ABSTRACT:
TECHNICAL FIELD OF THE INVENTION
The present invention is in the field of continuous steel casting.
BACKGROUND OF THE INVENTION
In continuous casting of steel, molten metal is poured from a large vessel called a “Tundish” into a water-cooled copper mold by using a submerged entry nozzle (“SEN”). Steel begins to solidify as it comes in contact with the walls of the copper mold, the slab descending down continuously at the casting rate. The thickness in a slab caster mold typically is about 9 to 12 inches, whereas in a thin slab caster the thickness is only about 2 to 4 inches. The width of the slab is generally very large, typically 60 to 72 inches. A layer of mold flux is maintained at the free surface of the as metal, which protects the hot metal from atmospheric oxidation and provides a thin lubricating layer between the descending slab and the mold walls.
Several fluid flow studies of slab caster molds have shown that the flow of molten metal in a mold has a large influence on the surface and subsurface quality of the resultant cast metal. The molten metal exiting the SEN is at an angle relative to the horizontal and impinges on the narrow wall. This results in the formation of upper and lower recirculating flows, which are schematically shown in a general flow pattern in FIG.
1
. The upper recirculation causes a standing wave at the free surface. The height of the Wave typically oscillates with time. This oscillating standing wave and associated turbulence at the free surface is considered to be the main reason for most of the defects in cast slabs made by this process.
Due to other physical factors (e.g., the slide gate and non-uniform nozzle blockage) and turbulence, the patterns on the two sides in the mold may not be symmetrical and may continuously change over time. The wave height depends upon the SEN submergence depth, as the wave is typically higher with shallow submergence. The wave height also depends on the port angle and opening area, as smaller angles and smaller area typically yield a higher wave height. Surface turbulence and standing waves are probably the most important factors affecting cast quality. The wave and recirculations oscillate from one side to another, adversely affecting the quality of the cast.
The flow is further biased due to the influence of the slide gate or preferential nozzle blockage. The biased flow increases the chances of mold flux slag entrainment. A larger jet angle downward from the horizontal helps in reducing the surface turbulence and wave height by pushing the impingement point to a lower depth in the mold. A lower impingement point, however, results in a thin solidified shell at the exit from the mold and associates itself with a danger of breakout. Another problem is that a deeper lower recirculation carries the inclusions down to much greater depth and affects the quality of cast metal.
Accordingly, it is an object of the present invention to provide an apparatus and method for continuous casting of metal that provides for a flatter and less turbulent free surface to provide effective flux flow while also allowing for more efficient removal of inclusions and allowing for potential reduction in the risk of break out. This is expected to reduce surface and subsurface defects in the cast slab associated with this surface wave and turbulence.
Although described with respect to the field of steel casting, it will be appreciated that similar advantages of surface wave damping, along with other advantages, may obtain in other applications of the present invention. Such advantages may become apparent to one of ordinary skill in the art in light of the present disclosure or through practice of the invention.
SUMMARY OF THE INVENTION
The invention includes a molten metal vessel system for casting molten metal and a method of providing a flow of molten metal for continuous casting.
In general terms, the apparatus of the present invention includes a molten metal vessel system for casting molten metal, the system comprising: (a) a vessel containing a molten metal adapted to contain and dispense the molten metal for casting, the vessel having interior surfaces and the molten metal forming an upper surface; (b) a submerged entry nozzle extending below the upper surface; and (c) a surface flow modifier member disposed between at least one of the interior surfaces and the submerged entry nozzle, and in sufficient proximity to the upper surface of the molten metal so as to impede the formation of waves in the upper surface of the molten metal.
Preferably, the surface flow modifier member(s) are located on either side of the submerged entry nozzle, and a series of surface flow modifier member(s) may be used on either side of the submerged entry nozzle.
The surface flow modifier member(s) typically extend into the molten metal surface, although they may be adapted to reside just above the free surface of the molten metal so as to impede the formation of waves in the upper metal surface. Normally, the molten metal surface will bear a flux layer and the surface flow modifier member(s) will extend into the flux layer and/or the molten metal.
In general, the invention is not limited to any geometry of the surface flow modifier member(s). For instance, in one embodiment, the surface flow modifier member(s) may be shaped so as to provide a relatively thin portion adapted to extend through the flux layer and a relatively wide portion adapted to extend into the molten metal. In another embodiment, the surface flow modifier member(s) comprise(s) a plurality of tines adapted to extend through the flux layer and a relatively wide portion adapted to extends into the molten metal. These geometries are examples of preferred geometries that impede turbulence and wave action while allowing as much as practicable the free and uniform flow of flux on the free metal surface.
In still another embodiment, the surface flow modifier member(s) comprise(s) a lower portion being tapered away from the submerged entry nozzle and toward the interior surface, so as to be somewhat trapezoidal in shape.
The surface flow modifier member may be supported in contact with or in functional proximity to the free metal surface by any appropriate mechanical means, such as through a bracket attached to the casting mold. Being attached to a structure other than the casting mold may also support the surface flow modifier member. Materials and attachment protocols may be any of those appropriate for the handling of temperature resistant materials, such as refractory ceramics. It is preferred that the surface flow modifier member(s) not contact the interior mold surface to avoid disrupting both the solidification of metal and the mold was and the flow of flux into the casting mold.
Another aspect of the present invention is that the surface flow modifier member(s) or other surface wave impedance means allows the submerged entry nozzle optionally to direct the flow of molten metal at an angle at or above the horizontal (rather than the typical downward angled flow). This feature helps both to allow the more efficient elimination of inclusions during the casting process, while avoiding the risk of high temperature break-out in the freshly solidified layer as it emerges from the mold occasioned by the hot molten metal being directed too low and too near the downstream end of the casting mold.
The molten metal vessel system for casting molten metal of the invention also includes (a) a vessel containing a molten metal adapted to contain and dispense the molten metal for casting, the vessel having interior surfaces and the molten metal forming an upper surface; (b) a submerged entry nozzle extending below the upper surface; and (c) means for impeding the formation of waves in the upper surface of the molten metal.
The means for impedance of the formation of waves in the upper surface of the molten metal is accomplished by application of mechanical force (such as in the form of the surface flow modifier member or equivalent mechanical arrangement or device), fluid force (such as in the form
Kastler Scott
The Ohio State University
LandOfFree
Method and apparatus for controlling standing surface wave... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method and apparatus for controlling standing surface wave..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method and apparatus for controlling standing surface wave... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3063074