ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The invention relates to monomeric or oligomeric materials in which polymerization-induced shrinkage is desirably avoided. In particular, the invention relates to holographic recording media formed from such materials.
2. Discussion of the Related Art
Developers of information storage devices and methods continue to seek increased storage capacity. As part of this development, so-called page-wise memory systems, in particular holographic systems, have been suggested as alternatives to conventional memory devices. Page-wise systems involve the storage and readout of a representation, e.g., a page, of data. Typically, recording light passes through a two-dimensional array of dark and transparent areas representing data, and the holographic system stores, in three dimensions, holographic representations of the pages as patterns of varying refractive index in a storage medium. Holographic systems are discussed generally in D. Psaltis et al., “Holographic Memories,”
Scientific American,
November 1995, the disclosure of which is hereby incorporated by reference. One method of holographic storage is phase correlation multiplex holography, which is described in U.S. Pat. No. 5,719,691 issued Feb. 17, 1998, the disclosure of which is hereby incorporated by reference. In one embodiment of phase correlation multiplex holography, a reference light beam is passed through a phase mask, and intersected in the recording medium with a signal beam that has passed through an array representing data, thereby forming a hologram in the medium. The spatial relation of the phase mask and the reference beam is adjusted for each successive page of data, thereby modulating the phase of the reference beam and allowing the data to be stored at overlapping areas in the medium. The data is later reconstructed by passing a reference beam through the original storage location with the same phase modulation used during data storage.
FIG. 1
illustrates the basic components of a holographic system
10
. System
10
contains a modulating device
12
, a photorecording medium
14
, and a sensor
16
. Modulating device
12
is any device capable of optically representing data in two-dimensions. Device
12
is typically a spatial light modulator that is attached to an encoding unit which encodes data onto the modulator. Based on the encoding, device
12
selectively passes or blocks portions of a signal beam
20
passing through device
12
. In this manner, beam
20
is encoded with a data image. The image is stored by interfering the encoded signal beam
20
with a reference beam
22
at a location on or within photorecording medium
14
. The interference creates an interference pattern (or hologram) that is captured within medium
14
as a pattern of, for example, varying refractive index. It is possible for more than one holographic image to be stored at a single location and/or for holograms to be stored in overlapping positions, by, for example, varying the angle, the wavelength, or the phase of the reference beam
22
, depending on the particular reference beam employed. Signal beam
20
typically passes through lens
30
before being intersected with reference beam
22
in the medium
14
. It is possible for reference beam
22
to pass through lens
32
before this intersection. Once data is stored in medium
14
, it is possible to retrieve the data by intersecting reference beam
22
with medium
14
at the same location and at the same angle, wavelength, or phase (depending on the multiplexing scheme used) at which reference beam
22
was directed during storage of the data. The reconstructed data passes through lens
34
and is detected by sensor
16
. Sensor
16
is, for example, a charged coupled device or an active pixel sensor. Sensor
16
typically is attached to a unit that decodes the data.
The capabilities of such holographic storage systems are limited in part by the storage media. Iron-doped lithium niobate has been used as a storage medium for research purposes for many years. However, lithium niobate is expensive, is relatively poor in sensitivity (1 J/cm
2
), has relatively low index contrast (An of about 10
−4
), and exhibits destructive read-out (i.e., images are destroyed upon reading). Alternatives have therefore been sought, particularly in the area of photosensitive polymer films. See, e.g., W. K. Smothers et al., “Photopolymers for Holography,” SPIE OE/Laser Conference, 1212-03, Los Angeles, Calif., 1990. The material described in this article contains a photoimageable material system containing a liquid monomer material (the photoactive monomer) and a photoinitiator (which promotes the polymerization of the monomer upon exposure to light), where the photoimageable material system is located within an organic polymer host matrix that is substantially inert to the exposure light. During writing of information into the material by exposure to radiation in selected areas, the monomer polymerizes in the exposed regions. Due to the lowering of the monomer concentration caused by induced polymerization, monomer from the dark, unexposed regions of the material diffuses to the exposed regions. The polymerization and resulting concentration gradient create a refractive index change, forming the hologram representing the data.
Most holographic systems of this type are based on photopolymerization of free-radical photosensitive monomers such as acrylate esters. See, for example, U.S. patent application Ser. No. 08/698,142 (our reference Colvin-Harris-Katz-Schilling 1-2-16-10), the disclosure of which is hereby incorporated by reference. A variety of such photosensitive monomers are commercially available. While media based on such monomers provide useful results, it is possible for such media to encounter several limitations. One typical problem is shrinkage introduced into a recording medium due to the polymerization of the photosensitive monomer. Specifically, because polymerized monomers occupy a smaller volume than individual monomers, each step of writing data into a recording medium introduces localized shrinkage. The combined effect of the localized shrinkage increases the difficulty in accurately retrieving the stored data.
One way to address this shrinkage problem is to adjust the optics of a holographic storage system based on the shrinkage, e.g., rotating the orientation of the medium based on the extent of shrinkage, as discussed in Zhao et al., “Shrinkage-corrected volume holograms based on photopolymeric phase media for surface-normal optical interconnects,”
Appl. Phys. Lett.
71 (11), Sep. 15, 1997, at 1464. Such a method is useful for some types of holographic storage, but is not suitable for data storage applications where images with a well-defined angular bandwidth are recorded.
Some photosensitive monomers were developed which exhibited less shrinkage than conventionally-used acrylate monomers. These monomers not only formed holograms by polymerization (as discussed above), but also exhibited ring-opening during such polymerization. (See, e.g., Waldman et al., “Cationic Ring-Opening Photopolymerizatin Methods for Volume Hologram Recording,”
SPIE
Vol. 2689, 1996, at 127.) Waldman et al. used epoxy polymerization to form holograms, and, because epoxy polymerization involves opening of epoxide monomer rings, the polymerization exhibits about half as much shrinkage as acrylate polymerizations.
It has further been proposed that spiro-orthoesters and spiro-orthocarbonates, so-called expanding monomers, be added to epoxy polymerization systems or employed as the sole polymerizing monomers. (See, e.g.,
Expanding Monomers: Synthesis. Characterization, and Applications
(R. K. Sadhir and R. M. Luck, eds., 1992) 1-25, 237-260; T. Takata and T. Endo, “Recent Advances in the Development of Expanding Monomers: Synthesis, Polymerization and Volume Change,”
Prog. Polym. Sci.,
Vol. 18, 1993, 839-870.) Such spiro compounds have been reported to exhibit relatively small shrinkage, or even expansion, upon polymerization due to op
Dhar Lisa
Katz Howard Edan
Angebranndt Martin
Lucent Technologies - Inc.
Rittman Scott J.
LandOfFree
Material exhibiting compensation for polymerization-induced... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Material exhibiting compensation for polymerization-induced..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Material exhibiting compensation for polymerization-induced... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2444346