Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – Treating polymer containing material or treating a solid...
Reexamination Certificate
2001-02-20
2002-05-07
Boykin, Terressa M. (Department: 1711)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
Treating polymer containing material or treating a solid...
Reexamination Certificate
active
06384184
ABSTRACT:
Acidic aqueous solutions of melamine-formaldehyde resins are used in the following technical fields: in the paper industry, as binders of water-based and solvent-based coatings, and as adsorbents or flocculating agents in waste-water treatment, as well as for coagulating solvent-based or water-based paints, for example, for the coating of automobiles.
For the purposes of the present invention, the term “aqueous solution” includes not only low-molecular solutions, but also colloidal solutions. For the above-mentioned fields of application, the melamine-formaldehyde polymers are, as a rule, cross-linked to the extent that they are in the colloidal size range. Owing to the method of preparation, at a content of from about 5 to about 30 wt. % melamine-formaldehyde resin, these solutions contain free formaldehyde in a concentration of between about 0.2 and about 4 wt. %. As formaldehyde may cause damage to health and is, moreover, regarded as being carcinogenic, it is desirable to lower the content of free formaldehyde.
The preparation of melamine-formaldehyde resins and the use thereof as an acidic colloidal solution for coagulating paint is described in U.S. Pat. No. 4,656,059. This reference contains detailed information regarding the preparation and the use of such resins and is hereby expressly incorporated in the present disclosure. In the; said document, the following information is given regarding the preparation of the melamine-formaldehyde resins and of an acidic colloidal solution therefrom:-
63 g melamine and 30 g formaldehyde or paraformaldehyde are mixed together in 93 ml distilled water. The mixture is adjusted to pH 10 by addition of sodium hydroxide solution and heated to 70° C. It is maintained at this temperature for 5 minutes and then cooled to room temperature. In the course of this, methylol melamine is precipitated. The precipitate is filtered, washed with methanol and dried under vacuum. The resins are partially cross-linked by acid in order that they may be used in the above-mentioned fields. To this end, the starting materials (melamine-formaldehyde, partially etherified), in the form of powder or dissolved, for example, in water or in alcohols, are reacted with acid. To prepare an acidic aqueous solution, 10 g of the methylol melamine is stirred into 100 ml of an 1.35% aqueous solution of hydrochloric acid. Prior to use, this solution is aged by being allowed to stand for 12 days at room temperature.
The melamine-formaldehyde resins may be in at least partially etherified form. To this end, the unetherified resins are etherified using alcohols preferably having 1 to 5 carbon atoms. Examples of such alcohols are methanol, ethanol, as well as propanol, butanol, pentanol and isomers thereof. Etherification is preferably carried out using methanol and/or n-butanol.
Besides hydrochloric acid, other strong monobasic acids, such as nitric acid and formic acid, are suitable for preparing the acidic aqueous solution. Which acid is preferred depends on the intended field of use. The economically priced hydrochloric acid is preferred for use in the paper industry and for the treatment of waste water. For use as a coagulant for paint, formic acid is preferably employed, as this is less corrosive than hydrochloric acid. Polybasic acids are unsuitable as a rule, because they lead to the formation of a deposit. Nitric acid gradually causes damage to the resins by oxidation; more strongly oxidizing acids, such as perchloric acid, cause such damage after a short time.
The object of lowering the content of free formaldehyde in acidic aqueous solutions of this type may be achieved according to WO 94/10231 by the addition to the solution of a &bgr;-Miketo compound. This is able to react with the free formaldehyde. This method has the disadvantage that 2 mol of a reagent having a high molecular weight compared with that of formaldehyde has to be added in order to bind 1 mol of formaldehyde. This weight relation of removed formaldehyde to added reagent is therefore very unfavorable and this entails economic disadvantages, as well as environmental disadvantages during disposal.
