ABSTRACT:
BACKGROUND OF THE INVENTION
Nacreous pigments produce pearl-like, metallic, and iridescent effects. A widely used type comprises muscovite mica platelets coated with a metallic oxide, such as titanium dioxide. A relatively thin titanium dioxide coating produces a pearl-like or silvery luster. Mica platelets with thicker coatings produce color, even though the components are colorless, through the phenomenon of light interference. This type of coated platelets is known as an interference pigment. The color, called the reflection color, is seen most effectively by specular or mirror-like reflection, where the angle of reflection equals the angle of incidence. The reflection color is a function of optical thickness, i.e. the geometrical thickness times the refractive index, of the coating. Optical thickness of about 80 nm to about 140 nm produce reflections which may be called white, silvery or pearly while optical thickness of about 190 nm or more produces color reflections.
The pearlescent pigments which are most frequently encountered on a commercial basis are titanium dioxide-coated mica and iron oxide-coated mica pearlescent pigments. It is also well known that the metal oxide layer can be overcoated to achieve various desired effects. For instance, Linton, U.S. Pat. No. 3,087,828, describes mica coated with various oxides including those of titanium, iron, cobalt and chromium over which, if desired, a layer of calcined titanium dioxide can be positioned. Brand, U.S. Pat. No. 3,711,308, describes mica coated with a first layer which is a mixture of oxides of titanium and one or more metal oxides which can be, for instance, the oxides of iron, chromium and/or cobalt and a second layer of titanium dioxide. Franz, U.S. Pat. No. 4,744,832, describes coating mica with a layer of titanium dioxide and calcining to form two layers, an inner titanium dioxide layer and an outer pseudobrookite layer. A second layer of iron oxide is deposited and the pigment is recalcined.
Producing pearlescent interference pigments having black absorption colors which are high quality lustrous products has proven to be difficult. To obtain such products, use of chemical vapor deposition techniques is described, for instance, in European Patents 0579091 and 0571836. Techniques are known which use carbon black or titanium reduction as described, for instance, in U.S. Pat. Nos. 5,356,471 and 5,286,291. Unfortunately, these approaches have proven to be costly and/or impractical. Vapor deposition procedures are expensive and can have difficulty in producing the desired pigments in mass quantities required by the market. In addition, many pigments prepared in this manner need to be reheated at higher temperatures after initial production in order to achieve the desired result. Carbon black procedures are not very efficient since the majority of the pigment platelets being treated are not coated properly. The reduction techniques are very costly.
It is accordingly the object of the present invention to provide a new technique for producing lustrous, interference pigments having a black absorption color which overcomes difficulties encountered in the prior techniques and to provide high quality, lustrous, interference pigments having the black absorption color.
SUMMARY OF THE INVENTION
The present invention relates to lustrous pearlescent interference pigments having black absorption color and to a process for the production of such pigments. More particularly, the pigment is a mica substrate coated with a calcined layer containing a mixture of the oxides of titanium, iron and at least one of cobalt and chromium and a second calcined layer containing an oxide of titanium or iron or both. The product is achieved by coating a mica substrate with hydrous titanium, iron and cobalt and/or chromium oxides, calcining the coated mica, coating the calcined mica with hydrous oxides of titanium and/or iron and then calcining the resulting product.
The process of the invention has the advantage of employing well known deposition technology while taking advantage of the interaction of particular metal oxides to develop black interference colors. Special equipment is not required and the product can be made in very large quantities and employed in the usual industrial, automotive and cosmetic markets in which pearlescent pigments have been employed heretofore.
REFERENCES:
patent: 3087828 (1963-04-01), Linton
patent: 3087829 (1963-04-01), Linton
patent: 3711308 (1973-01-01), Brand et al.
patent: 3926659 (1975-12-01), Bernhard et al.
patent: 4456486 (1984-06-01), Bernhard
patent: 4744832 (1988-05-01), Franz et al.
patent: 5286291 (1994-02-01), Bernhardt et al.
patent: 5356471 (1994-10-01), Reynders
patent: 5626661 (1997-05-01), Schmid et al.
patent: 0278633 (1988-08-01), None
patent: 278633 (1988-08-01), None
patent: 0571836 (1993-12-01), None
patent: 571836 (1993-12-01), None
patent: 0571836 (1993-12-01), None
patent: 0579091 (1994-01-01), None
patent: 579091 (1994-01-01), None
patent: 0579091 (1994-01-01), None
patent: 974874 (1964-11-01), None
patent: 93/12182 (1993-06-01), None
patent: WO 93/12182 (1993-06-01), None
DeLuca, Jr. Carmine Vincent
Kurtenbach William P.
Mans Christine
Engelhard Corporation
Koslow C. Melissa
Ostrolenk Faber Gerb & Soffen
LandOfFree
Lustrous interference pigments with black absorption color does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Lustrous interference pigments with black absorption color, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Lustrous interference pigments with black absorption color will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2857257