Metal plating method

Electrolysis: processes – compositions used therein – and methods – Electrolytic coating – Depositing predominantly single metal or alloy coating on...

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C205S103000, C205S104000, C205S133000

Reexamination Certificate

active

06641710

ABSTRACT:

BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a metal plating method for depositing a metal such as chromium on the surface of an object body to be plated which is immersed in a plating solution by electroplating by pulsed electrolysis.
2. Description of the Prior Art
Chromium plating has conventionally been carried out to obtain a highly corrosion resistible hard coating. In this case, since cracking is likely to occur on the surface of the object body to be plated if chromium is plated directly on the surface, nickel plating is carried out on the surface of the object body to make the surface of the foregoing object body smooth and then chromium plating is carried out. That is, in general, the highly corrosion resistant hard chromium coating has a double layer structure of nickel and chromium.
The foregoing chromium deposition is carried out by depositing a chromium layer on the surface of an object body to be plated by applying direct current while immersing the object body in a plating solution in a plating tank. Electrolysis is generally carried out by continuously applying direct current of 10 to 60 A/dm
2
. The temperature of the plating solution bath is about 40 to 60° C.
SUMMARY OF THE INVENTION
With the foregoing electroplating method, the coating thickness of the resulting chromium layer cannot be about 10 &mgr;m or thinner and when attempting to make the coating thicker, cracking may occur resulting poor corrosion resistance.
Further, there also occurs a problem that the luster of the plated film is inferior.
The foregoing cracking occurrence is attributed to stress generated by hydrogen evolved simultaneously with chromium electrode position. In other words, at the time of reductive precipitation, about 8 to 10 hydrogen atoms are evolved per chromium atom and with the foregoing conventional method, metal ion falls like a shower on the surface of the object to be plated, so the time between the reduction and the lattice assembly cannot be sufficiently long. In this reason, while the chromium layer to be deposited is grown as a crystal lattice with low atomic density, hydrogen is incorporated in the chromium layer. Consequently, the thicker the coating thickness is made, more likely cracking is to occur.
The present invention is, therefore, performed in consideration of the above described problems and provides a metal plating method for obtaining a metal plated film with good luster and excellent corrosion resistance and wear resistance.
According to one aspect of the present invention, a metal plating method can be provided for carrying out pulse plating by pulsed electrolysis by periodically applying electricity, wherein the above described pulsed electrolysis is carried out in condition that the pulse frequency and the current density are controlled so that the ratio of the quantity of deposited lattice per pulse to the height of the lattice is about 0.28 or lower, that the duty ratio of the above described pulse frequency is controlled to be 0.5 or lower, and that the duration of complete pause caused by distortion of pulse waveform is controlled to be one half or longer of the duration of current interruption.
“the ratio of the quantity of deposited lattice per pulse to the height of the lattice” is dimensionless number. Further, “the height of the lattice” indicates the height of lattice when the crystal face is oriented in the (111) face where the atomic density is highest.
“the ratio of the quantity of deposited lattice per pulse to the height of the lattice” is defined as “(the quantity of deposited lattice per pulse)/the height of the lattice” and “the ratio of the quantity of deposited lattice per pulse to the height of the lattice” is sometimes only described to be the ratio of the quantity of deposited lattice.
The above described duty ratio means t
i
/(t
i
+t
0
) (refer to FIG.
2
), wherein t
i
denotes a duration of pulsed current application and t
0
denotes a duration of current interruption.
If the pulse waveform is an ideal one, the duration of current interruption t
0
is equal to the time during which no current flows between the electrodes, however owing to the distortion of the waveform, the time during which current does not actually flows differs. Such non-application time during which current does not actually flows is called duration t
k
of complete pause as mentioned above.
According to the present invention, hydrogen is dispersed in the duration of current interruption t
0
and suppressed from being incorporated in plated film, and the crystal face of a deposited metal can be controlled by controlling the reduced atom weight per pulse, thereby allowing for plating without cracking. The foregoing control of the reduced atom weight per pulse can be carried out by controlling the current density and the frequency.
According to the present invention, electroplating is carried out by pulsed electrolysis wherein hydrogen emitted from the cathode interface is dispersed far from the interface to lower the probability of absorbing hydrogen in crystal particles of chromium as well as to give arrangement of preferential orientation in high energy face, to prevent cracking, and to improve the wear resistance, ductility, and hardness of a plated film. In the case of chromium plating, which is of a body-centered cubic lattice, the crystal face is oriented in the (111) face where the atomic density is highest and the orientation ratio can be made to be 95% or higher by using the plating conditions as claimed in the present invention.
The numeral definitions of the present invention will be described below.
As described later, the relation between the quantity of deposited lattice per pulse and existence of cracks was studied using the pulse frequency as a parameter, and it was found that no cracking occurred (refer to table 1) in the condition that the ratio of the quantity of deposited lattice is 0.28 or lower (700 Hz or higher). Therefore, the ratio of the quantity of deposited lattice is 0.28 or lower (700 Hz or higher).
Meanwhile, the relation between the ratio of the quantity of deposited lattice and the pulse frequency is approximately same at current density used commonly for metal plating in a range of 10 to 1,200 A/dm
2
if the current density is set up uniformly. When the ratio of the quantity of deposited lattice is 0.28, the frequency is 700 Hz and when the ratio of the quantity of deposited lattice is 0.22, the frequency is 900 Hz. Further, as described later, the surface roughness or the like of the plated film is stabilized and improved by controlling the frequency to be 900 Hz or higher, so it is preferable to control the ratio of the quantity of deposited lattice to 0.22 or lower.
If the duty ratio is controlled to be 0.5, cracking is stably suppressed, so that the duty ratio is set to be 0.5 or lower. The smaller the duty ratio is, the longer becomes the ratio of pause duration of the current application. Further, at the same current density, though the ratio of pause duration of the current application per pulse becomes shorter as the frequency increases, the quantity of electrolysis per pulse is lowered as well. In this case, there is no lower limit of the duty ratio. However, as the foregoing duty ratio is lowered, the pause duration of the current application becomes longer and that is effective for dispersion of emitted hydrogen and on the other hand, it takes a long plating time accordingly.
Also, the higher the current density is, the easier the pulse waveforms are distorted and the time (the duration of complete pause) during which practically no current flows becomes shorter than the pause duration (the duration of current interruption) of the current with ideal waveform. Taking that in consideration, the relation between the duration of current interruption and the duration of complete pause is studied and in the present invention, the duration of complete pause is regulated to at shortest one half of the duration of current interruption, because cracking occurred when the du

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Metal plating method does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Metal plating method, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Metal plating method will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3141242

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.