Method for continuous curing of hipe into hipe foams

Details Method for continuous curing of hipe into hipe foams Method for continuous curing of hipe into hipe foams

2001-08-07

2003-02-25

Foelak, Morton (Department: 1711)

Synthetic resins or natural rubbers -- part of the class 520 ser

Synthetic resins

Cellular products or processes of preparing a cellular...

C521S063000

Reexamination Certificate

active

06525106

ABSTRACT:

FIELD OF THE INVENTION
This application relates to flexible, microporous, open-celled polymeric foam materials with physical characteristics that make them suitable for a variety of uses. This application particularly relates to methods for continuously curing high internal phase emulsions to form such foams.
BACKGROUND OF THE INVENTION
The development of microporous foams is the subject of substantial commercial interest. Such foams have found utility in various applications, such as thermal, acoustic, electrical, and mechanical (e.g., for cushioning, or packaging) insulators, absorbent materials, filters, membranes, floor mats, toys, carriers for inks, dyes, lubricants, and lotions, and the like. References describing such uses and properties of foams include Oertel, G.,
Polyurethane Handbook
, Hanser Publishers, Munich, 1985, and Gibson, L. J.; Ashby, M. F.,
Cellular Solids. Structure and Properties
, Pergamon Press, Oxford, 1988. Other uses for foams are generally obvious to one skilled in the art.
Open-celled foams prepared from High Internal Phase Emulsions (hereinafter referred to as “HIPEs”) are particularly useful in a variety of applications including absorbent disposable articles (U.S. Pat. No. 5,331,015 (DesMarais et al.) issued Jul. 19, 1994, U.S. Pat. No. 5,260,345 (DesMarais et al.) issued Nov. 9, 1993, U.S. Pat. No. 5,268,224 (DesMarais et al.) issued Dec. 7, 1993, U.S. Pat. No. 5,632,737 (Stone et al.) issued May 27, 1997, U.S. Pat. No. 5,387,207 (Dyer et al.) issued Feb. 7, 1995, U.S. Pat. No. 5,786,395 (Stone et al.) Jul. 28, 1998, U.S. Pat. No. 5,795,921 (Dyer et al.) issued Aug. 18, 1998), insulation (thermal, acoustic, mechanical) (U.S. Pat. No. 5,770,634 (Dyer et al.) issued Jun. 23, 1998, U.S. Pat. No. 5,753,359 (Dyer et al.) issued May 19, 1998, and U.S. Pat. No. 5,633,291 (Dyer et al.) issued May 27, 1997), filtration (Bhumgara. Z.
Filtration
&
Separation
1995, Mar., 245-251; Walsh et al.
J. Aerosol Sci
. 1996. 27, 5629-5630; published PCT application W/O 97/37745, published on Oct. 16, 1997, in the name of Shell Oil Co.), and various other uses. The cited patents and references above are incorporated herein by reference. The HIPE process provides facile control over the density, cell and pore size and distribution, proportion of cell struts to windows, and porosity in these foams.
The physical properties of the foam are governed by: (1) the properties of the polymer from which the foam is comprised, (2) the density of the foam, (3) the structure of the foam (i.e. the thickness, shape and aspect ratio of the polymer struts, cell size, pore size, pore size distribution, etc.), and (4) the surface properties of the foam (e.g., whether the surface of the foam is hydrophilic or hydrophobic). Once these parameters have been defined and achieved for a particular application, an economically attractive process for preparing the material is desired. A key aspect of this process is the rate of polymerization and crosslinking, together referred to as curing, of the oil phase of a HIPE to form a crosslinked polymer network. Previously, this curing step required that the emulsion be held at an elevated temperature (40° C.-82° C.) for a relatively long period of time (typically from 2 hours to 18 hours or longer). Such long cure times necessitate relatively low throughput rates, as well as high capital and production costs. Specifically, such long cure times result in a long residence time requirement with attendant large curing chambers for commercially desirable throughput rates.
