Chemistry: electrical current producing apparatus – product – and – Current producing cell – elements – subcombinations and... – Electrode
Reexamination Certificate
2000-07-03
2002-07-02
Ryan, Patrick (Department: 1745)
Chemistry: electrical current producing apparatus, product, and
Current producing cell, elements, subcombinations and...
Electrode
C429S218100
Reexamination Certificate
active
06413673
ABSTRACT:
BACKGROUND OF THE INVENTION
The present invention relates to an active material for a lithium secondary battery using a non-aqueous electrolyte, and to a lithium ion secondary battery which uses that material.
In accordance with future development of our information society, wider use of personal computers, portable telephones, and the like can be anticipated. Accordingly, batteries, which provide the source of electric power for these portable devices, are required to have a higher energy density and a larger capacity.
Because the lithium secondary battery using a non-aqueous electrolyte has a high battery voltage and a high energy density, its development has been widely carried out. Some lithium secondary batteries are already in practical use. However, a manganese spinel material, which is used as a material for the positive electrode of the battery, has several problems in practical use.
The first problem is deterioration of the cycle life. The capacity of a spinel type oxide is decreased significantly after repeated charge-discharge operations, because trivalent manganese ion in the oxide has the Jahn-Teller instability. The second problem is one of elusion, that is, manganese tends to dissolve into the electrolyte, whereby the performance of the battery is deteriorated. The third problem is safety, that is, the positive electrode generates heat or fire when a short circuit or rupture of the battery occurs.
All of these problems can be solved by increasing the structural stability of the active material of the positive electrode. In accordance with conventional positive materials, these problems could not be solved. However, some trials have been reported.
In accordance with JP-A-6-187933 (1994) by Technology Finance Co., improvement of the cycle life and prevention of elusion are promoted by using a spinel type oxide Li
1+x
M
z
Mn
2−x−z
O
4
(0≦x<0.33), wherein a composition ratio of Li to Mn, is varied, as the active material. The same advantage is expected by replacing Mn with Co. However, in accordance with this method, a problem occurs in that the initial capacity itself is decreased .
In accordance with a Laid-open patent (JP-B-9-147867 (1997)) of Mori Energy Co., improvement of the cycle life characteristics is promoted by using a spinel type oxide Li
1+x
M
z
Mn
2−x−z
O
4
(0≦x<0.33, M: transition metallic element such as Co, Cr, and the like), wherein a composition ratio of Li to Mn is increased and Mn is replaced with a transition metal such as Co, Cr, and the like, as the active material. However, a cycle life of more than 1000 cycles, which is. required for practical use, can not be obtained with the proposed battery.
As described above, efforts to achieve extension of the battery life, prevention of elusion, and improvement of its safety have been tried conventionally with a stabilizing crystal structure of the material for the positive electrode by various methods. However, if extension of the battery life is achieved, the battery capacity is decreased. On the contrary, if an increase in the battery capacity is achieved, a problem in safety is generated, and heating or ignition results if a short circuit occurs.
SUMMARY OF THE INVENTION
One of the objects of the present invention is to provide a spinel type oxide active material for a positive electrode of a secondary battery and a method of manufacture thereof for providing a long life, safe, and large capacity battery.
In order to achieve the foregoing object of the present invention, an oxide having a spinel type structure defined by the chemical formula of Li
1+x
Mn
2−x
O
4
(0≦x<0.33), which is further supplemented with at least an element other than Li, Mn, and oxygen, is used as the positive electrode material. The composition ratio of Li to Mn is called hereinafter the Li/Mn molar ratio. Increasing the Li/Mn ratio operates to decrease the lattice constant, and accordingly, the crystal structure is stabilized. The stabilization of the crystal structure operates to improve the cycle characteristics and to prevent elusion, and brings about an advantage in that the battery life characteristics are improved. However, increasing the Li/Mn ratio brings about a lowering of the theoretical capacity, and so a lowering of the initial capacity can not be avoided in practice. Practically, the capacity of the battery is defined by the capacity of the positive electrode material. Therefore, lowering the capacity of the positive electrode material is not desirable.
In accordance with the present invention, the material, which is an oxide having a spinel type structure defined by a chemical formula of Li
1+x
Mn
2−x
O
4
(0≦x<0.33), which is further supplemented with at least an element other than Li, Mn, and oxygen, is used as the positive electrode material. The element to be added is preferably at least any one selected from the group consisting of B, P, Mg, As, Sb, Zr, Na, Be, Y, Si, Al, C, F, Bi, Pb, Ge, and Sn. The amount of the added element is preferably in the range of 0.01%-10% in molar ratio to the total amount of Mn contained in the positive electrode material. However, no problem is caused when adding an amount more than or less than the above range.
In particular, the addition of B, P, and Sb does not change its crystal structure, that is, its stability is maintained, and so an increase in its capacity can be achieved without harming its life characteristics. With a view toward increased safety, the addition of Al, Si, Ga, and mg is effective. As the composition ratio for the material to be added, the range, 0.02<x<0.14, in the chemical formula Li
1+x
Mn
2−x
O
4
is most preferable.
The method of manufacturing the positive electrode material in accordance with the present invention comprises the following Steps: First, a manganese spinel type oxide to be a parent material is manufactured. Li
2
CO
3
, LiOH, LiNO
3
, LiCOOH, Li
2
O, and the like are used as a lithium raw material, and MnO
2
(either of electrolytic manganese dioxide (EMD) and chemically purified manganese dioxide (CMD) can be used), Mn
3
O
4
, Mn
2
O
3
, MnO, MnCO
2
, MnCOOH, MnOOH, and the like are used as a manganese raw material.
A mixture of these raw materials in a designated composition ratio, or a mixed powder obtained by mixing a solution, co-precipitation, and drying, is used as a raw material. The raw material is calcined in air or in an oxygen atmosphere for 40 hours. The temperature at the calcination depends on the composition ratio, but generally a range of approximately 600° C.-900° C. is desirable. A designated amount of the additive is added to the parent material obtained by the calcination, and a heat treatment follows. The temperature of the heat treatment is desirably in the range of 400° C.-900° C. Of course, the advantage of the additive can be observed even if the heat treatment is not performed, but the heat treatment is desirable.
Furthermore, in order to solve the problem, the following active material for the positive electrode is used. The active material can be obtained by adding at least an element other than Li, Mn, and oxygen to an oxide having a spinel type structure defined by the chemical formula of Li
1+x
M
y
Mn
2−x−z
O
4
(0≦x<0.33, 0<y<2, M: at least a transition metal other than Mn). The element to be added is desirably at least any one selected from the group consisting of B, P, Mg, As, Sb, Zr, Na, Be, Y, Si, Al, C, F, Bi, Pb, Ge, and Sn.
Furthermore, in order to solve the problem, the following active material for a secondary battery and a lithium secondary battery using the same are provided. The active material is an oxide having a spinel type structure defined by a chemical formula of Li
1+x
M
y
Mn
2−x−y−z
B
z
O
4
(0≦x<0.33, 0<y+z<2, M: at least a transition metal other than Mn), and the B substituting Mn is at least an element other than Li, Mn, oxygen, and the transition metal M. The B is desirably a transition metal other than
Douzono Toshinori
Kasai Masahiro
Antonelli Terry Stout & Kraus LLP
Hitachi , Ltd.
Ryan Patrick
Wills M.
LandOfFree
Lithium menganes oxide secondary battery does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Lithium menganes oxide secondary battery, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Lithium menganes oxide secondary battery will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2861650