ABSTRACT:
TECHNICAL FIELD
This invention relates to a temperature compensating member having a negative coefficient of thermal expansion and an optical communication device using the same.
BACKGROUND ART
With the advance of the optical communication technology, a network using optical fibers has been rapidly built up. In the network, a wavelength multiplexing technique of collectively transmitting light beams having a plurality of different wavelengths has come into use, and a wavelength filter, a coupler, a waveguide, and the like have become important devices.
Some of the devices of the type described are changed in characteristics depending upon the temperature and may therefore cause troubles if used in the outdoors. This requires a technique for keeping the characteristics of these devices fixed or unchanged regardless of a temperature change, i.e., a so-called temperature compensating technique.
As a typical optical communication device which requires temperature compensation, there is a fiber Bragg grating (hereinbelow, referred to as FBG). The FBG is a device in which a portion varied in refractive index in a grid-like pattern, i.e., a so-called grating is formed within a core of an optical fiber, and has a characteristic of reflecting a light beam having a specific wavelength according to the relationship represented by the following formula (1). Therefore, the device attracts attention as an important optical device in the optical communication system using a wavelength division multiplex transmission technique in which optical signals different in wavelengths are multiplexed and transmitted through a single optical fiber.
&lgr;=2n&Lgr; (1)
Herein, &lgr; represents a reflection wavelength, n, an effective refractive index of the core, and &Lgr;, a grid interval of the portion varied in refractive index in the grid-like pattern.
However, the above-mentioned FBG has a problem that the reflection wavelength will be varied following the change in ambient temperature. The temperature dependency of the reflection wavelength is represented by the following formula (2) which is obtained by differentiating the formula (1) with the temperature T.
∂
λ
/
∂
T
=
2
{
(
∂
n
/
∂
T
)
Λ
+
n
(
∂
Λ
/
∂
T
)
}
=
2
Λ
{
(
∂
n
/
∂
T
)
+
n
(
∂
Λ
/
∂
T
)
/
Λ
}
(
2
)
The second term of the right side of the formula (2), i.e., (∂&Lgr;/∂T)/&Lgr; corresponds to a coefficient of thermal expansion of the optical fiber and has a value approximately equal to 0.6×10
−6
/° C. On the other hand, the first term of the right side corresponds to the temperature dependency of a refractive index of the core portion of the optical fiber and has a value approximately equal to 7.5×10
−6
/° C. Thus, it will be understood that the temperature dependency of the reflection wavelength depends on both the variation in refractive index of the core portion and the change in grid interval due to thermal expansion but mostly results from the temperature-dependent variation of the refractive index.
As means for avoiding the above-mentioned variation in reflection wavelength, there is known a method in which the FBG is applied with tension depending upon the temperature change to thereby change the grid interval so that a component resulting from the variation in refractive index is cancelled.
As a specific example of the above-mentioned method, proposal is made of a method in which the FBG is fixed to a temperature compensating member which comprises a combination of a material, such as an alloy or a silica glass, having a small coefficient of thermal expansion and a metal, such as aluminum, having a large coefficient of thermal expansion. Specifically, as shown in
FIG. 1
, an Invar (trademark) bar
10
having a small coefficient of thermal expansion has opposite ends provided with Al brackets
11
a
and
11
b
having a relatively large coefficient of thermal expansion attached thereto, respectively. An optical fiber
13
is fixed to these brackets
11
a
and
11
b
by the use of clasps
12
a
and
12
b
so that the optical fiber is stretched under a predetermined tension. At this time, adjustment is made so that the grating portion
13
a
of the optical fiber
13
is located between the two clasps
12
a
and
12
b.
If the ambient temperature rises in the above-mentioned state, the brackets
11
a
and
11
b
are expanded to reduce the distance between the two clasps
12
a
and
12
b
so that the tension applied to the grating portion
13
a
of the optical fiber
13
is decreased. On the other hand, as the ambient temperature falls, the brackets
11
a
and
11
b
are contracted to increase the distance between the two clasps
12
a
and
12
b
so that the tension applied to the grating portion
13
a
of the optical fiber
13
is increased. Thus, by changing the tension applied to the FBG depending upon the temperature change, it is possible to adjust the grid interval of the grating portion. As a result, it is possible to cancel the temperature dependency of the reflection center wavelength.
However, the above-mentioned temperature compensating device is disadvantageous in that the structure is complicated and the handling is difficult.
As a method for solving the above-mentioned disadvantages, Japanese Unexamined Patent Publication No. 2000-503415 or Japanese Unexamined Patent Publication No. 2000-503967 discloses a method shown in
FIG. 2
, in which a FBG
16
is, under a tension applied by a weight
15
, fixed to a glass ceramic substrate
14
having a negative coefficient of thermal expansion, by use of an adhesive
17
, which substrate is obtained by heat-treating and crystallizing a raw glass material preliminarily formed into a plate shape. The tension is controlled by expansion or contraction of the glass ceramic substrate
14
. In order to cancel the temperature dependency of the reflection center wavelength, it is necessary to apply a stress in a direction of contraction of the FBG when temperature rises and in a direction of expansion when temperature falls, as described above. As long as the substrate material has a negative coefficient of thermal expansion, such stress can be produced by a single component. The invention disclosed in the Japanese Unexamined Patent Publication No. 2000-503415 or the Japanese Unexamined Patent Publication No. 2000-503967 is achieved on the basis of the function and the effect mentioned above. In
FIG. 2
,
16
a
represents a grating portion.
The method disclosed in the Japanese Unexamined Patent Publication No. 2000-503415 or the Japanese Unexamined Patent Publication No. 2000-503967 is advantageous in that the structure is simple and the handling is easy because temperature compensation is achieved by a single component. However, there is a problem that the glass ceramic member used in the method is large in hysteresis of thermal expansion. The hysteresis of thermal expansion is a phenomenon in which, when a material expands or contracts following a temperature change, an expanding behavior upon temperature elevation does not coincide with that upon temperature drop.
In addition, the Japanese Unexamined Patent Publication No. 2000-503415 or the Japanese Unexamined Patent Publication No. 2000-503967 discloses a method for the purpose of diminishing the hysteresis of the glass ceramic member, in which a heat-cycle treatment is carried out at a temperature between 400 and 800° C. to stabilize an internal structure. However, the hysteresis diminished by the method described above is unstable against a change in environment such as temperature or humidity and it is therefore difficult to maintain its initial value. Further, the above-mentioned heat treatment requires a complicated manufacturing process, resulting in a problem of a high cost.
Therefore, it is an object of the present invention to provide a temperature compensating member which is small in hysteresis of thermal expan
Matano Takahiro
Sakamoto Akihiko
Collard & Roe P.C.
Healy Brian
Nippon Electric Glass Co. Ltd.
LandOfFree
Material for temperature compensation, and optical... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Material for temperature compensation, and optical..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Material for temperature compensation, and optical... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2921716