Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – Treating polymer containing material or treating a solid...
Reexamination Certificate
2001-11-15
2002-10-15
Boykin, Terressa M. (Department: 1711)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
Treating polymer containing material or treating a solid...
Reexamination Certificate
active
06465608
ABSTRACT:
The present invention relates to a method for drying and degassing polyolefins in which the polymerization product leaving the polymerization reactor is decompressed and then brought into contact with a degassing medium. The invention also relates to a polyethylene prepared in this way.
The invention basically relates to all industrially feasible variants of the method of olefin polymerization, such as suspension polymerization, gas-phase technology, solution polymerisation and combinations thereof (cascade technology).
The solid polymerization product obtained after the polymerization reaction usually still contains, as impurities, certain amounts of unconsumed starting materials and of solvents employed in the polymerization. The drying and degassing of the polymerization product which are necessary for safety, environmental and organoleptic reasons generally mean high costs, since, in particular, relatively high-boiling comonomers can only be removed slowly and thus at high cost.
A known degassing method comprises employing ethylene directly as a degassing medium, since in this way closed circuits to the polymerization reactor are possible. Thus, EP-A-0 341 540 describes a method in which, after pressure reduction, the reaction mixture is separated into a gaseous phase and a solid phase. The solid phase is then firstly pre-rinsed continuously with gaseous ethylene and, in a second step, post-rinsed with N
2
/H
2
O. Post-polymerization is not mentioned in this specification, but instead the same degassing efficiency as with inert gas is described. However, it has been found, disadvantageously, in a practical experiment that the method disclosed in this citation can result in considerable fisheye formation due to the presence of the ethylene.
Direct incorporation of unconsumed starting materials, in particular the relatively high-boiling comonomers, into the polymer product before deactivation of the catalysts is explicitly mentioned in EP-A-0 801 081. The degassing is carried out using an ethylene/hydrogen mixture in addition to inert gas, and it has been found to be particularly advantageous that the post-polymerization causes the liberation of heat energy, with the aid of which the degassing is accelerated.
A further method is described in EP-A-0 728 772 for gas-phase reactors.
In this method, the product is, as usual hitherto, discharged by opening a valve located in the polymerization reactor. However, the product is not conveyed directly into the degassing tank, but instead is firstly transferred into a so-called intermediate tank, which is subsequently closed again via valves, and where a post-polymerization takes place under substantially identical temperature and pressure conditions as in the actual reactor. The problem in this method is that the intermediate tank easily becomes blocked, and that the usual fluidized-bed density is firstly discharged from the polymerization reactor, i.e. a large amount of compressed reactor gas is discharged concomitantly per product mass unit. In addition, the sealed reaction space means that the monomer mixture present is initially depleted in ethylene, and low-density polyethylene thus tends to form. However, the sealed polymerization space means that the proportion of polymer formed here is negligible and thus does not influence the product properties to a significant extent.
EP-B 127 253 has likewise already described a method for drying and degassing polyolefins in which the degassing medium employed is the monomer to be polymerized. However, no polymerization takes place in the degassing tank there, but instead the mixture of desorbed monomers and monomers serving as degassing medium is fed back into the polymerization reactor, where the polymerization then takes place. This citation does not give any indication to the person skilled in the art of the particular way in which the method is carried out in accordance with the present invention.
The object of the present invention was to indicate a method for drying and degassing solid polyolefin in which the effectiveness of the drying or degassing is increased through specific use of post-polymerization in the decompression zone and at the same time the polymer properties can be influenced in a very targeted manner through the post-polymerization in the degassing step. A further object was to provide a polyethylene prepared in this way.
This object is achieved by a method of the generic type mentioned at the outset, whose characterizing feature is to be regarded as that the degassing medium employed is the monomer to be polymerized, which flows through the decompression tank in a circulation process, and in that polymerization takes place in the degassing tank in an amount of up to 10%, based on the total polymerization conversion.
In a particularly preferred embodiment of the method according to the invention, the degassing medium flowing through the decompression tank in a circulation process is enriched with ethylene or other low-boiling olefins in an amount in the range from 0 to 100 mol %, based on the total amount of circulating gas, and is subjected to temperature control.
The temperature conditions within the decompression tank are matched to the requirements inasmuch as the temperature is usually from 5 to 10 K above the temperature prevailing in the polymerization reactor.
Through the method according to the invention, some or even all of the total amount of olefin starting material required can be introduced into the process via the decompression tank. A gas separation unit is accordingly not necessary in accordance with the invention.
In a particularly preferred embodiment of the method according to the invention, the decompression tank employed is a fluidized-bed reactor. Use of a fluidized-bed reactor of this type in the degassing zone is known per se: thus, heated hydrocarbon gas is used as stripping gas in WO-A-93/13843.
U.S. Pat. No. 4,424,341 describes successive pressure reduction in the downstream area. The aim is to be able to re-liquefy the evaporated fraction of suspension medium by simple cooling. According to the teaching in this citation, the first decompression tank is operated as a fluidized bed.
The method according to the invention enables the preparation of polyolefins from olefins having from 2 to 20 carbon atoms, preferably from 2 to 10 carbon atoms. The monomers employed can also be cyclic olefins, such as cyclopentene or norbornene. For the purposes of the present invention, the term “polyolefins” is also taken to mean copolymers of monomers having a different number of carbon atoms. Polyethylene (PE) can particularly preferably be prepared in accordance with the invention.
In summary, the ethylene introduced into the degassing tank simultaneously takes on a number of functions in accordance with the invention:
1. It is a component of the degassing medium, which can remain in the closed return-gas circuit both in suspension technology and in the fluidized-bed method. Nitrogen, for example, would have to be removed at considerable effort, i.e. the gas stream would have to be separated into its individual components by complex operations.
2. The post-polymerization in the degassing tank causes a reduction in the content of high-boiling comonomers (for example hexene), thereby significantly reducing the degassing effort.
3. The polymer formed in the degassing step has a significant effect on the product and/or processing properties. By varying the temperature and pressure conditions in the decompression tank, there is a certain degree of freedom to match the product properties (and to reduce high-boiling comonomers).
A specific application of the method according to the invention comprises PE products having a density of 0.94 g/cm
3
and an HLMI (190° C./21.4 kg in accordance with ISO 1133) of about 20, which are employed, inter alia, for pipe coatings and as material for plastic pipes. A very important quality criterion is, inter alia, the so-called ESCR value (rupture strength under defined experimental conditions). It has been found, for exampl
de Lange Paulus
Deckers Andreas
Evertz Kaspar
Lilge Dieter
Perner Thomas
Basell Polyolefine GmbH
Boykin Terressa M.
Connolly Bove & Lodge & Hutz LLP
LandOfFree
Method for drying and degassing polyolefins does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for drying and degassing polyolefins, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for drying and degassing polyolefins will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2975915