Stock material or miscellaneous articles – Three dimension imitation or 'treated' natural product
Reexamination Certificate
2000-01-14
2002-04-23
Jones, Deborah (Department: 1775)
Stock material or miscellaneous articles
Three dimension imitation or 'treated' natural product
C428S426000, C428S432000, C428S542200, C428S543000, C427S126200, C427S126300, C427S140000, C427S217000
Reexamination Certificate
active
06376031
ABSTRACT:
FIELD OF THE INVENTION
The present invention relates to methods for enhancing the color of gemstones and to novel colored gemstones produced by invention methods.
BACKGROUND OF THE INVENTION
A variety of materials having the physical and aesthetic properties desirable for use as gemstones are widely available. However, many of these materials but do not always have an aesthetically pleasing appearance. A variety of procedures have been employed in the art to improve the physical and/or aesthetic properties of minerals, e.g., electron beam irradiation, Cobalt-60 irradiation, neutron bombardment, exposure to intense heat, and the like.
Each of the above-described prior art methods suffer from significant drawbacks in terms of cost, safety, efficacy, and the like. For example, Carr, et al.,in U.S. Pat. No. 3,950,596, describe methods for coloring corundum crystals by heating them to temperatures of 1600° C. or higher while in contact with a powder composed primarily of alumina, with added metal oxides as colorants. However, even at such high temperatures (where furnace time is expensive) the Carr method requires from 20 to 200 hours. If the temperature were reduced even to 1350° C. (well above temperatures employed in the present invention) general chemical principles would predict that the reaction would take years to run. Furthermore metals such as cobalt, that melt at such high temperatures, cannot be used as colorants.
Other methods are used for coloring non-gemstone alumina. For example, in U.S. Pat. No. 4,732,867, Schnable describes methods for implanting ions such as cobalt in order to make identifying marks in alumina chips. However, as recognized by Schnable, the method is not particularly effective for providing lasting color. Furthermore the colors achieved by ion implantation are not very vivid depite the sophisticated and expensive-to-operate machinery required.
Therefore, it would be desirable to be able to readily impart enhanced and/or modified color to materials useful as gemstones employing readily practiced methods which do not suffer from the drawbacks of prior art methods.
BRIEF DESCRIPTION OF THE INVENTION
In accordance with the present invention, methods have been developed for enhancing the color of minerals useful as gemstones, by heating them to moderate temperatures while in contact with powdered cobalt or cobalt oxide (or precursors thereof) and in the absence of alumina. Given the length of time required for prior art methods to take place at much higher temperatures (such as that of Carr, above), under generally recognized chemical principles, one would not expect invention methods to work during the average human lifetime at the moderate temperatures contemplated herein. As shown herein, however, invention methods are useful for enhancing the color of minerals while unexpectedly employing substantially lower temperatures, and for substantially shorter times, than predicted by the prior art. Invention methods are relatively inexpensive to carry out, avoid the use of hazardous materials and require no specialized equipment.
DETAILED DESCRIPTION OF THE INVENTION
In accordance with the present invention, there are provided methods for enhancing the color of gemstones, said methods comprising:
subjecting a combination of a gemstone and at least one non-alumina treating agent, wherein said treating agent comprises a powdered (i.e., finely divided) form of cobalt metal or cobalt oxide (or precursor thereof) to conditions suitable to enhance the color of said gemstone, without causing a significant level of surface damage to said gemstone.
A wide variety of minerals can be treated according to the present invention. Examples of suitable minerals contemplated for use herein (thereby rendering them useful as gemstones) include topaz, chrysoberyl, sapphire, quartz, garnet, and the like. As used herein, “gemstone” refers to transparent (non-opaque), single crystal minerals useful both as gemstones and/or in optical applications.
A wide variety of metals can be employed in combination with the cobalt metal or cobalt oxide (or precursors thereof) as the major component of treating agent used in the invention process. Examples of suitable metals include transition metals, as well as other metals which can modify the color imparted by the treating agent and/or the mineral being treated.
A wide variety of metal oxides can also be employed in combination with the cobalt metal or cobalt oxide (or precursors thereof) as the major component of treating agent used in the invention process, optionally in further combination with a plurality of the metals set forth hereinabove. Examples of suitable metal oxides include transition metal oxides, as well as other metal oxides which can modify the color imparted by the treating agent and/or the mineral being treated.
Metals and metal oxides contemplated for use in invention methods are preferably employed in a powdered (i.e. finely divided) form in order to maximize contact between the gemstone and the treating agent. As is readily understood by those skilled in the art, a range of particle sizes is suitable for the powdered, or finely divided treating agent. Particles that will pass through the openings of a standard screen of mesh size up to about 400 are contemplated within the present invention. Preferred particles are of a size that will pass through a standard screen of up to about 200 mesh.
As used herein, the term “enhance” and any variations thereof, refer to an increase or modification in the color of minerals treated by invention methods, thereby rendering the mineral more valuable as a gemstone. Enhanced colors which can be imparted by the invention process can be varied based on such variables as the particular gemstone being treated, the particular treating agent (s) employed, the conditions to which the gemstones are subjected, and the like. For example, topaz can be modified to have a light blue to dark blue color, or a light green to dark green color, or a light blue-green to dark blue-green color, or a light green-blue to dark greenblue color, depending on the treating agent(s) and treating conditions employed. Similarly, chrysoberyl can be modified to have a light green to a deep blue-green color; sapphire can be modified to have a light blue to a dark blue color (if clear stones are used for treatment) or green, yellow-green or blue-green stones can be produced if the untreated stones are yellow; quartz can be modified to have a light pink to a dark pink color; garnet can be modified to have a green to a blue-green color; and the like.
A wide range of treating conditions can be employed in the practice of the present invention. Typically conditions suitable to enhance the color of a gemstone, without causing a significant level of surface damage thereto, comprise subjecting the combination of gemstone and at least one powdered (i.e., finely divided) form of cobalt metal or cobalt oxide (or precursors thereof) to a temperature in the range of about 825° C. up to about 1050° C. for a time in the range of about 3 up to about 200 hours or more (up to about 6 weeks). Presently preferred temperatures contemplated for use herein fall in the range of about 875° to about 925° C. Typically such contacting is carried out at ambient pressure.
Generally, longer exposure times and/or higher exposure temperatures lead to a greater intensity of color being imparted to the mineral being treated, as well as impacting the degree of color saturation achieved by the process. As readily recognized by those of skill in the art, higher treating temperatures are also possible (i.e., >1050° C.). Such temperatures are likely, however, to cause significant damage to the surface of the mineral being treated, while also providing higher color saturation. The resulting treated gemstone could be polished to remove the surface damage, thereby providing a color-enhanced gemstone with a satisfactory surface finish.
As will be readily appreciated by those of skill in the art, any method which causes significant surface damage to minerals,
Bahta Abraham
Foley & Lardner
Forrestal Kevin J.
Jones Deborah
Reiter Stephen E.
LandOfFree
Method for enhancing the color of minerals useful as gemstones does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for enhancing the color of minerals useful as gemstones, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for enhancing the color of minerals useful as gemstones will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2840852