Chemistry: electrical current producing apparatus – product – and – Current producing cell – elements – subcombinations and... – Electrode
Reexamination Certificate
2001-02-06
2003-12-16
Ruthkosky, Mark (Department: 1745)
Chemistry: electrical current producing apparatus, product, and
Current producing cell, elements, subcombinations and...
Electrode
C029S623100
Reexamination Certificate
active
06664003
ABSTRACT:
BACKGROUND
Silver in amounts of 0.02-0.06% has been added to the positive grid alloys for SLI service. Silver not only decreases the rate of oxidation of the positive grid, but it also decreases the rate of corrosion and growth of the battery grid during service life.
As batteries containing silver in the positive grid are returned for recycling, the silver content of recycled lead has increased markedly. Because silver decreases the rate of oxidation of lead, as the silver content of recycled lead has increased, the rate of oxidation of this lead to produce leady lead oxide for use as active material in lead-acid batteries has also decreased.
Barton pots are used to produce lead oxide for batteries. In the Barton process, molten lead is reacted with air to produce lead oxide. In Barton pot reactors, the reduced rate of oxidation due to the higher silver content of the recycled lead has resulted in lower oxide production rates, higher free lead in the oxide product, and larger oxide particles. The airflow through the Barton pot must be increased to account for the reduced oxidation rate of the silver containing lead. The Barton pots have become much more difficult to regulate when lead of variable silver content from lot to lot is used.
Lead oxidizes at a faster rate than silver. During operation of the Barton pots, a buildup of material can occur in the reactors. This material has the consistency of sand, which will not melt, oxidize, or be swept out of the mill. When the sandy material builds up to an unacceptable level, the oxide reactor must be stopped, the sandy material removed, and the reactor restarted. Downtime from the sandy material generation has increased as the silver content of the lead used for oxide production has increased.
In ball mills used to produce the leady oxide for the active material of the batteries, the oxidation of the lead occurs on the surface of solid lead particles. Due to attrition of the lead by impact with other lead particles, the oxide and some metallic lead are released. The free lead content and rate of production of the oxide is controlled by the rate of air movement through the ball mill and the return of heavier unreacted particles back to the ball mill.
As the silver content of the lead has increased, the amount of recirculating lead in the ball mill system has also increased. In addition, because of the reduced rate of reaction, the free lead content of the resultant leady oxide is more difficult to control.
Antimony in amounts of 0.002-0.004% has been added to the lead for many years to increase the rate of oxidation of the lead in Barton pot reactors and to smooth out variations in the rate of oxidation of the lead caused by variations in the silver content. As the silver content of the lead has increased, higher antimony additions have been required to assure uniform oxide production.
Antimony additions to the active material of lead acid batteries were not a problem as long as the grids of the batteries were constructed of lead alloys containing antimony. With the advent of maintenance-free batteries containing lead-calcium based grid alloys instead of lead-antimony alloys, the use of antimony for control of oxidation of the lead can cause an increased rate of gassing at the negative electrode. Antimony may also cause higher rates of water loss with consequent shorter battery life because water cannot be readily added to the maintenance-free batteries. As silver has increased in the lead to produce oxide, antimony additions at levels unacceptable for maintenance-free batteries are required to increase the rate of lead oxidation.
Higher silver content in the battery oxide and increased free lead of the oxide resulting from reduced rates of oxidation in the reactors can also cause problems in the curing or hydroset process. The battery oxide containing small metallic lead particles (free lead), water, sulfuric acid and additives are mixed together to form a paste. The leady oxide mixture is pasted onto lead alloy grids to produce plates or electrodes for the lead acid batteries.
The plates undergo a curing or hydroset process wherein oxygen and the water in the paste reacts with the free lead in the oxide portion of the mix to convert the free lead into basic lead sulfates which cement the materials together. Battery production plants generally attempt to reduce the free lead of the finished cured plates to less than 3% from a starting oxide free lead of 20-35%.
As the silver content of the lead used to produce the oxide for the battery active material has increased, the rate of reaction of the free lead in the pasted plates during the curing or hydroset process has also decreased. It has become more difficult to reach the lower free lead requirements of the production process as the silver content has increased, resulting in scrapped or reworked cured plates.
SUMMARY OF THE INVENTION
This invention provides an improved method for producing lead oxide for lead-acid batteries. In accordance with the invention, the rate and extent of oxidation of lead in battery oxide production, particularly where silver is present in the lead, is increased by the presence of at least about 0.001 weight percent magnesium alloyed with the lead being oxidized. The method comprises alloying magnesium with the lead and thereafter subjecting the magnesium-lead alloy to oxidizing conditions such as those used in a Barton pot reactor, a ball mill or during the curing or hydrosetting processes.
Generally, magnesium additions between about 0.001 and 0.010 weight percent are made, most preferably 0.002 to 0.005 weight percent. The presence of the magnesium increases the rate of oxidation of lead. It can offset the reduced oxidation rate observed in lead containing silver. The invention improves battery production by reducing the problems noted above with respect to recycled lead containing silver, including increasing the rate of curing the battery paste.
DETAILED DESCRIPTION OF THE INVENTION
This invention overcomes the reduced rate, extent and quality of oxidation of the lead during lead-acid battery production caused by increased silver contents in lead. The invention utilizes an addition of magnesium to the lead to accelerate oxidation, reduce the amount of free lead and improve oxidation during curing. The addition of the magnesium to the lead improves the reactivity of the lead at all stages of lead oxide production and utilization, including during Barton pot reactor processes, ball milling processes and hydrosetting processes.
The invention utilizes magnesium added in amounts sufficient to produce 0.001-0.010 weight percent magnesium in the lead. Presence of this magnesium accelerates the oxidation of the lead containing silver in Barton pots, ball mills and during curing. Magnesium additions also reduce the free lead content of the oxide and the number of large oxide particles.
Magnesium addition not only accelerates the oxidation of lead and reduces operating problems caused by silver content in the lead during production of the leady oxide; it also enhances the curing of the leady oxide on the electrode. It is believed that magnesium accelerates the oxidation of lead in the curing process by increasing the pH of the water in the proximity of the free lead particle. Lead is resistant to corrosion and oxidation in acid environments, particularly H
2
SO
4
environments. Lead, however, is readily corroded in alkaline environments. Addition of magnesium to the lead for oxide production results in production of Mg(OH)
2
at the surface of the magnesium doped free lead particle when it is mixed with water. The Mg(OH)
2
is a highly basic material which increases the pH of the water to which it is added. In the proximity of the free lead particle, it accelerates the reaction of free lead to basic lead sulfates during the curing process. The addition of 0.001-0.010% magnesium to lead overcomes the negative effects of silver in the curing or hydroset process.
The magnesium in the cured plate can also have a beneficial effect on the performance of the batt
Prengaman R. David
Siegmund Andreas
Gillis Theresa M.
RSR Technologies, Inc.
Ruthkosky Mark
LandOfFree
Method for enhancing lead oxidation during production of... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for enhancing lead oxidation during production of..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for enhancing lead oxidation during production of... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3168127