Electrolysis: processes – compositions used therein – and methods – Electrolytic coating – Forming nonmetal coating
Reexamination Certificate
2000-08-07
2002-02-12
Mayekar, Kishor (Department: 1741)
Electrolysis: processes, compositions used therein, and methods
Electrolytic coating
Forming nonmetal coating
C205S320000, C205S198000, C072S041000, C072S046000
Reexamination Certificate
active
06346186
ABSTRACT:
BACKGROUND OF THE INVENTION
The invention concerns a method for electrochemical phosphating of metal surfaces, particularly stainless steel, in connection with cold forming of metal workpieces, which method provides the cold formed workpiece with a lubricant after the phosphating, particularly molybdenum disulphide or sodium stearate. The invention also concerns the application of an aqueous phosphating solution with a method of the kind described above.
In connection with cold forming of metal workpieces, e.g. steel workpieces, it is known that a better result is obtained if the cold formed workpiece is provided with a lubricant. It could be a glass-based lubricant melting during the strong heat development, thus having a lubricating effect, c.f. e.g. EP 0 043 639 B1 describing electrophoretic application of a glaseous lubricant, in this case on a titanium workpiece, or the lubricant could be e.g. molybdenum disulphide or sodium stearate. To obtain a better adhesion of the lubricant on cold formed workpieces, a precoat is often added first.
Cold formed iron and standard steel workpieces are often provided with a precoat of zinc phosphate or zinc calcium phosphate, applied chemically during a pure immersion process, c.f. U.S. Pat. No. 4,517,029. This process is not used with stainless steel due to the increased corrosion resistance. Zinc phosphate can be applied on iron, standard steel and zinc-plated steel through an electrochemical process, c.f. e.g. EP 0 653 502 A2, however, this process is used for corrosion protection and proor paint.
Besides, it is Known from Journal of Materials Science 29, 949-953 (1994) to provide stainless steel with calcium hydrogen phosphate through a similar process when producing bio-implants.
Summing up, it can be stated that the state of the art shows an extensive use of lubrication of cold formed workpieces through immersion or dipping, whereas, to the best of our knowledge, electrochemical application has until now never been used for cold forming.
SUMMARY OF THE INVENTION
According to the invention, it has turned out that electrochemical phosphating of metal surfaces, particularly stainless steel, when cold forming metal workpieces, can be made with a good result, when a lubricant, as e.g. molybdenum disulphide or sodium stearate, is applied on the cold formed workpiece after the phosphating, when carrying through an electrochemical phosphating through a cathodic process using an aqueous phosphating solution containing:
0.5 to 100 g Ca
2+
/l
0.5 to 100 g Zn
2+
/l
5 to 100 g PO
4
3−
/l
0 to 100 g NO
3
−
/l
0 to 100 g ClO
3
−
/l and
0 to 50 g F
−
or Cl
−
/l
with the ratio of Ca
++
/Zn
++
being greater than 1, and where temperature of the solution is between 0 and 95° C., the pH-value of the solution is between 0.5 and 5, and the current density is between 0.1 and 250 mA/cm
2
.
The addition of calcium to the phosphating solution involves some surprising improvements during precipitation, as calcium partly improves the initiation of the precipitation, partly provides a more dense layer than pure zinc phosphate. The improved initiation means that a lower current is required for the precipitation, and the increased density and thus the decreasing electrical conductivity of the precoat means that the process is less sensitive to the geometrical configuration of the workpiece to be phosphatised. Thus the coating of e.g. the inside of a cup is possible, without requiring a change of the geometrical configuration of the anode, which increases the applicability of the process substantially when compared with the known processes. Further, the addition of calcium gives a reduced friction when compared with pure zinc phosphate.
The invention also concerns the application of an aqueous phosphating solution 4 for electrochemical phosphating of metal surfaces, particularly stainless steel, by which the cold formed workpiece are provided with a lubricant after the phosphating, particularly molybdenum disulphide or sodium stearate.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
The present invention enables precipitation of a phosphate layer having a thickness appropriate for cold forming, and additionally the applied addition of calcium causes an improvement of the precipitation initiation, improves the applicability of the process for workpieces having a complicated geometrical configuration, and reduces friction. Additionally, a polymer, when added, is incorporated in and thus improving the coating. Besides, the addition of F
−
gives a better adhesion, particularly to stainless steel surfaces, and thus a more expedient texture is obtained than with ordinary phosphating. Cl
−
can be used instead of F
−
. The application of NO
3
−
and/or ClO
3
−
limits the formation of bubbles on the workpiece surface.
The following table shows a number of examples demonstrating a series of typical test results obtained by using the method according to the invention. The properties of the precipitated coatings are tested through cup pressing, by which a piston is pressed against the workpiece placed in a die or a holder. When measuring the piston pressure as a function of the cup height, the decomposition of the lubricant film can be registered as an increase in the piston pressure caused by increased friction. The maximum cup height is the one at which the piston pressure has increased to the same level as the static piston pressure when starting the cup pressing.
It appears from the table that a known procedure (c.f. examples 1 and 1a) at a temperature of 70° C., pulsating current and a pulse-pause relation of 0.25 and a duration of the coating process of 10 minutes will give a maximum cup height of 27 mm; the obtained layer is very porous, has a poor adhesion and often is “caked”, i.e. in the form of flakes. The application of an aqueous phosphating solution with the method according to the invention, c.f. examples 4 to 6, enables applying the precoat at temperatures as low as 25° C., without requiring special equipment for pulsation of the current, i.e. pure DC, and for a much shorter time, approx. 3 minutes. Additionally, larger cup heights can be obtained, c.f. examples 5 and 6. The use of a water soluble polymer, c.f. example 6, for which an ordinary, commercially available polymer (polyethylene glycol in the form of PEG 1000) is used, will give a more robust coating.
The coating obtained in accordance with the invention is very tight and uniform, facilitates the handling of cold formed workpieces, and permits transport without risking that the coating falls off. The method according to the invention can also be used in connection with other processes than cold forming, e.g. for corrosion protection and provision of a substrate for paint.
Known prior art uses small amounts of calcium on an interchangeable basis with metals such as iron or nickel to regulate parameters in the bath. The invention of this application has recognized use of calcium for improving lubrication and precipitation. In accordance with the invention, it is not possible to use the same large amounts of iron or nickel instead of calcium, as this will cause the precipitation to be slow and also cause seizure during cold forming. The prior art has not recognized the unique property of calcium when used in large amounts.
Calcium is used as a main ingredient in the solution. As will be seen from examples 3 through 6 following, the calcium content in the aqueous solution is equal to or greater than the zinc content, which is a marked difference from conventional phosphatization. Thus, in accordance with the present invention, the relation of Ca
++
/Zn
++
is greater than 1. The large calcium content in the solution results in the phosphate layer being precipitated on the workpiece with a high content of calcium. For example, calculated from example 5 following, the calcium is 23.9% by weight and the zinc is 25.6% by weight, or, expressed in g/m
2
, 10.5 g/m
2
calcium and 11.3 g/m
2
zinc. The la
Bjerrum Niels Janniksen
Christensen Erik
Steenberg Thomas
Danfoss A/S
Lee, Mann, Smith McWilliams, Sweeney and Ohlson
Mayekar Kishor
LandOfFree
Method for electrochemical phosphating of metal surfaces does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for electrochemical phosphating of metal surfaces, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for electrochemical phosphating of metal surfaces will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2968250