Method for heat-treating recyclings containing oil and iron...

Specialized metallurgical processes – compositions for use therei – Processes – Producing or treating free metal

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C075S658000, C075S694000, C075S962000

Reexamination Certificate

active

06391088

ABSTRACT:

The invention relates to a process for thermal treatment of residual materials containing oil and iron oxide in the form of oily sludges, e.g. sludges from steel mills.
Large quantities of sludges containing iron oxide, which are produced during cleaning of the cooling water from the continuous casting plants or mill trains, occur in the rolling mills in the steel industry. Depending on the granulometry of the iron constituents these sludges are contaminated by oil or grease residues. The oil or grease content increases the finer the granulometry of the constituents. The finest fraction (<40 &mgr;m), which may contain 14% oil, is particularly oily. Because of the high oil content it is difficult to return these sludges to the existing production line. An attempt was thus made to utilise these sludges in sintering plants. However, such high dioxin concentrations were measured during combustion of these sludges that this type of treatment is neither economical nor ecological. These sludges are therefore deposited in artificial lakes and thus pose a potential hazard to the environment, because oil and other residues may enter the ground water.
Typical compositions of these sludges are shown in the following table:
TABLE 1
Fe (%)
Oil (%)
H
2
O (%)
Rolling mill sludges
50-70
2-14
30-40
In this context “oil” is generally understood to mean primarily lubricants and greases, which are used when rolling steel. Accordingly, they are chiefly hydrocarbons containing the various additives customary with these lubricants.
Document DE-C-552 387 relates to a process for the smelting of fine iron ores in a reduction furnace with six hearths. The multiple-hearth furnace is divided into two zones. In the first zone, formed by the top two hearths, the iron ore is initially pre-heated. To do this, hot gases of any suitable kind are supplied in an adjustable quantity. Burners may additionally be used, if appropriate. The second zone, comprising the bottom four hearths, is gastightly insulated from the pre-heating zone. No gas exchange therefore takes place between the two zones. The second zone is intended for the reduction of the iron ore. For this purpose reduction gases are supplied either in the bottom hearth or separately in each individual hearth. The top three hearths of the reduction zone are provided with muffles, to which heating gases are supplied. In this way the heating gases do not come into contact with the ores, and so the composition of the reduction gases can be altered independently of the temperature adjustment.
Consequently the task of the invention is to propose a process for thermal treatment of such residual materials containing oil and iron oxide.
According to the invention this problem is solved by a process for thermal treatment of residual materials containing oil and iron oxide in a multiple-hearth furnace with several hearths one above the other, in which the residual materials containing oil and iron oxide are mixed with a solid reducing agent, introduced continuously into the multiple-hearth furnace, placed on the top hearth and gradually transferred to the lower hearths, the residual materials containing oil and iron oxide being dried on the top hearths, and the oil subsequently evaporated and pyrolised. A gas containing oxygen is injected into the multiple-hearth furnace and reacts with part of the reducing agent to form reduction gas, the reduction gas reacting with the iron oxides to form directly reduced iron, the latter being discharged together with residues of reducing agents in the area of the bottom hearth in the multiple-hearth furnace.
An important advantage of the invention is that by-products are obtained from important constituents of the residual materials containing oil and iron oxide. The iron content can be returned after passing through the process into the production operations of the steel mill, the oil is pyrolised and the resulting pyrolysis gases are burnt. The oil thus contributes to generation of the necessary process heat. Ash consisting essentially of inert materials such as SiO
2
, Al
2
O
3
, MgO, etc. and possibly an excess of reducing agents may remain.
Sludge-type residual materials containing oil and iron oxide can be charged in this process, agglomeration of the particles being prevented by selective process control and continuous circulation. The process supplies a fine-grained end product regardless of the consistency of the feed material.
This is particularly advantageous if ash-forming reducing agents are used. As the solid end product is fine-grained, the ash can easily be separated from the iron. This separation can take place, for example, in the hot condition by screening.
After cooling below 700° C. it is possible on the other hand to separate the reduced iron via magnetic separators from the ash and excess reducing agent. The quality of the directly reduced iron obtained in this way is virtually independent of the quantity of residues of the reducing agent.
The iron obtained can subsequently be processed into briquettes or introduced directly into a melting furnace (electric furnace, etc.) and further processed.
The reducing agent residues produced can be used with any unused reducing agents in a separate gasification reactor, the ash-forming constituents being advantageously separated as liquid slag and the crude gas formed used in the multiple-hearth furnace as combustion or reducing gas. Accordingly it is also possible to use a cheaper reducing agent with a relatively high ash content and/or work with a relatively high excess of reducing agent, which prevents agglomeration of the residual materials.
When working with excess reducing agents it is advantageous to process the residues in order to separate and reuse the unused reducing agents. This can be done, for example, by screening the residues, if the unused reducing agents are present in sufficiently coarse form. The unused reducing agents can be introduced directly into the multiple-hearth furnace.
However, part of the required reducing agent can also be deposited on one or more hearths at lower levels in the furnace.
It is thus possible that coarse-grained reducing agents (1-3 mm) are introduced at higher levels in the multiple-hearth furnace and fine-grained reducing agents (<1 mm) further below. Consequently discharge of dust with the waste gases is largely avoided and the reaction accelerated by the fine reducing agent particles introduced further below.
Consumption of reducing agents is reduced by the charging of coarser particles, because the small particles are quickly consumed by reaction with H
2
O and CO
2
from the waste gas in the upper hearths, on which an oxidising atmosphere prevails. The reduction gases in the furnace can be adjusted to an optimum concentration by selective feed of reducing agents in the lower hearths of the furnace with the result that a higher degree of metallisation can be achieved.
The process space is subdivided into different zones, the solids move continuously from the top downwards and the gases are conducted from the bottom upwards through the furnace. By subdividing the process space into different zones the process conditions in the different zones or even for each hearth can be measured and selectively influenced if required.
The residual materials containing oil and iron oxide are circulated continuously by rakes mounted on each furnace hearth and conveyed gradually to the underlying hearth.
Agglomeration of the reducing agents and residual materials containing oil and iron oxide is prevented by the continuous circulation. The rate of circulation depends on many factors such as the geometry of the rakes, the thickness of the layers, etc. The residual materials containing oil and iron oxide, the reducing agents and any reduced iron on the hearths should be circulated at least once every one to three minutes with the result that agglomeration is largely prevented.
Gases containing oxygen can be injected on the hearth, where the heat requirement must be covered by combustion of the excess process gases.
It is advanta

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Method for heat-treating recyclings containing oil and iron... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Method for heat-treating recyclings containing oil and iron..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for heat-treating recyclings containing oil and iron... will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2885051

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.