Metal treatment – Process of modifying or maintaining internal physical... – Producing or treating layered – bonded – welded – or...
Reexamination Certificate
2000-04-17
2002-03-26
Wyszomierski, George (Department: 1742)
Metal treatment
Process of modifying or maintaining internal physical...
Producing or treating layered, bonded, welded, or...
C148S565000
Reexamination Certificate
active
06361628
ABSTRACT:
The present invention relates to a process for the compositional setting of a metal product by the addition of at least one substance to this product.
In the current state of iron-and-steel technology, the compositional setting of a steel by means of one or more substances is generally carried out in a steelmaking ladle, a situation which has several drawbacks.
This is because the volumes treated are very large, thereby resulting in a certain lack of flexibility so far as some products require special heats. This is, for example, the case with phosphorus steels. These volumes also result in flux problems often associated with problems of downgrading the steels.
Moreover, the composition of a steel is always isotropic since the compositional setting is carried out in the liquid phase of the metal. It is therefore impossible to produce “composite” steels with a ductile core and a hard shell.
In addition, the crystallization and development of textures giving rise to optimum mechanical properties, such as a high yield stress, a high elongation and drawability, is often difficult in the presence of certain elements such as, for example, carbon and titanium, which could advantageously be introduced after the step of solidifying the metal.
The proposed process according to the invention provides a solution to these various problems.
By virtue of the process according to the invention, the compositional setting of the steels after the solidification step makes it possible to work with standard compositions of very large volume in steel making, something which makes it possible to dispense with special heats and, consequently, to greatly reduce the problems of downgrading. It is even possible to produce very small tonnages of special steels.
It furthermore makes it possible to produce “composite” steels having a compositional gradient between the surface and the core. It is thus possible, for example, to produce steels with a hard shell and a ductile core.
According to the invention, a process is proposed which allows the compositional setting of steels or of other metals after solidification. Thus, the crystallization of an ultralow-carbon steel followed by its compositional setting is possible. This manner of proceeding makes it possible to improve the mechanical properties compared with the case in which the crystallization is obtained with the final composition.
The process according to the invention is one wherein use is made of a metal product in the form of a continuous strip which is moved through a vacuum chamber, wherein the substance is applied to this strip and this substance is made to at least partially diffuse into the strip while it is passing through the vacuum chamber, by maintaining it at a temperature below its melting point but high enough to allow this diffusion.
Advantageously, the strip is preheated before the aforementioned substance is incorporated.
According to one particularly advantageous method of implementing the invention, the addition of the aforementioned substance into the strip is carried out by the technique of sputtering, by the technique of vacuum evaporation, by arc deposition, by decomposition of a carrier gas containing this substance in a plasma or by a combination of two or more of these techniques.
Further details and features of the invention will emerge from the description given below, by way of nonlimiting example, of a few particular embodiments of the invention with reference to the appended figure, which is a schematic representation of a plant for implementing the process according to the invention. In this description, the reference numbers relate to this figure.
In general, the invention relates to a process allowing the chemical composition of a metal to be modified in the solid state, according to which process use is made of a metal product in the form of a continuous strip which is moved continuously through a vacuum chamber, in which a total gas pressure of 10
−4
to 100 torr, for example, obtains and in which a plasma is optionally created, opposite one or both of its faces, so as to introduce, for example by bombardment and/or diffusion, a predetermined substance, present in this chamber, into said strip. This strip is heated and maintained at a temperature high enough to allow at least partial diffusion of this substance into the strip. This temperature is, however, less than the melting point of the material of which the strip is composed. This may, for example, be a strip made of mild steel, stainless steel or aluminum. Thus, in the case of mild steel or stainless steel, the strip is preferably maintained at a temperature of about 600 to 1200° C., whereas in the case of aluminum this temperature is generally about 200 to 600° C.
According to the invention, it is in fact necessary to maintain conditions in the vacuum chamber which are such as to allow this substance to diffuse from the surf ace of the strip toward the core of the latter and thus to allow the composition of the strip to be set.
In order to allow this diffusion, the strip is advantageously preheated and the aforementioned substance is incorporated before or after an annealing step by means of discharges formed, for example, by a plasma.
The appended figure shows an annealing plant in which the compositional setting of a metal strip can be carried out according to the invention, this strip preferably consisting of a steel sheet moving approximately continuously through a vacuum chamber
2
of this plant in which the annealing is carried out by means of plasma discharges.
The discharges are established between the sheet
1
, during its passage through a first zone
10
of this chamber
2
, and a counterelectrode
3
in such a way as to dissipate the electrical power from the discharges in this sheet
1
and thus accomplish the annealing.
More specifically, this is, in fact, a process during which the sheet is bombarded by ions coming from a plasma
4
, allowing rapid and uniform heating and, at the same time, descaling of the surface of the latter.
The plasma may be a DC plasma, the sheet then forming the cathode, or an AC plasma.
In the latter case, use is made of a counterelectrode
3
which extends, facing the sheet
1
, in the vacuum chamber or annealing chamber
2
and has a surface, directed toward the sheet, whose area is greater than that of that part of the sheet which faces it, so as to maintain negative self-biasing of the latter.
As in the conventional process of magnetron sputtering, the discharge may optionally be carried out in the presence of magnetic induction fields by virtue of the presence of magnets
5
close to the sheet
1
and on the opposite side thereof with respect to the counterelectrode
3
.
The power densities dissipated per face in the steel sheet
1
are typically between 1 W/cm
2
and 500 W/cm
2
, while the run speeds of this sheet are generally between 1 m/minute and 1500 m/minute.
The temperature rise takes place in that region of the sheet where the power dissipation takes place, while the rate of temperature rise depends on the matching of the power density used, on the line speed as well as on the thickness of the sheet and on its heat capacity.
In some cases, it may be useful to introduce a temperature hold in the annealing cycle. This may, for example, be obtained by providing, in the vacuum chamber
2
, a zone in which the sheet runs freely at a reduced pressure. In such a case, it is sufficient, for example, to provide a compartment
6
, somewhat isolated from the zone
10
in which the heating takes place by the creation of the plasma. In this regard, it should be noted that, at reduced pressure, the heat losses caused by conduction into the gas are limited and the losses caused by radiation may be recovered in the sheet by means of reflectors or by radiant heating means (not shown).
In yet other cases, it may be useful to cool the sheet
1
in the vacuum chamber
2
, and therefore at a reduced pressure, for example by making the sheet pass over cooling rolls
7
.
According to the invention, the addition of th
Harlet Philippe
Maseri Fabrizio
Renard Lucien
Van Den Brande Pierre
Weymeersch Alain
Browdy and Neimark
Recherche et Developpment du Groupe Cockerill Sambre
Wyszomierski George
LandOfFree
Method for making a composite metal product does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for making a composite metal product, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for making a composite metal product will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2848551