ABSTRACT:
FIELD OF THE INVENTION
The present invention relates to a mask film, a method of manufacturing the same, and a method of manufacturing a circuit board using the same.
BACKGROUND OF THE INVENTION
In the recent trend of smaller size and higher density of electronic devices, there is an increasing demand for multi-layer structure of circuit boards in the fields of industrial and consumer products. In such circuit boards, it is required to develop newly a manufacturing method for connecting circuit patterns of a plurality of layers with inner via holes, and a circuit board structure having a high reliability. As the manufacturing method of the two-sided circuit board, a manufacturing method of circuit board connecting inner via holes with conductive paste is proposed. This conventional manufacturing method of circuit board is explained below.
FIG. 8
is a sectional view of mask film used in manufacture of conventional circuit board.
FIG. 9
is a perspective view of a mask film in manufacture of conventional circuit board, showing the position of a large tension.
A conventional mask film
22
has a base material
11
, and a parting layer
12
placed on the whole surface of the base material
11
. The base material
11
is made of polyethylene terephthalate. In the manufacturing method of two-sided circuit board, the mask film is adhered to both sides of a prepreg sheet so that the parting layer
12
side may be positioned on the surface of the prepreg sheet. The prepreg sheet has a base and a resin impregnated in the base.
Penetration holes are formed in specified positions of the prepreg sheet to which the mask film
22
is adhered.
The penetration holes are filled with conductive paste. The conductive paste filling method comprises a step of putting the prepreg sheet having penetration holes on a table of a general printing press, and a step of applying conductive paste directly from above the mask film
22
by using a squeegee. At this time, the mask film
22
plays the role as printing mask, and also the role of prevention of contamination of the surface of the prepreg sheet.
The mask film
22
is parted from both sides of the prepreg sheet.
A metal foil is overlaid on both sides of the prepreg sheet.
The prepreg sheet having the metal foils is heated and pressed. In this process, the prepreg sheet and metal foils are mutually adhered. In this case, the metal foils adhered to both sides of the prepreg sheet are electrically connected to the conductive paste filling up the penetration holes formed in specified positions.
The both metal foils are selectively etched, and a circuit patterns are formed. Thus, a two-sided circuit board is manufactured.
In this conventional manufacturing method of multi-layer board, however, when the prepreg sheet and mask film are adhered, as shown in
FIG. 9
, the shrinkage stress
30
at four corners of a prepreg sheet
31
is larger than at other positions. Peeling occurs from these four corners. In the subsequent manufacturing process of conveying and handling, peeling expands gradually.
By forming the parting layer
12
of the mask film
22
very thinly to be 0.01 &mgr;m or less, pin holes are intentionally formed in the parting layer
12
. By these pin holes, the adhesion strength of the prepreg sheet and mask film is maintained.
When forming penetration holes in specified position by heating process such as laser process (in particular, CO
2
laser), the polyethylene terephthalate of the mask film
22
is melted by the process heat, and the molten material is fused with components of the prepreg sheet
31
. Accordingly, when parting the mask film
22
from the prepreg sheet
31
, the resin component or base in the prepreg sheet
31
may be peeled together with the mask film
22
.
Depending on presence or absence of penetration holes, the adhesion strength of the metal foils and the prepreg sheet
31
varies, and peeling is likely to occur by impact. Accordingly, part of the conductive paste may be peeled off. In this conventional method, conditions of these steps have large effects on the quality of the two-sided circuit board.
SUMMARY OF THE INVENTION
A mask film for manufacturing a circuit board of the invention comprises a base material, a parting layer placed on the base material, and a non-parting portion.
A manufacturing method of circuit board of the invention comprises:
(a) a step of preparing a mask film, in which the mask film comprises a base material, a parting layer and a non-parting portion placed on the base material,
(b) a step of adhering the mask film to both sides of a prepreg sheet, in which the parting layer and non-parting portion are adhered to the prepreg sheet,
(c) a step of forming a penetration hole in specified positions of the prepreg sheet having the mask film,
(d) a step of filling the penetration hole with conductive paste from the mask film side, using the mask film as the mask,
(e) a step of parting the mask film from the prepreg sheet,
(f) a step of overlaying metal foils on both sides of the prepreg sheet,
(g) a step of heating and pressing the prepreg sheet having the metal foils, and adhering the prepreg sheet and metal foils mutually, so that the metal foils placed at both sides are connected electrically with each other through the conductive paste filling up the penetration hole, and
(h) a step of etching the metal foils selectively to form circuit patterns.
Preferably, the parting layer is placed on the surface of the base material, the non-parting portion is formed on the surface of the base material, and the non-parting portion is formed in the region excluding the parting layer.
Preferably, the non-parting portion is formed at both ends along the length direction of the base material, parallel to the both ends.
Preferably, the non-parting portion has an adhesive layer or adhesion strength adjusting pattern.
In this constitution, an optimum adhesion strength between mask film and prepreg sheet is assured, and peeling between mask film and prepreg sheet is prevented. Further, a fusing adhesion between mask film and prepreg sheet by heat when forming penetration holes is prevented. As a result, a circuit board having an excellent quality is obtained.
REFERENCES:
patent: 4268614 (1981-05-01), Ueyama et al.
patent: 4642160 (1987-02-01), Burgess
patent: 4915983 (1990-04-01), Lake et al.
patent: 5358604 (1994-10-01), Lin et al.
patent: 6163957 (2000-12-01), Jian et al.
patent: 6368697 (2002-04-01), Petti et al.
patent: 1054582 (2000-11-01), None
patent: 1180921 (2002-02-01), None
patent: 6-268345 (1994-09-01), None
patent: 7-106760 (1995-04-01), None
Echigo Fumio
Kishimoto Kunio
Kondo Toshikazu
Nakamura Shinji
Takenaka Toshiaki
Matsushita Electric - Industrial Co., Ltd.
McDermott & Will & Emery
Trinh Minh
LandOfFree
Mask film having a non-parting portion does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Mask film having a non-parting portion, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Mask film having a non-parting portion will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3335109