Metal deforming – By use of tool acting during relative rotation between tool... – During rotation of work
Reexamination Certificate
2000-07-25
2002-03-19
Tolan, Ed (Department: 3725)
Metal deforming
By use of tool acting during relative rotation between tool...
During rotation of work
C072S093000, C072S102000, C029S893320
Reexamination Certificate
active
06357272
ABSTRACT:
This invention relates to a method of producing a gear wheel from a powder metal blank pressed and sintered with an overmeasure in the vicinity of the toothing, which powder metal blank is compacted under a plastic deformation in the vicinity of the overmeasure by pressing against a counter-toothing of at least one rotating pressing tool by the overmeasure, which counter-toothing engages in the toothing of the powder metal blank, and to an apparatus for performing the method.
Due to the porosity of the sintered material, gear wheels pressed and sintered from a metal powder have a comparatively low permanent bending strength in the vicinity of the tooth roots and a low wear resistance in the vicinity of the tooth flanks. To eliminate these disadvantages it is known (EP 0 552 272 B1) to compact the sintered powder metal blanks of the gear wheels in the flank area and in the root area of the teeth such that a largely non-porous surface layer is obtained. This non-porous surface layer in the area of engagement of the gear wheel involves a considerable increase in the admissible load-bearing capacity of sintered gear wheels. The compaction of the surface layer in the area of engagement of the gear wheel is effected via a pressing tool in the form of at least one gear wheel which has an external toothing engaging in the toothing of the powder metal blank. Since the driven gear wheel of the pressing tool is urged against the powder metal blank via a pressing means, the teeth of the powder metal blank are compacted in the area of engagement in several rotations via the counter-toothing of the pressing tool, until the desired contour of the toothing of the sintered gear wheel is achieved. Due to the kinematic conditions, sliding speeds occur between the flanks of the meshing teeth of the powder metal blank and the pressing tool along the line of engagement outside the pitch point during the rolling movement between the toothing of the powder metal blank and the counter-toothing of the pressing tool. This sliding movement, which increases with increasing distance from the pitch point, together with the contact pressure which is applied onto the flanks of the powder metal blank in particular in the vicinity of the tooth tips and tooth roots and is required for the local compaction, leads to a flank load of the powder metal blank which involves the risk of superficial fissures and material chippings in the vicinity of the surface of the tooth flanks and tooth roots of the powder metal blank. Such surface impairments involve, however, a considerable reduction of the load-bearing capacity of the sintered gear wheel which is compacted at the surface in the area of engagement. To avoid the harmful influences of the sliding movements of two flanks of meshing teeth it is known to use a lubricant to reduce the sliding friction, but the use of lubricants in the compaction of sintered powder metal blanks is prohibited, because the lubricant penetrating into the pores impairs or prevents the compaction of the material.
It is therefore the object underlying the invention to improve a method as described above with simple means such that the teeth of the powder metal blank can sufficiently be compacted in the area of engagement without having to fear an impairment of the compacted surface in particular in the vicinity of the tooth tips or tooth roots.
This object is solved by the invention in that the counter-toothing designed as internal toothing of the annular pressing tool enclosing the powder metal blank is pressed into the toothing of the powder metal blank by means of a pressure roller rolling on the outside periphery of the pressing tool.
The invention utilizes the fact that in the case of an internal toothing the sliding speeds between the tooth flanks of the powder metal blank and of the pressing tool, which occur during tooth engagement, are distinctly lower than in the case of a tooth engagement between two spur gears. This means that when using an annular pressing tool with an internal toothing as counter-toothing for the powder metal blank the load acting on the teeth of the powder metal blank can be restricted to a degree which excludes superficial fissures and material chippings in the vicinity of the tooth tips and tooth roots despite the necessary compaction in the area of engagement. The pressing force required for compaction is applied by a pressure roller which rolls on the outside periphery of the pressing tool, so that the compaction in the area of engagement can again be effected in several rotations, when the compaction in one rotation is not sufficient.
When a number of teeth larger than the number of teeth of the toothing of the powder metal blank is chosen for the internal toothing of the pressing tool, the internal toothing of the pressing tool is rolled over the toothing of the powder metal blank, while the pressing tool is continuously pressed onto the toothing of the powder metal blank, with the related sliding movement between the flanks rolling on each other decreasing with decreasing difference of the number of teeth of the pressing tool and of the powder metal blank. Accordingly, particularly favorable conditions are obtained in this connection when, with the same number of teeth of the internal toothing of the pressing tool and of the toothing of the powder metal blank, the pressing tool enclosing the powder metal blank with a clearance is continuously urged against the powder metal blank without a relative rotation between pressing tool and powder metal blank in peripheral direction. However, such compaction method requires a perfect pressing tool, because a defect in the vicinity of a tooth of the pressing tool is completely reproduced on a tooth of the powder metal blank without a possibility of compensation by the engagement of other teeth.
Despite the internal toothing, the same number of teeth of the pressing tool and of the powder metal blank provides for the simultaneous compaction of the toothing of the powder metal blank on two or more points distributed over the periphery, because the pressing tool can be urged against the powder metal blank at two or more points under an elastic deformation. Between the pressing tool and the powder metal blank there should merely be provided a slight initial clearance, which allows the pressing tool to be slipped onto the powder metal blank and correspondingly increases with increasing compaction of the tooth surfaces of the powder metal blank.
The possible compaction of the teeth of the powder metal blank in the vicinity of the intended overmeasure depends on the respective solidification of the material, which in the case of a cold working of the powder metal blank during a calibration process preceding the compaction or during the compaction of the tooth surfaces itself is obtained in the vicinity of the overmeasure. To be able to obtain a sufficient surface compaction even under more difficult conditions of compaction, the powder metal blank may be subjected to a heat treatment prior to compaction or between two compaction operations, in order to correspondingly reduce the deformation resistance for the subsequent compaction.
As has already been mentioned above, the harmful effects of the sliding movement of two flanks of meshing teeth can be reduced by using a lubricant. To be able to utilize the advantages of the lower sliding friction obtained by the use of a lubricant during the compaction of the tooth surfaces in the area of engagement, without impairing the compaction of the toot surfaces of the powder metal blank by lubricant penetrating into the pores, the powder metal blank can finally be compacted by using a lubricant after a precompaction. Precompaction should be effected to an extent which results in a substantial closure of the surface pores, so that during the use of the lubricant a penetration of the lubricant into surface pores, which is harmful for the further compaction, can be excluded.
For performing the method an apparatus can be employed which is provided with a take-up shaft for the powder me
Collard & Roe P.C.
Miba Sintermetall Aktien-gesellschaft
Tolan Ed
LandOfFree
Method and device for producing a toothed wheel does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method and device for producing a toothed wheel, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method and device for producing a toothed wheel will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2839711