Electrolysis: processes – compositions used therein – and methods – Electrolytic coating – Coating selected area
Reexamination Certificate
2001-11-21
2004-11-02
King, Roy (Department: 1742)
Electrolysis: processes, compositions used therein, and methods
Electrolytic coating
Coating selected area
C205S182000, C205S186000, C205S192000, C205S205000, C205S210000, C438S618000, C438S622000, C438S687000
Reexamination Certificate
active
06811670
ABSTRACT:
FIELD OF THE INVENTION
This invention generally relates to electroplating cathode contact areas and more particularly to a method for forming electroplating cathode contact areas with increased strength.
BACKGROUND OF THE INVENTION
In semiconductor fabrication, various layers of insulating material, semiconducting material and conducting material are formed to produce a multilayer semiconductor device. The layers are patterned to create features that taken together, form elements such as transistors, capacitors, and resistors. These elements are then interconnected to achieve a desired electrical function, thereby producing an integrated circuit (IC) device. The formation and patterning of the various device layers are achieved using conventional fabrication techniques, such as oxidation, implantation, deposition, epitaxial growth of silicon, lithography, etching, and planarization.
Sub-micron multi-level metallization is one of the key technologies for the next generation of ultra large scale integration (ULSI). The multilevel interconnects that lie at the heart of this technology require planarization of interconnect features formed in high aspect ratio apertures, including contacts, vias, metal interconnect lines and other features. Reliable formation of these interconnect features is very important to the success of ULSI and to the continued effort to increase circuit density and quality on individual substrates and die.
Copper and copper alloys have become the metal of choice for filling sub-micron, high aspect ratio interconnect features on semiconductor substrates. Copper and its alloys have lower resistivity and higher electromigration resistance compared to other metals such as, for example, aluminum. These characteristics are critical for achieving higher current densities increased device speed.
As circuit densities increase, the widths of vias, contacts, metal interconnect lines, and other features, decrease to sub-micron dimensions, whereas the thickness of the dielectric layers, through the use low-k (low dielectric constant) materials, has remained substantially constant. Consequently, the aspect ratios for the features, i.e., their height divided by width, has increased thereby creating additional challenges in adequately filling the sub-micron features with, for example, copper metal. Many traditional deposition processes such as chemical vapor deposition (CVD) have difficulty filling increasingly high aspect ratio features, for example, where the aspect ratio exceeds 2:1, and particularly where it exceeds 4:1.
As a result of these process limitations, electroplating or electrodeposition, which has previously been limited to the fabrication of patterns on circuit boards, is now emerging as a preferable method for filling metal interconnects structures such as via openings (holes) and trench line openings on semiconductor devices. Typically, electroplating uses a suspension of positively charged ions of deposition material, for example metal ions, in contact with a negatively charged substrate, as a source of electrons, to deposit (plate out) the metal ions onto the charged substrate, for example, a semiconductor wafer. A thin metal layer (seed layer) is first deposited on the semiconductor wafer and in etched features to provide an electrical path across the surfaces. An electrical current is supplied to the seed layer whereby the semiconductor wafer surface is electroplated with an appropriate metal, for example, aluminum or copper.
One exemplary process for forming a series of interconnected multiple layers, for example, is a dual damascene process. Although there are several different manufacturing methods for manufacturing damascene structures, all such methods employ a series of photolithographic masking and etching steps, typically by a reactive ion etch (RIE). In the typical multilayer semiconductor manufacturing process, for example, a dual damascene process, a series insulating layers are deposited to include a series of interconnecting metallization structures such as vias and metal line interconnects to electrically interconnect areas within the multilayer device and contact layers to interconnect the various devices on the chip surface. In most devices, pluralities of vias are separated from one another along the semiconductor wafer and selectively interconnect conductive regions between layers of a multi layer device. Metal interconnect lines typically serve to selectively interconnect conductive regions within a layer of a multilayer device. Vias and metal interconnect lines are selectively interconnected in order to form the necessary electrical connections. In forming a dual damascene structure via openings (holes) and trench line openings are etched into the insulating layers and are back-filled with metal. The insulating layers where metal interconnect lines (trench lines) are formed are typically referred to as metallization layers and the insulating layer including interconnecting vias are referred to as intermetal dielectric (IMD) layers. The IMD layers are preferably a low-k (low dielectric constant) insulating material which reduces signal delay times caused by parasitic capacitance. The process by which via openings (holes) and trench lines are selectively etched into the insulating layers is typically a photolithographic masking process, followed by a reactive ion etch (RIE) process, both of which are commonly known in the art.
In filling the via openings and trench line openings with metal, for example, copper, electroplating is a preferable method to achieve superior step coverage of sub-micron etched features. The method generally includes first depositing a barrier layer over the etched opening surfaces, such as via openings and trench line openings, depositing a metal seed layer, preferably copper, over the barrier layer, and then electroplating a metal, again preferably copper, over the seed layer to fill the etched feature to form, for example, vias and trench lines. Finally, the deposited layers and the dielectric layers are planarized, for example, by chemical mechanical polishing (CMP), to define a conductive interconnect feature.
Metal electroplating in general is a well-known art and can be achieved by a variety of techniques. Common designs of cells for electroplating a metal on semiconductor wafers involve positioning the plating surface of the semiconductor wafer within an electrolyte solution including an anode with the electrolyte impinging perpendicularly on the plating surface. The plating surface forms the cathode of the plating system such that ions in the plating solution deposit on the conductive portion of the plating surface.
One method for providing power to the plating surface uses, for example cathode contacts (e.g., pins, ‘fingers’, or springs) which contact the plating surface which includes a seed layer of metal. The cathode contacts make contact with the cathode contact area which includes a seed layer formed as close as possible to the edge (periphery) of the semiconductor wafer to minimize the wasted area on the wafer due to the cathode contact areas. In the prior art, the seed layer in the cathode contact areas at the edge of the wafer have typically been formed over an uppermost insulating (IMD) layer devoid of etched semiconductor features such as vias and trench lines. In order to minimize resistance between the cathode contacts and the cathode contact areas, force is applied to the cathode contacts to assure intimate contact with the seed layer in the cathode contact areas. A shortcoming in the prior art is that, frequently, the electroplating process results in the delamination or peeling of the uppermost insulating (IMD) layers, especially underlying the cathode contact areas, due to the stress induced by the force applied by the cathode contact to the cathode contact area.
The problem is exacerbated by the use of low-k (low dielectric) material in insulating (IMD) layers, for example, carbon doped silicon dioxide. In order to reduce signal delays caused by parasitic effects related to the capa
Liu Chung-Shi
Yu Chen-Hua
King Roy
Leader William T.
Taiwan Semiconductor Manufacturing Co. Ltd
Tung & Associates
LandOfFree
Method for forming cathode contact areas for an... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for forming cathode contact areas for an..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for forming cathode contact areas for an... will most certainly appreciate the feedback.