Method and apparatus for manufacturing patterned glass...

Stock material or miscellaneous articles – Structurally defined web or sheet – Including variation in thickness

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C428S038000, C428S542200, C065S102000, C065S104000, C065S255000, C052S204590

Reexamination Certificate

active

06372327

ABSTRACT:

This invention relates to a method and apparatus for manufacturing patterned glass products. In particular, this invention relates to a method and apparatus for manufacturing patterned glass products having an appearance similar to or simulating the appearance of glue chipped glass.
BACKGROUND OF THE INVENTION
Glue chipped glass is known in the art. For example, see U.S. Pat. No. 4,427,729, the disclosure of which is hereby incorporated herein by reference.
Conventionally, glue chipped glass is manufactured as follows. The manufacturer typically does not have glass making capability and thus begins with an annealed sheet of glass. The manufacturer then lightly roughens a surface of the glass sheet (e.g., via sand blasting). After the surface has been roughened, a solution of glue is applied on the roughened surface of the glass to a prescribed thickness (e.g., via spraying). Typically, the glue may consist of a common animal protein gelatin which may be purchased in dry powder form and mixed into solution form prior to application. Optionally, the glue may be preheated depending upon the effect desired, as heat and moisture both contribute to the appearance to the final product.
After the glue has been applied to the roughened surface, the glue is oven dried (i.e., heat dried). Optionally, following oven drying, the glue coated glass may be permitted to air dry. As the glass dries, it begins to form crystals which peel or “chip” away from the glass surface. Chipping is allowed to continue for a prescribed period of time, after which any remaining chips are simply brushed from the surface. The end result is a cut or chipped glass pattern as shown in
FIG. 1
, which resembles somewhat that of a fossil pattern (i.e., glue-chipped glass). The resulting product is esthetically attractive and has numerous applications in interior decorating, and the like.
Unfortunately, in the glue chipped glass manufacturing process described above the pattern of crystal growth cannot be controlled. To the contrary, the pattern is essentially random. Thus, the aforesaid process cannot be utilized to produce large quantities of glue chipped glass products in accurately duplicated patterns.
U.S. Pat. No. 4,427,729 discloses a method and apparatus for manufacturing glue chipped glass, as shown in FIG.
2
. Referring to
FIG. 2
, the apparatus of the '729 patent includes a pair of rollers
1
and
3
, defining nip
5
therebetween. Glue is fed through manifold
7
and exits the manifold at a desired thickness
9
. Rollers
1
and
3
cause the glue
11
to be deposited on the roughened surface of glass
13
. Conveyor
15
conveys the glass
13
below nip
5
whereafter the glass is conveyed to an oven where the glue is dried and chips off the glass.
Unfortunately, the system and apparatus of the '729 patent are undesirable for one or more of the following reasons. First, the requirement for the glue is burdensome and can be messy in certain manufacturing environments. Second, the time and structure required for the drying process is undesirable. Third, the structure and time required for the sweeping away of and collection of glue chips is undesirable. Fourth, the glue chipped pattern cannot practically be repeated on a regular basis in an accurate manner.
In view of the above, it will be apparent to those skilled in the art that there exists a need in the art for addressing and/or solving any one or more of the aforesaid problems in the manufacture of a glass sheet having a look similar to conventional glue-chipped glass.
SUMMARY OF THE INVENTION
An object of this invention is to provide a method and apparatus for manufacturing patterned glass sheets.
Another object of this invention is to provide a method and apparatus for manufacturing glass sheets having at least one pattern thereon in a manner so as to simulate a glue chipped type glass sheet.
Another object of this invention is to provide a method which enables a repeatable pattern that simulates a glue chipped type glass sheet to be repeatedly applied to a surface of a ribbon of glass.
Another object of this invention is to satisfy and/or fulfill one or more of the aforesaid objects and/or needs.
In certain embodiments, this invention fulfills any or all of the above listed needs and/or objects by providing a method of manufacturing patterned glass sheets having a visual appearance simulating an appearance of conventional glue chipped glass sheets, the method comprising the steps of:
providing a furnace or melter;
providing first and second opposing rollers which define a nip therebetween, and providing at least one of the first and second rollers with a glue chipped simulating pattern comprising a plurality of intersecting ridges of different lengths defined in an exterior surface thereof;
a ribbon of glass exiting the furnace or melter and proceeding toward the nip;
the ribbon of glass reaching the nip between the first and second rollers at a temperature from about 1,900-2,400° F.;
forming a glue chipped simulating pattern in at least one surface of the glass ribbon in the nip, by causing the glue chipped simulating pattern to be transferred from the at least one roller to the ribbon of glass;
the patterned glass ribbon exiting the nip;
annealing the patterned glass ribbon after the ribbon has left the nip; and
cutting the patterned glass ribbon into a plurality of sheets which simulate conventional glue chipped glass sheets from a visual perspective.
In other embodiments, this invention fulfills any or all of the above listed needs and/or objects by providing a patterned glass sheet aesthetically resembling a conventional glue chipped glass sheet, the patterned glass sheet comprising:
a sheet of glass including first and second opposing major surfaces;
a pattern simulating a conventional glue chipped glass sheet pattern defined in one of said first and second major surfaces of said sheet of glass;
wherein said pattern includes a plurality of ridges or lines of different lengths defined in said surface of said sheet, said ridges or lines being formed of glass; and
wherein certain of said ridges or lines intersect other of said ridges or lines in manner such that the pattern simulates a conventional glue chipped pattern.
This invention will now be described with respect to certain embodiments thereof, accompanied by certain illustrations.


REFERENCES:
patent: 370176 (1887-09-01), Brogan et al.
patent: 370178 (1887-09-01), Brogan et al.
patent: 720138 (1903-02-01), Hartung
patent: 720139 (1903-02-01), Hartung
patent: 737707 (1903-09-01), Chance
patent: 1528194 (1925-03-01), Burgess
patent: 3116166 (1963-12-01), Halley
patent: 3183140 (1965-05-01), Gibson, Jr.
patent: 3961929 (1976-06-01), Stockdale
patent: 4323423 (1982-04-01), Schruuk
patent: 4427729 (1984-01-01), Messer
patent: 4619850 (1986-10-01), Charlton
patent: 5182171 (1993-01-01), Aoyama et al.
patent: 5414968 (1995-05-01), Willner
patent: 5622019 (1997-04-01), Dorough, Jr.
patent: 5631057 (1997-05-01), Sundet
patent: 5721013 (1998-02-01), Pratt
patent: 5780726 (1998-07-01), Bastawros et al.
patent: 5840407 (1998-11-01), Futhey et al.
patent: 5888263 (1999-03-01), Nakata

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Method and apparatus for manufacturing patterned glass... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Method and apparatus for manufacturing patterned glass..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method and apparatus for manufacturing patterned glass... will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2842743

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.