ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
Zinc sulfide is a durable material which is intrinsically transparent to relatively long electromagnetic wavelengths in the far-infrared region. These properties contribute to its use in applications which require infrared transmission capability such as in infrared detectors and missile domes. Such zinc sulfide articles are typically produced by chemical vapor deposition (CVD) or hot pressing techniques. These techniques result in forms which are generally opaque and not functionally transparent in the visible or near-infrared regions of the electromagnetic spectrum. Hot-isostatic pressing (HIP) has been found to sufficiently improve the transparency of zinc sulfide articles in the visible and near-ultraviolet regions that these forms can be used in applications requiring multi-spectral capability, such as in tank and aircraft windows. However, difficulties in the final shaping/machining of these windows have compromised the capability of providing them in the precisely contoured shapes required for some applications, such as for some optical components. These difficulties have been particularly pronounced with attempts to fabricate relatively large articles. This invention relates to improvements in the CVD-Hipping process which have facilitated the consistent fabrication of precisely shaped, low stress, water-clear zinc sulfide articles.
2. Description of Related Art
Chemical vapor deposition has been used to produce zinc sulfide in bulk form or in the form of a layered coating on a substrate. Typically such production involves the reaction of H
2
S with vaporized zinc in proximity to either a substrate or a mandrel box on which the zinc sulfide deposits, such as is described in U.S. Pat. No. 5,686,195. The zinc sulfide deposits produced by this CVD method generally exhibit many inclusions and poor transmission in the visible and near-infrared regions of the electromagnetic spectrum. As described in U.S. Pat. No. 4,944,900, the transmission properties in these regions can be substantially improved by hot isostatic pressing (HIP) of the form produced by CVD.
A moderately clear ZnS has been commercially produced by a two-step process. First, elemental zinc vapors are reacted with hydrogen sulfide at a H
2
S/Zn molar ratio of 1, a mandrel (substrate) temperature of 735° C. and an absolute pressure of 35 torr, in a CVD reactor. Zinc sulfide is deposited on the mandrel until a deposit of the desired thickness is produced. The deposit is separated from the mandrel to provide a zinc sulfide form which is then HIP treated for up to 100 hours at 900-1000° C. and pressures of 15,000-30,000 psi. A recent application, Ser. No. 09/018,969 filed Feb. 5, 1998, describes an improvement of this process which reduced the number of visible inclusions present in the deposited form and provided a corresponding improved clarity of images viewed through articles prepared from these forms. The improved clarity of the product, referred to as water-clear zinc sulfide, has resulted in an expanded range of applications including some which require physical shaping/grinding to very precise final contours. Customers, however, have complained of difficulty accurately machining windows from 15-20 inch forms of water-clear zinc sulfide to a specification which required a figure of less than one tenth of a wave RMS (root mean square) at a wavelength of 632.8 nm. Exceeding this specification resulted in product windows which demonstrated unacceptable distortion of the transmitted images.
It was suspected the machining difficulties were related to a high level of stress birefringence, in the range of 80-240 nm/cm., which was measured in large water-clear zinc sulfide forms. These high stress birefringence values were generally measured near the edges of the forms, while relatively low values were measured near the forms' centers. Since considerable machining of the as deposited silicon carbide form, to reduce both its thickness and its edges, is required to result in the desired window shape, it was suspected such machining was responsible for the high stress birefringence values. Careful control of the machining and etching process provided a limited reduction of the total stress birefringence measured in forms; however, the stress birefringence per unit of window thickness was not appreciably reduced. A further attempt to reduce the stress values involved repeating the HIP treatment and controlling the cool down to less than 31° C. per hour. The second HIP treatment reduced the stress birefringence at the edges from a value in excess of 100 nm/cm to about 70 nm/cm. While this second HIP treatment demonstrated a reduction in the stress value, it was not sufficient to provide the required machinability. Providing a series of HIP treatments to achieve a satisfactory level of stress birefringence was not considered an economically viable approach, since each HIP treatment requires heat soaking the form at high temperature and high pressure for up to 100 hours in a fairly large, high temperature rated, pressure vessel.
Accordingly, there is a need for forms of machinable, low stress, water-clear zinc sulfide, particularly relatively large forms, i.e. those having thicknesses greater than {fraction (
1
/
2
)}inch and/or a maximum face dimension (length and/or width) greater than 10 inches. There is also a corresponding need for a process capable of consistently producing such low stress, water-clear zinc sulfide forms.
SUMMARY OF THE INVENTION
The invention is an improvement of the process of producing water-clear zinc sulfide by chemical vapor deposition and hot isostatic pressing which permits the production of low stress, water-clear forms which are capable of being formed/machined into precision windows and other optical articles. The invention also embraces the low stress, water-clear zinc forms/articles enabled by the improved process.
The improved process involves chemical vapor deposition of zinc sulfide, produced by the reaction of hydrogen sulfide with zinc vapor, on a substrate and the subsequent removal of the zinc sulfide deposited form from the substrate. The form is then subjected to high temperature and high isostatic pressure (Hipping) for an extended period of time. At the conclusion of the high temperature treatment, the form is allowed to cool to room temperature under controlled conditions which maintain a cooling rate of less than 50° C. per hour or, preferably, less than 31° C. Pressure is maintained on the cooling form at least until the temperature is reduced to 500° C.
The improved low stress, water-clear zinc sulfide forms/articles produced by this process are characterized by stress birefringence values no greater than 40 nm/cm, and, preferably no greater than 20 nm/cm.
REFERENCES:
patent: 4944900 (1990-07-01), Willingham et al.
patent: 4978577 (1990-12-01), Purohit et al.
patent: 5077092 (1991-12-01), Smith et al.
patent: 5686195 (1997-11-01), Taylor et al.
patent: 6083561 (2000-08-01), Goela et al.
patent: 6111689 (2000-08-01), Shibata
U.S. Patent application Ser. No. 09/018,969, filed Feb. 5, 1998 by Goela, Jitendra et al. (copy not included—previously of record with U.S. Patent and Trademark Office).
CVD Inc.
Jones Deborah
Piskorski John J.
Savage Jason
White Gerald K.
LandOfFree
Low stress, water-clear zinc sulfide does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Low stress, water-clear zinc sulfide, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Low stress, water-clear zinc sulfide will most certainly appreciate the feedback.