Metal working – Electric condenser making – Solid dielectric type
Reexamination Certificate
2001-11-08
2004-09-07
Trinh, Minh (Department: 3729)
Metal working
Electric condenser making
Solid dielectric type
C029S025410, C029S025350, C029S025030, C029S830000, C361S321200, C361S321400, C501S032000, C501S136000
Reexamination Certificate
active
06785941
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to multi-layer ceramic electronic parts having, for example, a laminated body of internal electrode patterns and ceramic layers therein, at end portions of which are provided external electrodes so as to connect to the internal electrodes, and in particular to multi-layer ceramic electronic parts in which a material common with a ceramic material for forming the ceramic layers of the laminated body is added into at least a portion of the external electrodes, and further a manufacturing method thereof.
2. Description of Related Art
As electronic components of a laminated type can be listed, for example, a laminated capacitor, a laminated inductor, a laminated piezo element, a laminated filter, a ceramic multi-layer circuit board, etc.
For example, in a laminated ceramic capacitor being the most representative one of the laminated electronic components, a large number of layers are stacked or laminated, each having an internal electrode and made of dielectric material, wherein the above-mentioned internal electrodes are pulled out to the end surfaces of the laminated body opposing to each other and, on the end surfaces to which those internal electrodes are pulled out, are formed external electrodes, and those external electrodes are connected to the above-mentioned internal electrodes, respectively.
The above-mentioned laminated body
3
of the laminated ceramic capacitor has a layer construction as shown in
FIG. 3
, for example. Namely, the ceramic layers
7
,
7
. . . , each having the internal electrode
5
or
6
and made of dielectric material, are laminated in an order as shown in the
FIG. 3
, and further on both sides (i.e., upper and lower sides) thereof are stacked or laminated the ceramic layers
7
,
7
. . . in a plurality thereof, on which no electrode
5
or
6
is formed, respectively. Upon the end portions of the laminated body
3
having such a layer structure therein, the internal electrodes
5
and
6
are exposed to one another, and as shown in
FIG. 1
, the above-mentioned external electrodes
2
and
2
are formed at the end portions of this laminated body
3
.
Such a laminated ceramic capacitor, ordinarily, is not manufactured one by one, or in a unit of one part as shown in
FIG. 3
, but actually is obtained with a manufacturing method which will described below. Namely, first of all, minute ceramic powder and organic binder are mixed to prepare a slurry, and it is extended thinly on a carrier film made from a polyethylene terephthalate film, etc., by means of doctor blade method. Then, it is dried to be formed into a ceramic green sheet. Next, this ceramic green sheet is cut out into a desired size by a cutting head, while being mounted on the supporting sheet, and is printed with a conductive paste on one side surface thereof by a screen printing method, and is dried. With this, the ceramic green sheets
1
a
and
1
b
are obtained, on each of which plural sets of the internal electrode patterns
2
a
and
2
b
are aligned or arranged in the vertical and horizontal directions, as shown in FIG.
4
.
Next, plural pieces of the ceramic green sheets
1
a
and
1
b,
each having the above-mentioned internal electrode patterns
2
a
or
2
b
thereon, are stacked or laminated, and further are stacked several pieces of the ceramic green sheets
1
,
1
. . . having no internal electrode
2
a
or
2
b,
at the top and the bottom thereof. They are compressed together, thereby to form the laminated body. Here, the above ceramic green sheets
1
a
and
1
b
are stacked on one another, on which the internal electrode patterns
2
a
and
2
b
are shifted by half of the length in a longitudinal direction thereof. After that, this laminated body is cut out into a desired size, thereby to manufacture laminated raw chips, and those raw chip are baked. In this manner are obtained the laminated bodies as shown in FIG.
3
.
Next, this baked laminated body
3
is applied with a conductor paste on both ends thereof and is baked, and on the surface of the baked conductive film is treated a plating, thereby completing the laminated ceramic capacitor formed with the external electrodes at both ends thereof, as shown in FIG.
1
.
The multi-layer ceramic electronic part, such as the laminated ceramic capacitor mentioned above, is mounted on a circuit board and is soldered at the external electrodes
2
and
2
on both ends thereof on land electrodes of the circuit board.
However, such a laminated ceramic capacitor generates thermal stress within the laminated body
3
due to heat-shock when being soldered at the external electrodes thereof or due to change of a circumference temperature under the condition of use after the soldering. With this thermal stress, in particular in an end portion of the external electrodes
2
and
2
of the laminated body
3
, can easily occur cracks. The cracks occurring in the laminated body
3
bring about a lowering in insulation due to invasion of moisture inside and a lowering in static capacitance due to discontinuity of the internal electrodes
5
and
6
, thereby causing a low reliability thereof.
Such a thermal stress causing the cracks in the laminated body occurs due to the difference in the thermal expansion ratio between the ceramic material, which is a main ingredient of forming the laminated body
3
, and the conductor which is a main ingredient of forming the external electrodes
2
and
2
. Then, conventionally, a measure was taken, into the conductor paste for forming the external electrodes
2
and
2
is added the ceramic material of forming the ceramic layer
7
as a common material, thereby to make small the difference between the ceramic layer
7
and the external electrodes
2
and
2
in the physical properties, such as the thermal stress therein.
However, if the common material, i.e., the ceramic material for forming the ceramic layer
7
, is put or added into the conductor paste for forming the external electrodes
2
and
2
much, stickiness or adhesiveness of the external electrodes
2
and
2
onto the external electrodes
5
and
6
comes to be inferior, i.e., connecting resistance therebetween becomes large and also the electric properties thereof are deteriorated. Further the stickiness or adhesiveness onto the solder or Sn plating is also deteriorated. As a result of this, solder wetability of the external electrodes
2
and
2
comes to be inferior, therefore mis-mounting easily occurs when mounting the multi-layer ceramic electronic part(s) on the circuit board.
SUMMARY OF THE INVENTION
An object, according to the present invention, for solving the problem in the conventional art mentioned above, is to provide a multi-layer ceramic electronic parts, wherein cracks in the laminated hardly occur due to the heat-shock accompanying a change of temperature under the conditions of being soldered and of use thereafter, and further the adhesiveness between the external and internal electrodes and the adhesiveness of solder onto the external electrode are superior, as well, thereby also being superior in soldering property with the external electrodes.
According to the present invention, for achieving the above-mentioned object, pillar-like ceramic portions
22
extending in a direction of thickness of a conductor film
21
are scattered in the conductor films
21
of the external electrodes
2
and
2
. Each ceramic portion contains a material common to the ceramic material forming the ceramic layers
7
of the laminated body
3
. Therefore, it has a strong bonding power onto the ceramic layers
7
of the laminated body
3
. On the other hand, the conductor layer
21
has a strong bonding power onto the internal electrodes
5
and
6
of the laminated body
3
, and shows a good adhesiveness onto a plating film
24
on the surface thereof. With the conductor films
21
and the ceramic portions
22
scattered therein complementing each other in the characteristics thereof, it is possible to ensure the bonding power of the external electro
Flynn ,Thiel, Boutell & Tanis, P.C.
Taiyo Yuden Co. Ltd.
Trinh Minh
LandOfFree
Method for manufacturing multi layer ceramic components does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for manufacturing multi layer ceramic components, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for manufacturing multi layer ceramic components will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3250042