ABSTRACT:
A mixture containing 65 to 72% by weight of aluminum oxide and 28 to 35% by weight of magnesium oxide is used to mold items which are then dried in vacuum at a temperature of a heater, which is a component element of a mold, attaining about 1000.degree. C., the items being subsequently subjected to a burn in an inert gas atmosphere at a temperature of approximately 1850.degree. C. and at a rate of more than 100.degree. C./minute.
The present invention permits the time required to manufacture the items to be brought down to 2-4 hours, the items produced being characterized by a high refractoriness, capable of withstanding temperatures of up to 1850.degree. C., high chemical inertness and resistance to dynamic action of refractory alloys and steels during melting and casting thereof. Thermal shock resistance of the manufactured items is 60 to 70 air thermal (heating-cooling) cycles.
REFERENCES:
patent: 2805167 (1957-09-01), McCreight et al.
patent: 3304153 (1967-02-01), Bakker et al.
patent: 3950504 (1976-04-01), Belding
Korolev et al., "Shaped Casting by the Lost Wax Process", Oborongiz Publisher, Moscow, 1962, pp. 96-97.
Belkevich, U. L., "Technical-Grade Ceramics", Moscow, 1968, pp. 177-178.
Anisimov Jury V.
Avdjukhin Sergei P.
Frolov Vladimir S.
Kalinin Viktor P.
Larionov Valentin N.
Bell Mark
Vertiz O. R.
LandOfFree
Method for manufacturing highly refractory aluminum and magnesiu does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for manufacturing highly refractory aluminum and magnesiu, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for manufacturing highly refractory aluminum and magnesiu will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-1293905