Meltblown fibrous sorbent media and method of making sorbent...

Adhesive bonding and miscellaneous chemical manufacture – Methods – Surface bonding and/or assembly therefor

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C156S181000, C156S252000, C156S270000, C156S290000, C156S308200, C264S112000, C264S126000

Reexamination Certificate

active

06270608

ABSTRACT:

BACKGROUND OF THE INVENTION
The present invention relates to “throw away” meltblown fibrous sorbent media of thermoplastic fibers and, in particular, to meltblown fibrous sorbent media of thermoplastic fibers which are especially suited for absorbing oil or water and other liquids and the method of making such sorbent media:
Fibrous sorbent media made of thermoplastic fibers are used for many clean up applications including but not limited to: cleaning up oil spills on water; cleaning machinery, engines and other equipment; cleaning up oil, water, grease or other liquids from floors and other surfaces; etc. Typically, these fibrous sorbent media are intended to be properly discarded after only one use or only a few uses.
Fibrous polypropylene sorbent media is particularly well suited for such tasks. For example, fibrous polypropylene sorbent media has an affinity for oil and is hydrophobic. Thus, fibrous polypropylene sorbent media will soak up or absorb oil without absorbing water and can be used effectively to clean up oil spills on water. When the fibers of fibrous polypropylene sorbent media are treated or coated with a surfactant, the media will absorb water and other similar liquids. Thus, when treated with a surfactant, fibrous polypropylene sorbent media can be used to clean up water and other liquids in addition to oil.
Previously, the process for producing the fibrous sorbent media manufactured and sold by Johns Manville International, Inc., has essentially included three processes. In the first process, a thin meltblown tightly bonded cover stock is formed having a basis weight of about 0.75 oz/yd
2
or another cover stock, such as but not limited to a spun bond cover stock is formed. In the second process an air-laid, non-woven mat or fibrous layer of loose lofty randomly oriented meltblown thermoplastic fibers, e.g. polypropylene fibers having a mean diameter of about 15 microns, and of the required thickness is formed. In a third process a heated pin or calendar roll collates a layer of cover stock onto each major surface of the mat or fibrous layer and, through the heated pins of a pin or calendar roll, heat point bonds the layers of cover stock to the major surfaces of the mat. The resulting product is a fibrous sorbent media laminate with a fibrous core layer of loose lofty fibers encapsulated between two surface layers of cover stock that are heat point bonded to the fibrous core layer. The loose fibers within the media provide an effective surface area for good liquid absorption and the layers of cover stock provide the laminate with the required tensile strengths and abrasion resistance. The heat point bonding of the layers of cover stock to the fibrous core layer provides the fibrous sorbent media with added integrity and improves the “handle-ability” of the product. Fibrous thermoplastic sorbent media laminates, such as the sorbent media just described, provide good liquid absorption for many applications. However, since these sorbent media are primarily used for applications where the sorbent media is discarded after only one use or only a few uses, there has remained a need for fibrous thermoplastic sorbent media, with equal or better liquid absorption and abrasion resistance properties, that can be more economically produced.
SUMMARY OF THE INVENTION
The fibrous sorbent media of the present invention and the method of making the fibrous sorbent media of the present invention provide fibrous sorbent media that have liquid absorption and abrasion resistance properties which are equal to or greater than the fibrous sorbent media laminates of Johns Manville International Inc. discussed above and media which can be produced more economically (e.g. cost savings of up to 30% to 40%) than the fibrous sorbent media laminates of Johns Manville International Inc. discussed above. The sorbent media of the present invention is made of thermoplastic fibers having a mean diameter between about 0.5 microns and about 25 microns; has a weight between about 2 oz/yd
2
and about 25 oz/yd
2
; a thickness typically between about {fraction (1/20)} of an inch and about ½ of an inch; a lofty fibrous core; and first and second major surfaces with thin, relatively tough, tear and abrasion resistant, integral skins thereon. The skins are liquid permeable and permit liquids, such as but not limited to oil and water, to pass easily through the skins for absorption in the fibrous core of the sorbent media. The abrasion resistant skins add to the tensile strength of the sorbent media; help to keep the sorbent media from tearing apart in use; and prevent or greatly reduce the loss of fibers from the sorbent media in use, especially when the sorbent media is used for wiping machinery, floors, etc.
The abrasion resistant integral skins of the mat are formed by melting fibers at and immediately adjacent the major surfaces of the non-woven mat to form thermoplastic melt layers which are subsequently solidified into the abrasion resistant skins on the major surfaces of the mat. For many applications, the thermoplastic fibers of the mat are point bonded together at spaced apart locations to increase the integrity of the mat and, preferably, increase the thickness or loft of the mat adjacent the point bonded locations.
The method of forming the sorbent media of the present invention, e.g. on an on-line process, includes: air laying thermoplastic fibers having a mean fiber diameter between about 0.5 microns and about 25 microns to form a non-woven mat; melting the thermoplastic fibers at and immediately adjacent the major surfaces of the mat to form thermoplastic melt layers on the major surfaces of the mat; subsequently cooling the thermoplastic melt layers to form thin, integral thermoplastic, liquid permeable skins on the major surfaces of the mat; and, normally, point bonding the thermoplastic fibers of the mat together at spaced apart locations to increase the integrity of the mat and preferably, increase the loft of the mat adjacent the point bonds by displacement of some of the thermoplastic fibers from the locations of the point bonds.
The thermoplastic fibers at and immediately adjacent the major surfaces of the mat can be melted to form a thermoplastic melt layer on the major surfaces of the mat by flame treating, infrared treating or corona treating the surfaces of the mat. However, preferably, the thin, integral skins are formed on the major surfaces of the mat by passing the mat between a pair of heated nip or calendar rolls with smooth surfaces. Preferably, the major surfaces of the mat on which skins are being formed are pressed against the heated surfaces of the nip or calendar rolls by compressing the mat between the pair of heated nip or calendar rolls. It is believed that the compression of the mat brings more fibers into contact with the heated surfaces of the nip or calendar rolls and increases the density of the mat at and adjacent the heated surfaces of the nip or calendar rolls for better heat transfer from the nip or calendar rolls into the thermoplastic fibers of the mat. The result is a better melting of the thermoplastic fibers at and immediately adjacent the major surfaces of the mat to form melt layers on the major surfaces of the mat that are subsequently cooled and solidified to form the relatively tough, tear and abrasion resistant, liquid permeable, integral skins. When skins were formed on major surfaces of a mat without compressing the mat between heated nip or calendar rolls, the quality of the skin formed was considerably inferior to the skins formed by compressing the mat between heated nip or calendar rolls.
The compression of the mat between a pair of heated nip or calendar rolls, decreases the thickness of the mat. Accordingly, the thickness and resiliency of the non-woven mat being introduced into the skin forming station of the process line must be sufficient to accommodate the decrease in thickness caused by the skin forming operation without permanently decreasing the thickness and absorbent properties of the mat below acceptable levels.
P

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Meltblown fibrous sorbent media and method of making sorbent... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Meltblown fibrous sorbent media and method of making sorbent..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Meltblown fibrous sorbent media and method of making sorbent... will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2436084

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.