Method for making an abrasion-resistant steel plate

Details Method for making an abrasion-resistant steel plate Method for making an abrasion-resistant steel plate

2003-11-13

2008-12-09

Yee, Deborah (Department: 1793)

Metal treatment

Process of modifying or maintaining internal physical...

Heating or cooling of solid metal

C148S547000, C148S548000, C148S654000, C148S660000, C148S661000

Reexamination Certificate

active

07462251

ABSTRACT:
The invention concerns a method for making an abrasion-resistant steel part consisting of 0.1%≦C≦0.23%; 0%≦Si≦2%; 0%≦AI≦2%; 0.5%≦Si+AI≦2%; 0%≦Mn≦2.5%; 0%≦Ni≦5%; 0%≦Cr≦5%; 0%≦Mo≦1%; 0%≦W≦2%; 0.05%≦Mo+W/2≦1%; 0%≦B≦0.02%; 0%≦Ti≦0.67%; 0%≦Zr≦1.34%; 0.05%≦Ti+Zr/2≦0.67%; 0%≦S≦0.15%; N<0.030, optionally 0% to 1.5% of Cu; optionally Nb, Ta and V such that Nb/2+Ta/4+V≦0.5 %; optionally Se, Te, Ca, Bi, Pb contents ≦0.1%; the rest being iron and impurities. Additionally: 0.095%≦C*=C−Ti/4−Zr/8+7×N/8, Ti+Zr/2−7×N/2≦0.05% and 1.05×Mn+0.54×Ni+0.5O×Cr+0.3×(Mo++W1/2)1/2+K>1.8, with K=1 if B≧0.0005% and K=0 if B<0.0005%. After austenitization, the method consists in: cooling at a speed >0.5° C./s between AC3and T=800−270×C*−90×Mn−37×Ni−70×Cr−83×(Mo+W/2) and about T−50° C.; then cooling at a speed 0.1<Vr<150×ep−1.7between T and 100° C., (ep=thickness of plate in mm); cooling down to room temperature and optionally planishing. The invention also concerns the resulting plate.

REFERENCES:
patent: 5645794 (1997-07-01), Beguinot et al.
patent: 5695576 (1997-12-01), Beguinot
patent: 5714116 (1998-02-01), Beguinot et al.
patent: 5900082 (1999-05-01), Hewitt
patent: 6251198 (2001-06-01), Koo et al.
patent: 6423426 (2002-07-01), Kobayashi et al.
patent: 1 072 689 (2001-01-01), None
patent: 410053814 (1998-02-01), None
patent: 10-324952 (1998-12-01), None
patent: 2000199034 (2000-07-01), None
patent: 2000-239791 (2000-09-01), None
patent: WO 98/40522 (1998-09-01), None
Computer-generated English translation of Japanese patent 10-324952, Watari, Koji et al., Dec. 8, 1998.

Affiliated with

Also associated with

Rating

Method for making an abrasion-resistant steel plate does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Method for making an abrasion-resistant steel plate, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for making an abrasion-resistant steel plate will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-4040096