Melt spinning of ultra-oriented crystalline polyester filaments

Details Melt spinning of ultra-oriented crystalline polyester filaments Melt spinning of ultra-oriented crystalline polyester filaments

1990-05-18

1992-09-22

Lorin, Hubert C.

Plastic and nonmetallic article shaping or treating: processes

Forming continuous or indefinite length work

Shaping by extrusion

264181, 2642108, 26421114, 26421117, D01D 662

Patent

active

051494809

ABSTRACT:
Ultra-oriented, crystalline synthetic filaments with high tenacity are produced by extrusion of a fiber-forming synthetic polymer melt into a liquid isothermal bath maintained at a temperature of at least 30.degree. C. above the glass transition temperature of the polymer, withdrawing the filaments from the bath and then winding up the filaments. Polyethylene terephthalate filaments so produced at 3000-5000 m/min exhibit a crystalline structure and possess birefringence of 0.20-0.22, tenacity of 7-9 g/d, break elongation of 14%-30% and boil-off shrinkage of 5%-10%.

REFERENCES:
patent: 3002804 (1961-10-01), Kilian
patent: 4134882 (1979-01-01), Franfort et al.
patent: 4425293 (1984-01-01), Vassilatos
patent: 4446299 (1984-05-01), Koschinek et al.
patent: 4909976 (1990-03-01), Cuculo et al.
T. Kawaguchi, Industrial Aspects of High-Speed Spinning, Chapter 3, "Industrial View on High-Speed Spinning", pp. 8-15.

Affiliated with

Also associated with

Rating

Melt spinning of ultra-oriented crystalline polyester filaments does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Melt spinning of ultra-oriented crystalline polyester filaments, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Melt spinning of ultra-oriented crystalline polyester filaments will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-1066622