ABSTRACT:
This application claims priority under 35U.S.C. §§119 and/or 365 to Japanese Patent Application No. 10-348187 and No. 11-231382 filed in Japan on Dec. 8, 1998 and Aug. 18, 1999, respectively, the entire content of which is herein incorporated by reference.
BACKGROUND OF THE INVENTION
The present invention relates to a martensitic stainless steel product containing chromium in the range of 9 to 15% by weight, which is mainly used under environments containing hydro-sulfide such as oil wells and gas wells (hereinafter, referred to simply as “oil well”) or chemical plants. In particular, the present invention concerns a martensitic stainless steel product which is superior in weatherability under atmospheric environments during transportation and storage, and also superior in corrosion resistance, more specifically, in sulfide stress cracking resistance, even Linder environments containing hydro-sulfide.
With respect to steel products widely used in the application under oil well environments, steel pipes, steel sheets, etc. are listed, and among these, the steel pipes include seamless steel pipes and welded steel pipes.
One of the typical production methods for seamless steel pipes is the so-called Mannesmann-mandrel mill method, and this method is widely used because of its superior dimensional precision and productivity.
Its pipe making process generally consists of a heating process in which a round billet as a material is heated to a predetermined processing temperature, a piercing process in which the heated round billet is formed into a hollow shell by using a piercing mill, an elongating process in which the hollow shell is formed into a pipe for finish rolling by using a mandrel mill, a re-heating process in which the pipe for finish rolling is again heated, and a finish rolling process in which the pipe for finish rolling thus again heated is shaped so as to have a predetermined product dimension by using a stretch reducing mill.
In this case, in general, the heating temperature of the material round billet is set at 1100 to 1300° C., the pipe temperature after the elongating process by the mandrel mill is set at 800 to 1000° C., the reheating temperature of the pipe for finish rolling is set at 850 to 1100° C., and the finish temperature by the stretch reducing mill is set at 800 to 1000° C.
In the case of welded steel pipes, a steel sheet as a material is finished so as to have a predetermined product dimension by using a method, such as an ERW (electric-resistance welding)-pipe making method, a UO-(UO press-submerged arc welding)-pipe making method, and a laser welding-pipe making method.
Thereafter, in the case of the steel pipe made of martensitic stainless steel containing chromium in the range of 9 to 15% by weight (hereinafter, referred to simply as “martensitic stainless steel pipe”), the product is further subjected to a quenching process at not less than 900° C., and then to a tempering process at 600 to 750° C. so as to impart a predetermined strength.
During the producing process of such a martensitic stainless seamless steel pipe or steel plate for welded steel pipe, in the case of the seamless steel pipe, it is subjected to a heat treatment of 600 to 1300° C. during the respective processes, and in the case of the welded steel pipe, a steel plate is subjected to heating at 600 to 1000° C. during a formation process into a steel pipe and a heat treatment process after the pipe formation. For this reason, oxide scales (hereinafter, referred to simply as “mill scales”) inevitably are generated on the inner and outer surfaces of the pipe.
Normally, mill scales are completely removed by a pickling process applied after the shot blasting process. This is because, in general, it is considered that a chromium depression zone exists in the base material steel right under the mill scales and that a desirable corrosion resistance can not be obtained without removing this chromium depression zone as well as the mill scales.
The combination of the shot blasting process and the succeeding pickling process is provided because the application of only the pickling process takes a long time to completely remove the mill scales and the chromium depression zone, resulting in degradation in productivity.
However, the pickling process requires a number of sub-processes and great costs, resulting in degradation in productivity and an increase in the production costs of the products, as well as causing deterioration in working environments due to acid mist, etc. For this reason, from the viewpoints of improvements in productivity, maintenance of good working environments and reduction of the production costs of the products, there have been ever-increasing demands for the simplification of the pickling process, and further, the elimination of the pickling process.
With respect to the shot blasting process, methods are proposed in which grains made of 13% chromium steel, which is the same as the processed steel, or alumina are used as the grains for shot blasting. The reason for this is described as follows: if iron grains are used for the blasting process for stainless steel, pulverized fine particles resulting from the iron grains for shot blasting remain on the surface of the stainless steel product, and in the case when the pickling process is omitted, rust develops from the fine particles of the iron grains for shot blasting serving as starting points in atmospheric environments; this causes so-called rust deposition, resulting in deterioration in the appearance of the products. Moreover, the rust deposition serves as a starting point of the occurrence of pitting corrosion, and accelerates corrosion under actual service environments, such as, high-temperature, high-moisture environments including carbon dioxide gas and hydro-sulfide in the case of oil country tubuler goods.
However, even in the case when the grains for shot blasting made of 13% chromium steel or alumina are used, the martensitic stainless steel containing chromium in the range of 9 to 15% by weight is sometimes subjected to slight corrosion when left in atmospheric environments, if the pickling process is omitted.
Conventionally, there is hardly any researches made on the relationship between the operation conditions of the shot blasting process and the generation of rust. At present, in actual operations, a pickling process for a short period of time is further carried out after the shot blasting process, or the processing time of the shot blasting is extended sufficiently longer than is necessary so as to completely blast and remove the chromium depression zone; consequently, the efficiency of the shot blasting process deteriorates.
However, some researches have been made on not only these grains for shot blasting, but also the shot blasting method itself. More specifically, in a commonly-used shot blasting method which is a so-called pressure blast system, grains for shot blasting are discharged and blasted onto target materials together with compressed air. However, the pressure blast system has the following problems: Running costs increase because of a high power consumption of the compressor, the compressor generates a high pressure, resulting in the possibility of rupturing, and fine grains of shot blasting scatter around, causing degradation in the working environments.
For this reason, a so-called vacuum suction blast system which utilizes the air suction function of an air suction device, has been proposed as a new shot blasting method for shot blasting a pipe inner surface. For example, this method is proposed by Japan Laid-Open Patent Application No. 60-263671. Moreover, blasting devices of the vacuum suction blast system, which enhance the blasting efficiency of this method by adjusting the difference in static pressures or circulating the air flow, have been proposed by, for example, Japanese Laid-Open Patent Application No. 63-22271 and Japanese Laid-Open Patent Application No. 6-270065.
However, the objective of these conventional proposals is to make the vacuum suction blast process more e
Amaya Hisashi
Anraku Toshiro
Hidaka Yasuyoshi
Burns Doane , Swecker, Mathis LLP
Sumitomo Metal Industries Ltd.
Yee Deborah
LandOfFree
Martensitic stainless steel products does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Martensitic stainless steel products, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Martensitic stainless steel products will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2878559