Optical waveguides – Planar optical waveguide
Reexamination Certificate
2002-05-07
2004-07-27
Ullah, Akm Enayet (Department: 2874)
Optical waveguides
Planar optical waveguide
C385S130000, C065S386000, C065S391000, C438S031000
Reexamination Certificate
active
06768857
ABSTRACT:
FIELD OF THE INVENTION
The invention relates to a method for manufacturing an optical device with a defined total device stress. More particularly, the invention relates to a method for manufacturing an optical waveguide wherein the waveguide core stress and the cladding layer stress sum up to a total device stress with a desired distribution, more particularly, this distribution being such that the optical mode(s) in the waveguides do not experience any birefringence and the polarization dependence is minimized or such that the birefringence and the polarization dependence are set to a desired, defined value.
BACKGROUND OF THE INVENTION
In the article “Characterization of Silicon-Oxynitride Films deposited by Plasma Enhanced CVD” by Claassen, v.d. Pol, Goemans and Kuiper in J. Electrochem. Soc.: Solid state science and technology, July 1986, pp 1458-1464 the composition and mechanical properties of silicon-oxynitride layers made by plasma-enhanced deposition using different gas mixtures are investigated. It is stated that the mechanical stress strongly depends on the amount of oxygen and hydrogen incorporated in the layer. Heat treatment at temperatures higher than the deposition temperature leads to a densification of the film due to hydrogen desorption and cross-linking.
In “Temperature dependence of stresses in chemical vapor deposited vitreous films” by Shintani, Sugaki and Nakashima in J. Appl. Phys. 51(8), August 1980, pp 4197-4205 it is shown that in vitreous silicate glass depending on deposition background pressure different components of tensile and compressive stress occur. Also a hysteresis of the stress is observed.
In “Stress in chemical-vapor-deposited SiO
2
and plasma-SiN
x
films on GaAs and Si” by Blaauw in J. Appl. Phys. 54(9), September 1983, pp 5064-5068 stress in films of CVD-SiO
2
and plasma-SiN
x
on GaAs is measured as a function of temperature. Different properties of the stress are observed depending on, e.g., film thickness, doping and annealing parameters.
“Stress in silicon dioxide films deposited using chemical vapor deposition techniques and the effect of annealing on these stresses” by Bhushan, Muraka and Gerlach in J. Vac Sci. Technol. B 8(5), September/October 1990, pp 1068-1074 deals with in situ measured stress as a function of temperature. Different deposition techniques are investigated and in PECVD silica films on silicon substrates a change of the stress sign from compressive to tensile is observed with rising annealing temperature.
U.S. Pat. No. 4,781,424 is related to a single mode optical waveguide having a substrate, a cladding layer formed on the substrate, a core portion embedded in the cladding layer, and an elongated member for applying a stress to the core portion or a stress relief groove for relieving a stress from the core portion in the cladding layer along the core portion. The position, shape and material of the elongated member or the groove are determined in such a way that stress-induced birefringence produced in the core portion in accordance with a difference in thermal expansion coefficient between the substrate and the single mode optical waveguide is a desired value.
In U.S. Pat. No. 5,502,781, integrated optical devices which utilize a magnetostrictively, electrostrictively or photostrictively induced stress to alter the optical properties of one or more waveguides in the device are disclosed. The integrated optical devices consist of at least one pair of optical waveguides preferably fabricated in a cladding material formed on a substrate. A stress applying material, which may be a magnetostrictive, electrostrictive or photostrictive material, is affixed to the upper surface of the cladding material near at least one of the optical waveguides. When the appropriate magnetic, electric or photonic field is applied to the stress applying material, a dimensional change tends to be induced in the stress applying material. The constrained state of the stress applying material, however, caused by its adhesion to the cladding material, causes regions of tensile and compressive stress, as well as any associated strains, to be created in the integrated optical device. By positioning one or more optical waveguides in a region of the device which will be subjected to a tensile or compressive stress, the optical properties of the stressed waveguide may be varied to achieve switching and modulation. Latchable integrated optical devices are achieved by utilizing a controlled induced stress to “tune” one or more waveguides in an integrated optical device to a desired refractive index or birefringence, which will be retained after the field is removed.
U.S. Pat. No. 4,358,181 discloses a method of making a preform for a high numerical aperture gradient index optical waveguide. Therein the concentration of two dopant constituents is changed during fabrication. Concentration of the first dopant, germanium, is changed radially as the preform is built up in order to produce the desired radial refractive index gradient. The concentration of the second dopant, boron, is changed radially to compensate for the radial change in thermal expansion coefficient caused by the varying Ge concentration. B is added to the cladding layer to make the thermal expansion coefficient of the cladding equal to or greater than the composite thermal expansion coefficient of the core. The magnitude of residual tension at the inner surface caused by thermal expansion gradients is reduced and premature cracking of the preform is eliminated.
Disclosed in U.S. Pat. No. 4,724,316 is an improved fiber optic sensor of the type in which a fiber optic waveguide component of the sensor is configured to be responsive to an external parameter such that curvature of the fiber optic waveguide is altered in response td forces induced by changes in the external parameter being sensed. The alteration of the curvature of the fiber optic waveguide causes variations in the intensity of light passing therethrough, these variations being indicative of the state of the external parameter. The improvement comprises coating material covering the exterior portion of the fiber optic waveguide, the coating material having an expansion coefficient and thickness such that distortion of the fiber optic waveguide caused by thermally induced stresses between the coating material and the glass fiber is substantially eliminated. Also disclosed is a support member for supporting the curved fiber optic waveguide, the support member and fiber optic waveguide being configured and arranged to minimize the effects of thermal stress tending to separate the waveguide from the support member.
SUMMARY OF THE INVENTION
According to a first aspect of the invention herein is provided a method for manufacturing an optical device with a defined total device stress and a therefrom resulting defined birefringence, which device is easy to manufacture and at the same time provides a high precision in the resulting birefringence value with the final intent to obtain a defined optical polarization dependence for the optical mode propagating in the device.
The total device stress is substantially determined by the waveguide core stress and the waveguide cladding stress, also referred to as cladding layer stress, both of which can be influenced by thermal annealing processes the device may be subjected to. The waveguide core stress and the waveguide cladding stress can be tuned independently, for example, by variation of the temperature of the respective annealing step. The tuned state, namely, the state when the desired waveguide core stress, the desired waveguide cladding stress, and the desired device birefringence have been achieved, will remain after the annealing step(s). The tuned state can be such that the optical mode(s) in the waveguides do not experience any birefringence and the polarization dependence is minimized, or such that the birefringence and the polarization dependence is set to a desired non-zero-value, e.g., to build an optical mode converter.
The waveguide core stress is typically prede
Bona Gian-Luca
Germann Roland
Meijer Ingmar
Offrein Bert
Salemink Huub L
Cheung Wan Yee
International Business Machines - Corporation
Ullah Akm Enayet
Wood Kevin S.
LandOfFree
Method for manufacturing an optical device with a defined... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for manufacturing an optical device with a defined..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for manufacturing an optical device with a defined... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3204624