In contrast, an object of the present invention is to lower the free formaldehyde content of acidic aqueous solutions of melamine-formaldehyde resins simply and economically, without thereby damaging the melamine-formaldehyde resin.
This object is achieved by a process for decreasing the content of free formaldehyde in acidic solutions of melamine-formaldehyde resins, characterized in that an acidic aqueous solution having a pH of from 0.5 to 4 and containing between 5 and 30 wt. % melamine-formaldehyde resin is brought into contact with from 0.1 to 6 wt. %, based on the acidic aqueous solution of the melamine-formaldehyde resin, of an oxidising agent selected from hydrogen peroxide, performic acid and/or peracetic acid.
The formaldehyde is accordingly oxidised by a suitable oxidising agent (hydrogen peroxide, performic acid, peracetic acid or a mixture of these) to formic acid and/or to CO
2
and H
2
O. The oxidising agents have a molar mass corresponding approximately to that of the formaldehyde. Within the above-mentioned concentration range they do not cause damage to the resin but they do bring about a definite lowering of the formaldehyde content. Depending on the procedure, the latter is lowered from starting values in the range of between 0.2 and 4 wt. % to values in the range of from 10 ppm to 1 wt. %.
The selected oxidising agents, hydrogen peroxide, performic acid and/or peracetic acid, have a redox potential at which formaldehyde may be readily oxidised, but the melamine-formaldehyde resin is not appreciably damaged by oxidation. Other oxidising agents, such as sodium perborate, prove to be insufficiently efficient or, for example in the case of potassium permanganate, potassium peroxydisulfate or sodium sulfite, they lead to decomposition of the melamine-formaldehyde resin or to the precipitation of a white paste from the acidic aqueous solution.
The decomposition of the formaldehyde may be effected by several procedural variants.
In variant A, 5 to 30 wt. % melamine-formaldehyde resin is dissolved in an acidic aqueous solution which contains from 0.1 to 5 wt. % hydrogen chloride and/or from 0.3 to 20 wt. % formic acid. Here, the solution in formic acid is preferred if the products are to be used for coagulating paint. This solution is maintained within a temperature range of about 5 to about 30° C. and, within 3 hours of its preparation, from 0.1 to 5 wt. %, based on the acid aqueous solution of the melamine-formaldehyde resin, of hydrogen peroxide, performic acid and/or peracetic acid is added thereto. Here, the content of free formaldehyde, which initially is in the range of 0.2 to 4 wt. %, falls to values in the range of about 0.01 to about 1 wt. %.
In variant B, an acidic aqueous solution of melamine-formaldehyde resin is first of all prepared as in variant A. This is allowed to stand at a temperature in the range of about 5 to about 30° C. for a period in the range of 3 to 48 hours, preferably in the range of 3 to 24 hours. This leads to a partial cross-linking of the melamine-formaldehyde polymer and renders this less sensitive to attack by the oxidising agent. After the above-mentioned waiting period, between 0.1 and 6 wt. %, based on the acidic aqueous solution of the melamine-formaldehyde resin, of hydrogen peroxide, performic acid and/or peracetic acid is added to this solution. Here again, the content of free formaldehyde falls to values of between 0.01 and 1 wt. %. Damage to the resin by oxidation is avoided more reliably than in variant A.
In variant C, an acidic aqueous solution of the melamine-formaldehyde resin is also first of all prepared as in variant A. This is heated to a temperature in the range of 30 to 100° C., preferably in the range of 50 to 70° C. and in particular to about 60° C. Under these temperature conditions, the partial cross-linking of the melamine-formaldehyde resin is terminated after about 30 minutes. From about 30 minutes to about 5 hours after the h
Boykin Terressa M.
Harper Stephen D.
Henkel Kommanditgesellschaft auf Aktien
LandOfFree
Method for decreasing the formaldehyde content in acidic... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for decreasing the formaldehyde content in acidic..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for decreasing the formaldehyde content in acidic... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2829397