ABSTRACT:
The present invention relates to a method for cathodic protection, electrochemical chloride extraction and realkalisation of reinforced concrete or similar materials, and also strengthening and crack prevention in concrete, comprising the impressing of a direct voltage between the reinforcement in the concrete and a conductive device which is placed on the concrete surface, and wherein crack prevention is achieved by embedding the device in fresh concrete.
BACKGROUND OF THE INVENTION
Today, corrosion of reinforcement in concrete structures is a major problem involving substantial maintenance costs. Corrosion is usually caused by chlorides, carbonisation or other changes in the environment surrounding the reinforcement where cracking is a major factor.
Electrochemical methods arm used ever-increasingly to protect the reinforcement against further corrosion. Methods used today include cathodic protection, chloride extraction and realkalisation. The principle common to these methods is that a direct voltage is impressed between the reinforcement, the cathode (negative pole), and various conductive devices which serve as the anode. This results in migration of ions in the concrete, formation of OH ions on the surface of the reinforcement or, in the case of cathodic protection, the potential impressed into the passive area. The anode may, for instance, be made of metal wire, metal mesh or conductive coatings which are placed on the surface of the concrete and incorporated therein to varying degrees. It is also possible to drill holes in which anode rods are inserted.
The use of, for example, wire cloths of valve metal for the same purpose as that of the present invention is previously known. Such solutions are described, for example, in NO B 169299, NO B 170291 and NO A 913222. According to these publications, the metal wires are welded together at their junctions. Clearly, this will result in a rigid and virtually inflexible cloth which is not easy to place on a surface that is to be treated. The use of these wire cloths is therefore limited.
NO B 162427 describes an anode comprising several wires which are connected to each other to form a flexible open cloth or netting. At least some of these wires are electrically conductive. According to this publication, the wires may connected to each other in a variety of ways. Among the characteristics of this cloth or netting is that it has a mesh size of at least 1.3 cm, preferably 5 cm, and that its fibres are not placed functionally in all directions. It also appears to be rather rigid in comparison with the present invention. When compared with the present invention, this anode yields a clearly limited capacity as regards current distribution and long-term durability. Tests have shown that when a coarse-meshed netting is used, the carbon wires become visible on the surface at a relatively early stage due to acid formation. As is commonly known, a system of this kind is broken down when acid is formed, and in particular when substantial current density is required.
GB A 2 175 609 describes an electrode having an enlarged area comprising one or more wires of valve metal in the form of a mesh, where the wires on the surface are provided with an anodic active layer. It is disclosed that the cloth may be woven or knitted, or that the wires may even be welded together. The material discussed in this publication is of a completely different type than the material used in the present invention. The material selection according to this publication results in a far more rigid product than that of the present invention.
NO 960841 describes 1-10% dispersed carbon fibres in a saturated epoxy/polyurethane mass (in the liquid phase). Flocking of the fibres results in an inhomogeneous distribution of the fibres, even at a content noticeably lower than 10%. The present invention differs substantially from this in that the amount, thickness and distribution may be designed in a premanufactured mat. Reference is also made to tests where the mat is incorporated in conductive coatings of dispersed fibres (see below). In this case, the current flow increased by a factor of seven or more.
A weakness of the aforementioned electrochemical methods is the anode system, or to be more precise, the current-carrying device. Several problems arise from this, including the following:
corrosion on the current distribution device, particularly in cases of chloride extraction and realkalisation;
repassivation of the current distribution device whereby the process comes to a stop;
risk of the anode material drying out and fire in the case of methods employing a high current density, approximately 1 A/m
2
or more;
the current distribution system often provides inadequate homogeneity of the current distribution on the surface. This applies inter alia to conductive coatings where there is liable to be an accumulation of fibres at some points on the surface, whilst at other points there is a minimum of fibres;
the anode material is required to have good conductivity in order to prevent a drop in potential between the individual conductors;
problems arise with the mechanical connection between intersecting current distribution bands, in particular with respect to durability and maintenance;
existing systems take virtually no account of cracking.
SUMMARY OF THE INVENTION
The present invention provides a method of the type mentioned above which is characterised in that there is used as conductive device a mat of optionally coated, conductive carbon fibres produced by blowing, pressing, weaving or knitting so that the fibres lie in almost every direction and wherein the fibres are of different thicknesses, wherein the mat further comprises current conductors in the form of bands or wires of conductive material which are placed over or under the mat or which are incorporated therein.
The mat used according to the present invention may, for instance, be embedded in the concrete surface of a new structure in an exposed environment (see FIGS.
2
and
3
). It is then possible to choose whether the system will later be used, if necessary, as a preventive system or as cathodic protection (CP) and where the costs involved will be minimal, The term “preventive CP” is used to mean the use of a lower impressed voltage than in normal CP where the electrical field acts as a shield against chloride penetration. The system will also to a great extent prevent shrinkage cracks, which is a major problem in structures of newly placed concrete.
The mat may also be used on existing structures where an electrically conductive material is placed on the surface of the structure (see FIG.
1
).
For a person well versed in the art of cathodic protection, one of the difficulties encountered is that the structures are generally located in particularly exposed areas. The present system can be premanufactured under controlled conditions, which means that the installation phase will be very short and of little complexity.
The solution according to the present invention will also prevent the outbreak of fire in the anode material, which, for example, is a problem when using cellulose pulp in realkalisation and chloride extraction.
Embedment in fresh concrete allows the mat to be embedded so as to act as additional reinforcement in the surface layer of the concrete.
The system is so thin and flexible that it is easy to shape according to the surface and incorporate in an electrically conductive material. As mentioned, the mat may also be embedded close to the surface in new structures which are built of fresh concrete or shotcrete and connected to serve as cathodicprotection, should the need arise. It is also possible to use a lower voltage between the reinforcement and anode than in cathodic protection in order to produce a “shield” against chloride penetration for structures in particularly exposed areas. As is commonly known, the negatively charged chloride ions are repelled by the cathode and attracted to the anode, even at low voltages. The system would also be suitable for water drainage in concrete an
Optiroc AS
Wenderoth , Lind & Ponack, L.L.P.
LandOfFree
Method for cathodic protection of reinforced concrete does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for cathodic protection of reinforced concrete, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for cathodic protection of reinforced concrete will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2823703