ABSTRACT:
BACKGROUND OF THE INVENTION
1. An Technical Field Affiliated with the Invention
The present invention concerns the manufacturing methods of an anisotropic magnet powder, the precursory anisotropic magnet powder and it manufacturing method, as well as a bonded magnet made from this powder.
2. The Conventional Technique
Magnets are widely used in many of the machines in our surroundings, including various types of motors. There is a need for a stronger permanent magnet in order to reduce the weight, thickness and length of an the increase efficiency of these machines. A rare earth element magnet (RFeB magnet) mainly composed of Nd
2
Fe
14
B has been attracting much attention as a candidate for such a permanent magnet, and its range of applications has been expanded greatly. For example, it is being considered as a motor magnet in various types of machines in the automobile engine room. Here it is desired that the magnet have a high heat resistance because the temperature inside the engine room exceeds 100° C.
However, the precursory anisotropic magnet powder (RFeB magnetic powder) has large temperature dependence (temperature coefficient), which causes a poor heat-resistance. The coercivity decreases rapidly at the high range of temperatures. It has been difficult to readily improve the temperature dependency so far. A remedy for this may be the use of an anisotropic magnet powder which originally has a very large coercive force (iHc), so that the magnet may keep a large enough coercive force even at the high range of temperatures. Such an anisotropic magnet powder and its manufacturing methods have been disclosed in Japanese laid-open patent numbers 9-165601 and 2000-96102.
Concretely, in Japanese laid-open patent number 9-165601, a manufacturing method of an anisotropic magnet powder by HDDR (hydrogenation—decomposition—desorption—recombination) method has been shown using an ingot to which a minute amount of Dy was added to the molten RfeB alloy, resulting in an average crystal radius ranging from 0.05-1 &mgr;m.
However, when the inventors actually tried to manufacture this anisotropic magnet powder, a stable coercivity could not be achieved due to the limited amount of Dy additive and the method was also difficult to mass-produce. In addition, the coercivity of the anisotropic magnet powder produced by this method was at most 16 kOe (1272 kA/m).
In general, a desirable anisotropic magnet powder should have large values for both coercivity (iHC) and degree of anisotropy (Br/Bs), where (Br) is the residual magnetic flux density and (Bs) is the saturation magnetic flux density. However, while the addition of Dy is efficient for improving the coercivity, it will also reduce the rate of HDDR reaction causing a decline in the degree of anisotropy. For these reasons, until now, these values have not been optimized at the same time.
In Japanese laid-open patent number 2000-96102, another manufacturing method of an anisotropic magnet powder is described in which and a Dy alloy powder is mixed with an already produced anisotropic magnet powder, and this mixture is heat treated under a vacuum or inactive gas atmosphere so that the anisotropic magnet powder receives a thin coating of Dy on its surface. In this way, an appropriate amount of Dy can be coated on the powder surface, increasing the coercivity to as high as 18 kOe (1432 kA/m) and maintaining a high degree of anisotropy.
However, because the starting material in this method is an anisotropic magnet powder such as Nd
2
Fe
14
B, the control of oxidization is difficult while Dy coating, there is substantial variation in the end powder's performance and quality. Thus a magnet made from this anisotropic magnet powder an uncontrollable loss of magnetization due to structure change, as will be discussed later, and a permanent magnet with stable heat-resistance could not be obtained.
SUMMARY OF THE INVENTION
1. A Problem to Solve in the Invention
The invention is proposed in light of the circumstances stated above, and intends to provide a manufacturing method of an anisotropic magnet powder by which a magnet with an improved coercivity and loss of magnetization due to structure change can be obtained with a high productivity and a constant quality.
The invention is also intended to provide a suitable precursory anisotropic magnet powder and to provide its manufacturing method, as well as to provide a bonded magnet with a high degree of permanent demagnetization.
2. A Means to Resolve the Problem
(1) The inventors devoted themselves to the resolution of the problem, making a systematic study on it with repeated trial and error, and finally found out that oxidation is inhibited if diffusion heat-treatment is carried out after blending a RFeB hydride powder material with R1 element diffusion powder containing Dy, while the process results in an anisotropic magnet powder in which Dy is uniformly diffused on the surface of and inside the powder. That is how the inventors came to develop the present invention of a manufacturing method of anisotropic magnet powder.
The manufacturing method of the present invention comprises the following processes;
A blending process of RFeB hydride (RFeBHx) powder, which is mainly composed of rare earth elements including yttrium (Y) (hereafter referred to as “R”), boron (B) and iron (Fe), with diffusion powder, which is composed of a simple substance, an alloy, a compound or a hydride of one or more elements in an elemental group which includes dysprosium (Dy), terbium (Tb), neodymium (Nd) and praseodymium (Pr) [hereafter referred to as “R1 elements”];
a diffusion heat-treatment process in which R1 elements are diffused uniformly on the surface and the inside of the RFeBHx powder; and
a dehydrogenation process (the second evacuation process) in which hydrogen is removed from the mixture of the powder after the diffusion heat-treatment process.
When RFeBHx powder and diffusion powder are mixed together in a blending process, R and Fe are difficult to oxidize compared to a conventional RFeB powder because the RFeBHx powder contains hydrogen. For this reason, in the following diffusion heat-treatment process, the diffusion of Dy, Tb, Nd and Pr (R1 elements) will diffuse into the surface and the inside of the RFeBHx powder with oxidization being sufficiently inhibited.
Furthermore, the speed of diffusion of R1 elements into the surface and the inside of the RFeBHx powder is enhanced by diffusion into the crystal particle boundaries and into the crystal particles, leading to uniform addition of R1 elements.
An anisotropic magnet powder with a large coercivity and a consistent quality can be achieved with RFeBHx powder material that can hardly be oxidized, and diffusion of R1 elements with inhibited oxidization. A bonded magnet molded from the anisotropic magnet powder obtained by this method will have an improved loss of magnetization due to structure change. This loss of magnetization is calculated using the magnetic flux when the sample magnet is initially put in a magnetic field and the magnetic flux after the sample is left under air atmosphere for 1000 hours at 120° C., where the magnet does not recover when remagnetized. And the loss of magnetization is a comparison to the initial magnetic flux.
Furthermore, the inventors of the present invention developed a suitable RFeBHx powder, or precursory anisotropic magnet powder, for manufacturing of such an anisotropic magnet powder. The precursory anisotropic magnet powder is the RFeB hydride (RFeBHx) powder which is mainly composed of rare earth elements including yttrium (Y), boron (B) and iron (Fe) and is characterized by an average crystal radius ranging from 0.1-1.0 &mgr;m.
The use of the RFeBHx powder, or precursory anisotropic magnet powder, makes it easier to manufacture, for example, the anisotropic magnet powder stated above.
The reasons that the range of 0.1-1.0 &mgr;m was chosen as the average crystal radius is the difficulty to manufacture RFeBHx powder whose average crystal radius is less than 0.1 &mgr;m, and the poor coercivity o
Hamada Norihiko
Mishima Chisato
LandOfFree
Manufacturing method of an anisotropic magnet powder,... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Manufacturing method of an anisotropic magnet powder,..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Manufacturing method of an anisotropic magnet powder,... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3248535