DESCRIPTION:
BRIEF SUMMARY
TECHNICAL FIELD
The present invention relates to a manufacturing method of composite sheet material which is formed by impregnating a synthetic resin in a glass fiber sheet.
BACKGROUND ART
A composite sheet material with a synthetic resin impregnated in a glass fiber sheet material is universally applied as a blank of various industrial products. Such composite sheet material is available in the forms of prepreg material wherein an impregnation resin is retained as uncured and cure material wherein an impregnation resin is fully cured. However, it has never been made in a prior art that a single composite sheet material is provided with surfaces one of which is retained as uncured and other of which is fully cured.
Though it is easy to apply a deformation processing to the prepreg material, the material may not readily accept an automatic punching or mold releasing operations. In turn, though it is easy to punch or release the cure material from a mold, the material may not readily accept a deformation processing and tends to resume its original shape after processed.
Therefore, an extreme industrial benefit will be derived if a composite sheet material possessing advantageous characteristics of above two materials in combination is available to use.
DISCLOSURE OF THE INVENTION
The present invention provides a manufacturing method of composite sheet material wherein one surface is retained as uncured and its other surface is fully cured, by use of glass fiber sheet material with a synthetic resin impregnated therein.
BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1 is a schematic illustrative view of manufacturing method of composite sheet material built in accordance with the present invention; and
FIG. 2 is a longitudinal cross-sectional view of sheet material in each step of manufacturing method in FIG. 1, illustrating respective conditions of sheet material.
BEST MODE OF CARRYING OUT THE INVENTION
In accordance with the manufacturing method of composite sheet material of the present invention, a resin is impregnated in a sheet material 3a by moving the sheet material to pass through a tank 2 containing a synthetic resin 20 therein, after the roll 1 of glass fiber sheet material is unwound, as shown in FIG. 1. A resin impregnated sheet material 3b is dried in a dying furnace 4, to place the resin in position. Then, the sheet material 3b dried is moved to a heating and cooling device 5 wherein one surface of material is heated up and its other surface is cooled down. The composite sheet material 3c thus formed is taken up as a roll 6.
The glass fiber sheet material 3a [FIG. 2(A)] is selected from a commercially available one which has been formed by weaving a glass fiber in a sheet-like configuration.
The synthetic resin is a thermally resistant and hot setting type such as, for example, a polyimide and a phenol butyral compound resin and the like. The resin is contained in the tank 2 in a liquidized state at an ambient temperature. The resin impregnated sheet material 3b is formed by impregnating a resin 20 uniformly into the glass fiber sheet material 3a and causing a resin film 21 to adhere uniformly to upper and lower surfaces of material, as shown in FIG. 2(B).
The drying furnace 4 serves to evaporate the solvent of resin by spraying a hot air moderately against the sheet material 3a. The drying furnace 4 should preferably maintain its internal temperature at 150.degree.-l60.degree. C. and its duration time of 5-12 minutes.
The heating and cooling device 5 consists of a heating unit 51 and a cooling unit 52 each of which is arranged to oppose against one surface of sheet material 3b. The heating unit 51 can blow out a very hot air therefrom and cures a resin which has been impregnated in or adhered to the sheet material 3b by directing a very hot air against the surface of sheet material 3b. The layer thus cured is called as a cure layer 21c [FIG. 2(C)] hereinbelow. Preferably, such very hot air should maintain its temperature at 200.degree.-240.degree. C. and its flow rate of 5-8 m.sup.3 /min.
REFERENCES:
patent: 4158070 (1979-06-01), Lewicki et al.
patent: 4505951 (1985-03-01), Kennedy
patent: 4590102 (1986-05-01), Rogamilia et al.
Lusignan Michael R.
Suzuki Kanshi Co., Ltd.
LandOfFree
Manufacturing method of composite sheet material having differen does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Manufacturing method of composite sheet material having differen, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Manufacturing method of composite sheet material having differen will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-8496