ABSTRACT:
A method for the fabrication of a superplastic composite material having metallic aluminum reinforced with silicon nitride includes thoroughly mixing silicon nitride with metallic aluminum, pressure-sintering the resultant mixture, further heating and pressing the sintered mixture, hot extrusion-molding the resultant sintered article, subjecting the molded article, when necessary, to a heat treatment such as the T6 treatment thereby forming a superplastic composite material, and deforming the composite material in a temperature region in which the material exhibits superplasticity.
REFERENCES:
patent: 4797155 (1989-01-01), Das
patent: 4894088 (1990-01-01), Yamaguchi et al.
patent: 4941918 (1990-07-01), Horikoshi et al.
patent: 4946500 (1990-08-01), Zedalis et al.
Superplasticity at High Strain Rates in a SiC Whisker Reinforced Al Alloy, vol. 18, pp. 1405-1408 (1984), T. G. Nieh et al.
Superplasticity in SiC Reinforced Al Alloys, vol. 2 (1986), A Composite Material of 7475 Al Alloy Reinforced with SiC Whiskers; M. W. Mahoney et al., Six International Conference on Composite Materials ICCM and ECCM.
Superplasticity in a High Strength Powder Aluminum Alloy With and Without SiC Reinforcement, Metallurgical Transactions A, vol. 18A (1987), p. 653, A Composite Material of 7064 Al Alloy Reinforced with Minute SiC Particles, M. W. Mahoney et al.
Influence of Anisotropic Distribution of Whiskers on the Superplastic Behavior of Aluminum in a Back-Extruded 6061 Al-20% SiC.sub.w Composite, Composites Science and Technology, 35 (1989), pp. 105-120, G. Gonzalez-Doncel et al.
Superplasticity in Silicon Nitride Whisker Reinforced 2124 Aluminum Alloy Composite, vol. 39, No. 11, Tsunemichi Imai et al., pp. 831-835.
Imai Tsunemichi
Mabuchi Mamoru
Agency of Industrial Science & Technology
Lechert Jr. Stephen J.
Ministry of International Trade & Industry
LandOfFree
Method for fabrication of superplastic composite material having does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for fabrication of superplastic composite material having, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for fabrication of superplastic composite material having will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-1695257