ABSTRACT:
Priority to German Patent Application No. 101 08 612.1-24, filed Feb. 22, 2001 and hereby incorporated by reference herein, is claimed.
BACKGROUND INFORMATION
The present invention relates to a method and a device for selective laser sintering in which powder is introduced in layers into a jacketed design space, forming a powder cake which is consolidated layerwise using laser radiation.
Selective laser sintering (SLS) is a rapid prototyping method in which a platform (design space bottom) which can be lowered into a design space carries a powder layer which is heated by a laser beam in selected regions so that the powder particles fuse to form a first layer. Subsequently, the platform is lowered downward into the design space by approximately 50 to 200 &mgr;m (depending on the particle size and type), and a new powder layer is applied. The laser beam draws its path again, fusing together the powder particles of the second layer as well as the second with the first layer. In this manner, a multilayer powder cake and, inside of it, a component such as an injection mold are formed little by little.
Inside of the design space, specific regions undergo a heating by the laser beam for a longer or shorter period of time, depending on the geometry of the component to be manufactured, whereas others are not heated at all. Moreover, in each case only the uppermost powder layer is heated by the laser; the lower layers give off the absorbed heat to their surroundings and cool off. The consequences include inhomogeneous temperature distributions and thermal stress within the powder cake which may result in component distortion.
To minimize this problem, it was already proposed in European Patent Document EP 5 56 291 to adjust a uniform base temperature of the respective surface layer, using a ring-shaped radiant heater mounted parallel to and above it. The intended result is a more uniform cooling of the individual layers and, consequently, less component distortion. This European Patent Document is related to U.S. Pat. No. 5,155,321, which is hereby incorporated by reference herein.
However, several tests have shown that temperature gradients still occur within and between the individual layers of which, in particular, those mentioned first result in component distortion which is not tolerable at least in the case of high-quality components.
SUMMARY OF THE INVENTION
An object of the present invention is to provide a method and a device for selective laser sintering in which the temperature within a layer of the deposited powder cake is as homogenous as possible and decreases as uniformly as possible, starting from the sintered regions of the surface down to the bottom of the design space.
The present invention provides a method for selective laser sintering of a powder in which the powder is introduced in layers into a jacketed design space, forming a powder cake, wherein the jacket is heated in such a manner that a temperature distribution develops in the jacket, the temperature in the jacket decreasing in the direction of the design space bottom, starting from the jacket regions bordering the powder cake surface which was sintered last.
The selective laser sintering carried out according to the present invention reduces component distortion since the temperature distribution within a layer of the deposited powder cake is homogenized better and decreases more uniformly, starting from the sintered regions of the surface down to the bottom of the design space.
This homogenization of the temperature distribution within a layer and of the temperature decrease is attained in that an additional temperature distribution featuring a decreasing temperature in the direction of the design space bottom is superposed via the jacket heating upon the temperature distribution generated by the laser radiation and, possibly, upon that generated by a ring-shaped radiant heater. This additional temperature distribution must, of course, not reach temperatures which would give rise to an independent sintering of the powder articles. It rather predetermines an essentially uniform base temperature of the individual powder layers so as to minimize the temperature dissipation of the sintered regions within a layer and to promote a temperature flow from the sintered regions into the depth, that is in a direction perpendicular to the powder layers. A suitable temperature distribution is, for example, a linear one.
The powder cake continuously grows by adding new powder layers and is at the same time lowered into the design space. In the process, the surface of the powder cake always borders the top edge of the design space. However, the platform of the design space bottom moves further and further away from the powder surface and borders regions of the design space wall which have lower and lower temperatures as the depth increases.
Therefore, it is advantageous for the jacket heating to include a design space bottom heating which is controlled in such a manner that the temperature of the design space bottom is, at each instant, adapted to the temperature of the design space wall region which it borders at this point in time.
It is particular advantageous to select an arbitrary, for example, also a non-linear and time-variant temperature distribution of the jacket heating which was optimized with regard to reduced component distortion with the assistance of a simulation of the laser sintering process. Simulations of the energy input of the laser into the powder layers have already been proposed, for example, in German Patent Document DE 10050280; the resulting temperature distributions within the powder cake can also be determined using known methods, for example, by solving the equation of heat conduction and, also, the influence on this temperature distribution by superposition of a jacket heating. Optimization methods are also known to one skilled in the art. Individual steps of the simulation can be experimentally verified or substituted.
The present invention also provides a device for selective laser sintering of a powder which features a jacketed design space for receiving the powder and which has a jacket heating device encircling the design space, wherein the jacket heating is able to heat different regions of the jacket separately.
The jacket heating device presets an essentially uniform base temperature of the individual powder layers so as to minimize the temperature dissipation of the sintered regions within a layer and to promote a temperature flow from the sintered regions into the depth, that is in a direction perpendicular to the powder layers. In this manner, thermal stress and, also, a resulting component distortion are minimized.
Advantageously, the jacket heating device is designed in such a manner that it can heat different regions of the jacket separately. For instance, in the case of a design space having a cylindrical configuration, this can easily be effected using heating rings which are disposed in parallel one over another and arranged concentrically around the design space. In addition to such an active heating, an active cooling via cooling circuits (e.g., piping) containing a coolant (e.g., water) can be advantageous as well.
In this context, it turns out to be particularly advantageous if the individual heating rings can also be separately controlled via at least one control device, and if this at least one control device features an input unit into which a temperature distribution can be entered. This temperature distribution can, for example, be one that is optimized via simulation of the laser sintering process with regard to homogeneity and/or reduced component distortion.
REFERENCES:
patent: 5155321 (1992-10-01), Grube et al.
patent: 5156697 (1992-10-01), Bourell et al.
patent: 5352405 (1994-10-01), Beaman et al.
patent: 5597589 (1997-01-01), Deckard
patent: 6376148 (2002-04-01), Liu et al.
patent: 6532394 (2003-03-01), Earl et al.
patent: 4439124 (1996-05-01), None
patent: 19846478 (2000-04-01), None
patent: 0556291 (1993-08-01), None
Manetsberger Karsten
Shen Jialin
Steinberger Juergen
Davidson Davidson & Kappel LLC
Dunn Tom
Johnson Jonathan
LandOfFree
Method and device for selective laser sintering does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method and device for selective laser sintering, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method and device for selective laser sintering will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3005981