Specialized metallurgical processes – compositions for use therei – Compositions – Solid treating composition for liquid metal or charge
Reexamination Certificate
2001-03-20
2004-09-07
Andrews, Melvyn (Department: 1742)
Specialized metallurgical processes, compositions for use therei
Compositions
Solid treating composition for liquid metal or charge
C075S319000, C075S321000, C075S380000, C266S087000
Reexamination Certificate
active
06786949
ABSTRACT:
BACKGROUND OF THE INVENTION
The present invention relates to self-reducing agglomerates for use in the production of iron, and to methods and apparatus for the production thereof.
The development of iron bearing agglomerates began in the fifties. These agglomerates were mainly in the form of pellets, with the purpose of enabling the use of mineral fines, which the conventional methods, such as those used in blast furnaces, cupola furnaces, electric furnaces and others, could not accept as raw materials due to the fine size thereof, articularly in the case of iron ore. Some time thereafter the development of self-reducing agglomerates began. This development was characterized by the use of cold cure binders, particularly cement, lime and silica, which exhibit as the cure mechanism, mainly reactions with water (hydration) and in lesser amount with the carbon dioxide present in the air (carbonation). Those reactions, although imparting to the agglomerate the desired mechanical properties, are slow reactions, requiring between 10 to 30 days for completion, and sometimes even more depending on the weather conditions (the cure velocity diminishes with the decrease of the ambient temperature).
Some alternatives were developed to accelerate the hydration reactions referred to above, by means of treatment of the agglomerates in pressure vessels (autoclaves) by applying pressures on the order of up to 20 atmospheres and water vapor at 250° C., as recited in U.S. Pat. No. 4,528,029, which is incorporated herein. The major disadvantage of this alternative practice is the high cost of the equipment required and the complex operating conditions, rendering the commercial application thereof difficult.
SUMMARY OF THE INVENTION
The present invention relates to self-reducing agglomerates for use in the production of iron. The agglomerates include a mixture of iron oxide containing particles and particles of a reducing agent. The mixture is bonded by a pre-gel.
The mixture may include particles of a fluxing agent.
The reducing agent may include carbonaceous material.
The iron oxide containing particles may include at least one of iron ore, industrial residue containing iron oxide with or without metallic iron and oxides of metal other than iron.
The method in accordance with the invention for producing the self-reducing agglomerates includes mixing iron oxide containing particles and particles of a reducing agent with a pre-gel. This mixing is performed in an atmosphere of air and addition of 5 to 20% of water to produce the agglomerates. Thereafter, the agglomerates are cured by heating at a temperature of about 100 to 180° C. for about 10 to 60 minutes. Thereafter, the agglomerates are introduced to a reduction chamber for use in the production of iron therefrom.
The apparatus for the continuous production of the agglomerates, in accordance with the invention, includes equipment for conveying the agglomerates, for introducing hot gas to the agglomerates while they are being conveyed, and for controlling the speed of the conveying equipment to expose the agglomerates to the hot gas for about 10 to 60 minutes.
Additional equipment may be provided for uniformly distributing the hot gas to the agglomerates while they are being conveyed.
The conveying equipment may include a perforated belt allowing passage of the hot gas therethrough to the agglomerates.
The method according to the invention may comprise the step of forming the agglomerate in the shape of pellets or briquettes or any other suitable geometric shape.
The method according to the invention may employ fluxing materials, such as lime, limestone, steel plant slag, blast furnace slag and similar materials, to flux the nonmetallic impurities present in the agglomerate.
In the method according to the invention, the pre-gel is added to develop the mechanical properties of the agglomerate, particularly the compression strength thereof, upon curing at temperatures in the range from about 100 to about 180° C.
The equipment according to the invention may include a system for the uniform distribution of hot gasses along the belt.
The equipment according to the invention, the heated gas may comprise air, burned gas, water vapor, inert gas and mixtures thereof without restrictions to proportions.
The equipment according to the invention may comprise a plurality of overlapping belt segments in the same direction or with alternately opposed directions of movement.
The equipment according to the invention may include a uniform exhaust system that does not affect the distribution of the heated gasses through ports distributed along the belt.
The heating of the agglomerates to provide drying and curing may be effected using heated air, burned gas, water vapor, inert gas and mixtures thereof, without restriction in terms of proportions, distributed along the belt to enable the same to pass uniformly through the agglomerates and not interfere with the distribution of the inflow of the heated gas. This avoids the occurrence of preferential gas flow and excessive variation of the uniformity of drying and curing. Hence, the speed of the belt may be constant while providing the required agglomerate residence time for adequate curing.
After the passage of the agglomerates through the curing equipment, the same are ready for use for the metal production.
REFERENCES:
patent: 3922165 (1975-11-01), Harker et al.
patent: 3957482 (1976-05-01), Whigham
patent: 4113479 (1978-09-01), Buker
patent: 4316718 (1982-02-01), Drugge
patent: 4372968 (1983-02-01), Kitamori et al.
patent: 4402736 (1983-09-01), Graham
patent: 4410355 (1983-10-01), Feichtner et al.
patent: 5294250 (1994-03-01), Panigraphy et al.
patent: 6071325 (2000-06-01), Schmitt
patent: 6342089 (2002-01-01), McGaa
patent: 6391086 (2002-05-01), Contrucci et al.
patent: 6692688 (2004-02-01), Contrucci et al.
patent: 0 916 742 (1999-05-01), None
patent: 0 960 952 (1999-12-01), None
patent: 1 434 406 (1976-05-01), None
Andrews Melvyn
Startec Iron LLC
LandOfFree
Method and apparatus for using a pre-jel for producing... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method and apparatus for using a pre-jel for producing..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method and apparatus for using a pre-jel for producing... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3206229