipic acid, sebasic acid, 2,6-naphthalenedicarboxylic acid or mixtures thereof.
Examples of said other glycol ingredient for modification useful in the present invention are 1,4-cyclohexanedimethaneol, 1,2-propanediol, 1,3-propanediol, 1,4-propanediol, 2,2-dimethyl-1,3-propanediol, 1,6-hexanediol, 1,2-cyclohexanediol, 1,4-cyclohexanediol, 1,2-cyclohexanedimethanol, 1,3-cyclohexanedimethanol or mixtures thereof, with preference for 1,4-cyclohexanedimethanol. At this time, 1,4-cyclohexanedimethanol, representative of said other glycol, may be a cis- or a trans-isomer, or mixtures thereof.
Said other glycol ingredient is added at an amount approximated to a desired mol % of the final copolyester product. In the present invention, said other glycol content of the copolyester ranges from 20 to 80 mol % of the total glycol content so as to prevent the difficulties in polymer processing processes due to crystallization and improve other physical properties.
Additionally, multifunctional compounds such as trimellitic anhydride, trimellitic acid, trimethylolpropane, and/or pentaerythritol may be used in small quantities.
The esterification is carried out at 230 to 260° C., preferably, at 240 to 260° C., and even more preferably, at 245 to 255° C. under a pressure of 0.1 to 3.0 kg/cm
2
. Also, the esterification generally requires 100 to 300 min to complete, depending on the reaction temperature, pressure and molar ratio of total glycols to dicarboxylic acid.
The esterification is usually carried out in the absence of catalysts, but a decrease in reaction time requires use of catalysts. In the present invention, the esterification of glycols and dicarboxylic acid may be conducted in a batch or a continuous manner. The materials may be separately fed, but it is most preferable to feed the materials together in a slurry form.
Following the completion of the esterification reaction, the polycondensation is conducted. In advance of the second stage, a polycondensation catalyst is added, along with a stabilizer and optionally a color toning agent, to the esterification product.
For use in polycondensation, catalysts are conventionally selected from titanium, germanium and antimony compounds. Among these, the titanium-based catalyst is the most advantageous since it is used at a smaller amount than the antimony-based catalyst and is less expensive than the germanium-based catalyst.
Examples of generally usable titanium-based catalyst include tetraethyl titanate, acetyltripropyl titanate, tetrapropyl titanate, tetrabutyl titanate, polybutyl titanate, 2-ethylhexyltitanate, octyleneglycol titanate, lactate titanate, triethanolamine titanate, acetylacetonate titanate, ethylacetoacetic ester titanate, isostearyl titanate, titanium dioxide, titanium dioxide/silicon dioxide coprecipitates, and titanium dioxide/zirconium dioxide coprecipitates. In the present invention, titanium dioxide/silicon dioxide coprecipitates are employed because they are easy to store and handle because of their insensitivity to moisture, as well as bringing about an improvement in color and transparency. In accordance with the present invention, titanium dioxide/silicon dioxide coprecipitates are added in the form of 4% or less strength by weight suspen
Hong Yoon-Hee
Jeon Jae-Young
Kim Sung-Gi
Abelman ,Frayne & Schwab
SK Chemicals Co. Ltd.
LandOfFree
Method for preparing copolyester resins using titanium... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for preparing copolyester resins using titanium..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for preparing copolyester resins using titanium... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3025399