Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – Treating polymer containing material or treating a solid...
Reexamination Certificate
2002-02-19
2004-12-28
Truong, Duc (Department: 1711)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
Treating polymer containing material or treating a solid...
C528S086000, C528S480000
Reexamination Certificate
active
06835803
ABSTRACT:
The present invention relates to a method for doping a conjugated polymer. Polymers preparable according to the method of the present invention are provided.
Doping of conjugated polymers (polymers with pi-conjugated backbone structures and/or pi-conjugated pendant groups) with strong protonic acid (p-doping) or strong oxidising (p-doping) or reducing agents (n-doping) is well established in the literature. However, the doping proceeds readily to completion in the presence of a stoichiometric or excess amount of dopants. The chemical driving force for maximum doping is very high, so that it is difficult to arrest the doping level at an intermediate; is value. The system achieves the maximum doping with about 10-50% of the conjugated repeat units doped depending on the polymer system. For poly(p-phenylenevinylenes) and polyacetylenes, this is typically 10-20%; for polythiophenes, 20-30%; for polyanilines, 40-50%. This maximum level of doping imparts a high level of electrical conductivity of the order of 1-1000 S/cm to the polymers, depending on the nature and type of the polymers and dopants used, so that they become conducting polymers in the process. The bulk carrier concentration is then roughly of the order of 10
20
/cm
3
to 10
21
/cm
3
.
However, this high level of doping is unnecessary or even undesirable for some applications. For example, for a 1-&mgr;m thick film (which is typical of the vertical thickness of photonic structures) having a conductivity of 10
−6
S/cm, only a modest 1-V potential difference is required to drive a practical device current density of 10 mA/cm
2
through the film thickness direction. Therefore, film conductivities of the order of 10-6 10
−2
S/cm (typical of the semiconducting range) are already sufficient for these films to be employed in semiconducting photonic structures such as distributed Bragg reflectors and waveguides.
Furthermore, when the films are doped to the maximum, such as achieved by straightforward exposure to strong acids or oxidants, their optical properties change in drastic ways owing to the formation of new sub-gap transitions-that change the refractive indices of the films and cause parasitic absorption of any emitted light. Both these factors are not desirable or acceptable for photonic applications. Therefore control of the bulk carrier concentration between 10
17
/cm
3
to 10
20
/c
3
, at an intermediate doping-level at least about one order of magnitude less than the maximally-doped case, is crucial.
Applied Physics Letters, volume 73, Number 2, pages 253-255 (1998) reports a study of the Hall mobility and the carrier concentration of a conjugated polymer, namely polythiophene, as a function of the electrochemical doping level. The doping level of the polymer is changed by varying the oxidation potential i.e. by potentiometric control.
Synthetic Metals, 68, pages 65-70 (1994) is concerned with field-effect mobility and conductivity data obtained from two different amorphous organic semiconductors which can be doped to a range of different conductivities.
Synthetic Metals, 89, page 11-15 (1997) investigates the doping and temperature dependence of the conductivity of poly(p)-phenylene vinylene) (PPV).
Synthetic Metals, 55-57, page 3597-3602 (1993) investigates electrical conductivity of &agr;,&agr;-coupled dodecathiophene as a function of both dopant level and time.
Synthetic Metals, 30, page 123-131 (1989) discloses a relationship between acid strength and ionization potential of a conjugated polymer that will give a highly conductive doped complex.
Applied Physics Letters, volume 72, page 2147-2149 (1998) describes a doped hole transporting polymer. Differing levels of doping are realized by adjusting the co-evaporation rates of polymer and dopant material.
The methods used to achieve different levels of doping in the above systems are not satisfactory for controlling the doping level to such a degree so that a balance between optical and electrical property of the doped polymer can be struck.
In view of the above, there remains a need to develop a method for preparing polymers which are doped to a controlled, low or intermediate level which is both simple and cost effective It is envisaged that polymers doped to such a level will be particularly useful in devices such as those referred to,below in order to avoid the disadvantages associated with polymers that are doped to a high level. These disadvantages include intense sub-group absorptions, changes in the optical properties of the polymer and degradation of the photonic structure of the polymer. Using polymers that are doped to a controlled, low level or intermediate it will be possible to strike a balance between optical and electrical properties of an organic semiconductor when used in an optoelectronic device.
The present invention aims to provide a method for forming a conjugated polymer that is partially doped. The present invention further aims to provide a polymer preparable according to the method of the present invention and uses of such polymers.
Accordingly, the present invention provides a method for forming a conjugated polymer which is doped by a dopant comprising the steps of:
(a) adding a doping agent comprising a dopant moiety to a solution comprising the conjugated polymer or a precursor thereof and, optionally, a second polymer, the dopant moiety being capable of bonding to the conjugated polymer, precursor thereof or the second polymer;
(b) allowing the dopant moiety to bond to the conjugated polymer, precursor thereof or the second polymer to perform doping of the conjugated polymer, characterised in that the amount of doping agent added in step (a) is less than the amount required to form a fully doped conjugated polymer.
The present invention further provides a conjugated polymer that is doped to a controlled, low or intermediate level which is preparable according to the method of the present invention.
The present invention still further provides a photonic device including a polymer according to the present invention.
One embodiment of the present invention provides a method for forming a partially doped polymer material, comprising: adding a doping agent to the polymer or a precursor thereof, the doping agent being capable of bonding to the precursor or the polymer chain; and causing the doping agent to leave the precursor or the polymer chain to form a dopant capable of doping the polymer chain; wherein fewer moles of the doping agent are added than would be numerically sufficient to fully dope the polymer chain. Also, the present invention provides a partially doped polymer material formed by that method. Further, the present invention provides a device/structure (such as a photonic device) that includes such a material.
The conjugated polymer or its precursor is:
(i) derivatised with a controlled concentration (typically at the level less than 10-20% of the amount required for full doping) of a dopant moiety(ies) or its(their) precursor form(s); or
(ii) blended together with a polymer partner (the second polymer),, which may or may not be a conjugated polymer itself, which is derivatised with such moieties to give the equivalent dopant concentration.
Photonic structures are then fabricated from the partially doped polymer materials, including higher-order blends and composites, containing these modified conjugated polymers by film-forming techniques. A subsequent thermal, irradiation or chemical activation step may be required to generate the active dopant to dope the conjugated polymer.
In a first aspect of the invention, a method is provided to manipulate a precursor polyelectrolyte to give a controllable partially-doped conjugated polymer after elimination. The method involves replacement of a fraction of the counter-anions of the precursor polyelectrolyte by acid anions, such as sulfonates, phosphonates, phosphates, etc, of benzene, naphthalene and other organic derivatives while the precursor polyelectrolyte is in solution. These anions are converted during thermal elimination to the corresponding strong or
Friend Richard Henry
Ho Peter Kian-Hoon
Kim Ji-Seon
Cambridge Display Technology Ltd.
Truong Duc
LandOfFree
Method for doping a polymer does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for doping a polymer, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for doping a polymer will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3281879