Method for making m- type hexaferrite powders or wafers

Compositions – Magnetic – Iron-oxygen compound containing

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C252S062630, C252S062570

Reexamination Certificate

active

06761830

ABSTRACT:

This invention relates to the field of powders or cakes of M type hexaferrites, that is to say constituted of particles of magnetoplumbite of general formula AFe
12
O
19
where typically A represents Ba, Sr, Ca, Pb, the element A and/or Fe being able to be partly substituted by other chemical elements.
These powders are used to manufacture ceramic magnets by compression with orientation of the particles under a magnetic field, and then sintering of oriented and compressed particles.
These powders can also be used in the production of magnetic recording media.
STATE OF THE ART
The usual method for manufacturing powders of ferrite particles is as follows:
the raw materials are provided in the form of powders, typically iron oxide Fe
2
O
3
and strontium carbonate SrCO
3
in the case where A represents Sr,
the powders are mixed with excess Sr relative to the formula of the ferrite, typically a molar ratio Fe
2
O
3
/SrO of about 5.5 instead of 6, a ratio which corresponds to the M phase formula (SrFe
12
O
19
), and possibly after incorporating additives,
the powder mixture is shaped, usually by granulation, or powder compression,
type M ferrite is formed by calcination of the powder granules in an oven at about 1200° C., and after cooling, ferrite granules are obtained, typically with an apparent density d
a
of at least 4, that is a porosity typically lower than 20% compared to that of an M ferrite of Sr of density d
x
equal to 5.11.
the calcinated granules are ground in several stages, with a first rough grinding followed by one or several fine grindings, comprising classification by particle size, the final ferrite powder obtained being exempt of any big aggregates constituted of primary particles (elementary particles), even fine ones.
It is to be noted that in this process, an excess of Sr is used, which leads to the formation of a second liquid phase, which facilitates the calcination reaction and makes the process less difficult to implement. But in this case, it is generally necessary to add silica to limit crystalline growth.
Afterwards, in the case of production of magnets, the fine powder obtained is shaped, to the form of the final magnet, after being dispersed, with orientation of the primary particles under magnetic field and compression.
The compressed product is then dried, sintered and if necessary machined to the required dimensions.
POSSIBLE PROBLEMS
The final performances or final magnetic properties obtained, typically the remanence Br or coercive force HcJ, depend in particular directly on the morphology of the ferrite particles, the remanence Br depending in particular on the ability of the primary particles to be aligned in parallel, and the coercive field HcJ depending in particular on the size and shape of the particles.
Thus, the presence of aggregates formed of primary particles aligned randomly is greatly detrimental for obtaining high magnetic properties, the aggregates being polycrystalline and formed of particles oriented in a haphazard way.
The grinding phase of the state of the art method is thus an important stage of the method, both because of its length and because of its cost, including investments, and through its consequences concerning the final properties of the magnets.
The principal problems associated with this grinding are as follows:
on the one hand, as calcinated ferrites are difficult to grind, one observes significant wear of the grinding equipment and also ferrite pollution by outside elements from the grinding media, which have negative effects on the magnetic properties;
on the other hand, since the elementary particles are very difficult to separate, the final grinding stage is very long—and consequently there is a high proportion of smalls (particles of particle size lower than 0.3 &mgr;m), with negative effects, both concerning the shaping of the ferrite powder for forming magnets, and concerning the possibility of aligning these low dimension particles under a magnetic field, or furthermore the possibility of reagglomeration of smalls, the high possibility of recrystallisation during sintering etc . . .
The consequences are a lowering of the final magnetic properties, the values of Br and HcJ and/or the square appearance of the demagnetisation curve.
Furthermore, taking into account the difficulty of grinding the ferrite, at this stage it is no longer possible to modify the size and/or shape of the elementary particles during this phase of grinding.
The applicant therefore sought a way of making the usual production method more economical and more efficient, while still remaining close, to present technology.
DESCRIPTION OF THE INVENTION
According to the invention, the method for manufacturing M type hexaferrite powders or cakes, of formula AFe
12
O
19
, A and Fe being able to be partially substituted, where A refers to a metal chosen among Ba, Sr, Ca, Pb, or their mixture in which:
a) an iron oxide Fe
2
O
3
and an A compound are provided, usually under the form of powders, and a mixture is made of said iron oxide and said A compound, with a molar ratio n=Fe
2
O
3
/AO,
b) the said mixture is shaped in the form of agglomerates of shape and size adapted to the calcination stage, and these are calcinated in an oven, usually between 1100° C. and 1300° C., in such a way as to form the type M ferrite,
c) said calcinated agglomerates are ground to obtain a fine ferrite powder,
is characterised in that
at the previous stage a) of said calcination:
1) said mixture is formed with a ratio n comprised between 5.7 and 6.1,
2) simultaneously with the formation of said mixture or after this, said mixture is ground, so as to have both a mixture with a degree of homogeneity at least equal to a predetermined threshold, and an average particle size of predetermined value comprised between 0.25 and 1 &mgr;m,
3) before or during said grinding, one introduces into said mixture an agent for controlling the microstructure (ACM),
at stage b), the calcination conditions together with the nature and content of ACM are chosen in order to obtain, at the end of the calcination phase, a ferrite material under the form of a porous cake also having the following properties:
a transformation yield in crystallised M ferrite greater than 95%,
an apparent density d
a
lower than 3.5 and, preferably, lower than 3, or a porosity higher than 30% and preferably higher than 40%,
low cohesion energy at the grain boundaries between primary particles leading to high brittleness, in order to replace the grinding of stage c) by a simple dispersion of said cake.
The invention thus relates to a combination of essential means.
A first essential means is a choice of ratio n very much higher than the value normally used (5.5). A value n as low as this is used so that a 2nd liquid phase is formed with excess Sr (in the case of a Sr ferrite), this formation of a 2nd liquid phase facilitating the total formation reaction of the ferrite and its crystallisation favouring good anisotropy, which makes the process relatively easy to implement on an industrial scale. But, on the contrary, this 2nd liquid phase has a tendency to weld the primary particles together, making later grinding long and difficult.
The risk associated with a value of n higher than the normal value is an incomplete reaction and poor crystallisation of the ferrite.
The means of the invention thus make it possible to obtain both a ratio n close to stoichiometry (n=6), that is to say to reduce to the minimum the presence of a 2nd liquid phase, while still obtaining a high ferrite transformation yield and a crystallisation sufficient for high anisotropy for the ferrite particles obtained.
A second means is constituted of the formation of a mixture of Fe
2
O
3
and the compound of A with a predetermined and high degree of homogeneity, a mixture associated most often with a third grinding means. In practice, several samples are taken from the mixture, typically 3, generally during the grinding, and these samples are calcinated under standard laboratory conditions.
A mixture is considered satisfactory

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Method for making m- type hexaferrite powders or wafers does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Method for making m- type hexaferrite powders or wafers, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for making m- type hexaferrite powders or wafers will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3202250

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.