ABSTRACT:
A metalorganic deposition method is disclosed for manufacturing a superconducting oxide film on a substrate, in which a mixed metalorganic precursor is coated and heated to its thermal decomposition temperature to create an amorphous mixed metal oxide layer. The amorphous layer is then converted to a crystalline coating by further heating followed by cooling in the presence of O.sub.2 atmosphere.
REFERENCES:
patent: 3873341 (1975-03-01), Janus
patent: 4239816 (1980-12-01), Breininger et al.
patent: 4316785 (1982-02-01), Suzuki et al.
patent: 4395436 (1983-07-01), Bianchi et al.
patent: 4401474 (1983-08-01), Donley
patent: 4418099 (1983-11-01), Cuevas et al.
patent: 4485094 (1984-11-01), Pebler et al.
patent: 4496398 (1985-01-01), Whitehouse
patent: 4507643 (1985-03-01), Sunano et al.
Vest et al., "Synthesis of Metallo-Organic Compounds for MOD Powders and Films", MRS Proceedings, Symposium, (Boston, Mass.), Dec. 2-4, 1985.
Kawasaki et al., "Compositional and Structural Analyses for Optimizing the Preparation Conductions of Superconducting (La.sub.1-x Sr.sub.x)CuO.sub.4-.delta. Films by Sputtering", vol. 26, No. 4, Apr., 1987, pp. L388-L390.
Koinuma et al., "Preparation of (La.sub.1-x Sr.sub.x).sub.2 CuO.sub.4-.delta. Superconducting Films by Screen Printing Method", vol. 26, No. 4, Apr., 1987, pp. L399-L401.
Meng et al., "High T.sub.c Superconducting Thin Films by Chemical Spray Deposition", International J. of Modem Phys. B., vol. 1, No. 2, (1987), 579-582.
J. G. Bednorz and K. A. Muller, "Possible High T.sub.c Superconductivity in the Ba-La-Cu-O System", Z. Phys. B.--Condensed Matter, vol. 64, pp. 189-193, 1986.
C. W. Chu, P. H. Hor, R. L. Meng, L. Gao, Z. J. Huang, and Y. Q. Wang, "Evidence for Superconductivity above 40 K in the La-Ba-Cu-O Compound System", Physical Review Letters, vol. 53, No. 4, pp. 405-407, Jan. 1987.
C. W. Chu, P. H. Hor, R. L. Meng, L. Gao, and Z. J. Huang, "Superconductivity at 52.5 K in the Lathanum-Barium-Copper-Oxide System", Science Reports, vol. 235, pp. 567-569, Jan. 1987.
R. J. Cava, R. B. vanDover, B. Batlog, and E. A. Rietman, "Bulk Superconductivity at 36 K in La.sub.1.8 Sr.sub.0.2 CuO.sub.4 ", Physical Review Letters, vol. 58, No. 4, pp. 408-410, Jan. 1987.
J. M. Tarascon, L. H. Greene, W. R. McKinnon, G. W. Hull, and T. H. Geballe, "Superconductivity at 40 K in the Oxygen-Defect Perovskites La.sub.2-x Sr.sub.x CuO.sub.4-y ", Science Reports, vol. 235, pp. 1373-1376, Mar. 13, 1987.
M. K. Wu, J. R. Ashburn, C. J. Torng, P. H. Hor, R. L. Meng, L. Gao, Z. J. Huang, Y. Q. Wang, and C. W. Chu, "Superconductivity at 93 K in a New Mixed-Phase Y-Ba-Cu-O Compound System at Ambient Pressure", Physical Review Letters, vol. 58, No. 9, pp. 908-910, Mar. 2, 1987.
Agostinelli John A.
Higberg Brian J.
Mir Jose M.
Paz-Pujalt Gustavo R.
Peterson David L.
Eastman Kodak Company
King Roy V.
Morgenstern Norman
Thomas Carl O.
LandOfFree
Metalorganic deposition process for preparing superconducting ox does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Metalorganic deposition process for preparing superconducting ox, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Metalorganic deposition process for preparing superconducting ox will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-1852873