Previous efforts to devise commercially successful schemes for producing HIPE foams have involved, for example, pouring the HIPE into a large holding vessel which is then placed in a heated area for curing (see for example U.S. Pat. No. 5,250,576 (Desmarais et al.) issued Oct. 5, 1993). U.S. Pat. No. 5,189,070 (Brownscombe et al.), issued Feb. 23, 1993; U.S. Pat. No. 5,290,820 (Brownscombe et al.) issued Mar. 1, 1994; and U.S. Pat. No. 5,252,619 (Brownscombe, et al.) issued Oct. 12, 1993 disclose curing the HIPE in multiple stages. The first stage is conducted at a temperature of less than about 65° C. until the foam reaches a partial state of cure. Then the temperature is increased to between 70° C. and 175° C. to effect final curing rapidly. The whole process takes about 3 hours. Another scheme to produce HIPE foams envisaged placing the emulsion on a layer of impermeable film which would then be coiled and placed in a curing chamber (U.S. Pat. No. 5,670,101 (Nathoo, et al.) issued Sep. 23, 1997). The coiled film/emulsion sandwich could then be cured using the sequential temperature sequence disclosed in the Brownscombe, et al patents discussed above. U.S. Pat. No. 5,849,805 issued in the name of Dyer on Dec. 15, 1998 discloses forming the HIPE at a temperature of 82° C. (pour temperature in Example 2) and curing the HIPE at 82° C. for 2 hours. However, none of these approaches offer the combination of very fast conversion (e.g., in minutes or seconds) from HIPE to polymeric foam that would provide for a relatively simple, low capital process for producing HIPE foams both economically and with the desired set of properties.
The art also discloses using pressure to control the volatility of monomers that, otherwise, would boil off at a suitable polymerization/curing temperature. For example, commonly assigned U.S. Pat. No. 5,767,168, issued to Dyer, et al, on Jun. 16, 1998, discloses the suitability of pressurization to control the volatility of relatively volatile conjugated diene monomers. However, the cure time for the foams disclosed therein is still greater than two hours so there is still substantial opportunity for substantial improvement in curing rate that would improve the economic attractiveness of HIPE foams.
Accordingly, it would be desirable to develop a rapid and efficient process for preparing open-celled polymeric HIPE foam materials with the desired properties. In particular, it would be desirable to develop a continuous process that can produce HIPE foams.
SUMMARY OF THE INVENTION
The present invention relates to a process for obtaining open-celled foams by polymerizing a High Internal Phase Emulsion, or HIPE, which has a relatively small amount of a continuous oil phase and a relatively greater amount of a discontinuous aqueous phase. The present invention particularly relates to relatively high temperature processes for curing the oil phase. This enables the foam to be prepared in a much shorter interval than has heretofore been possible. This enables practical continuous production processes of HIPE foams which have to this point been made via batch processes.
The process of the present invention generally comprises the steps of: 1) forming a water in oil emulsion (HIPE) wherein the oil phase comprises polymerizable monomers; 2) forming the emulsion into a continuous stream; and 3) polymerizing and crosslinking (i.e. curing) the monomers to form a HIPE foam. Specifically, the oil phase comprises: 1) from about 85 to 99% by weight of a monomer component capable of forming a copolymer having a Tg of about 90° C. or lower, wherein the monomer component comprises a blend of monofunctional monomers, crosslinkng agents, and comonomers capable of modifying foam properties, and 2) from about 1 to about 20% of an emulsifier component capable of forming a stable HIPE. The aqueous phase comprises from about 0.2 to about 40% by weight of a water soluble electrolyte and an effective amount of a polymerization initiator. The volume to weight ratio of aqueous phase to oil phase is between about 8:1 and about 140:1 After curing, the aqueous fraction of the HIPE foam may be removed by a variety of techniques to yield the open-celled, microporous, low density product.
The curing of HIPEs in a relatively short time period at elevated temperatures allows increased production and improved economics relative to previously described methods. Either batch or continuous processes can be used. In either case, because the vapor pressure of both phases in the emulsion increases as th

Affiliated with

Also associated with

Rating

Method for continuous curing of hipe into hipe foams does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Method for continuous curing of hipe into hipe foams, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for continuous curing of hipe into hipe foams will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-3173037