DESCRIPTION:
BRIEF SUMMARY
TECHNICAL FIELD OF INVENTION
The present invention relates broadly to novel anisotropic liquid-crystalline extended chain polymerpolyphosphoric acid compositions, to the production of high molecular weight extended chain polymers by polycondensation of selected monomers in certain polyphosphoric acids, and especially to the production of highly concentrated polymer compositions from which industrially useful polymeric articles such as fibers and films are readily produced.
Among some of the most serious difficulties encountered in the production of thermally stable articles such as fibers and films from extended chain polymers are described in the Background Art below.
BACKGROUND OF INVENTION
1. Reference to Related Applications
Reference is made to another United States patent application filed concurrently with the present application, both being assigned to SRI International and having as one of their inventors, James F. Wolfe. Said other application is entitled: "Liquid Crystalline Poly(2,6-benzothiazole) Compositions, Process, and Products" and is herein incorporated by reference.
2. Background Art
In general, the class of aromatic heterocyclic extended chain polymers are well known for their outstanding thermal, physical, and chemical properties. Unfortunately, these polymers are essentially non-melting and have proven very difficult to economically process into articles. In order to fashion such polymers into desired articles of commerce, for example fibers, films, fibrids, and the like, it is necessary that they be in solution or dope form. Although such polymers can be dissolved in various acidic solvents, such as sulfuric acid, methanesulfonic acid, chlorosulfonic acid, polyphosphoric acid, and the like, difficulty is often experienced in preparing and using the polymer-acid compositions or dopes because of poor polymer-acid solubility.
Normally, a precipitated or dried particulate form of the polymer is dissolved in a strong acidic solvent by mixing the (isolated) polymer particles at elevated temperatures and/or under high pressures for a period from several hours to several days. If the polymer is insoluble in the particular solvent, other solvents or various solvent mixtures are employed. Usually, heating and cooling cycles are applied and repeated to obtain a useful dope.
The resulting dopes often contain undissolved polymer and must be filtered before further processing into articles.
Although spinning dopes of polybenzobisoxazole, polybenzimidazole and polybenzobisthiazole in sulfuric acid and/or methanesulfonic acid and/or chlorosulfonic acid with polymer concentrations above about 10 percent are known in the art, the intrinsic viscosity of these polymers is for the most part below 5dL/g and oftentimes less than 3dL/g. The cohesive strength of such dopes is inherently weak and economically less desirable for use in dry-jet wet spinning. In the case of polybenzobisoxazole, numerous attempts of dry-jet wet spinning an approximately 10% polybenzobisoxazole/methane sulfonic acid-dope into fibers were not successful (E. W. Choe, et al., in Macromolecules 1981, 14, pp. 920-924).
In the case of polybenzimidazole, prior art dopes of this polymer lack adequate strength to maintain filament integrity while dropping through the air-gap. In order to overcome this problem U.S. Pat. No. 4,263,245 teaches dissolving a high concentration (up to 30%) of this polymer into suitable solvents such as concentrated sulfuric acid. At such high polymer concentrations lithium chloride is required to prevent the polybenzimidazole from phasing out of solution.
In the case of polybenzobisthiazole, U.S. Pat. No. 4,225,700 teaches the formation of a liquid crystalline composition of this polymer at concentrations near 10% in methane sulfonic acid and chlorosulfonic acid and at about 6% in polyphosphoric acid. Concentrations of polybenzobisthiazole in polyphosphoric acid above about 10% by weight are difficult, if indeed possible to achieve. One difficulty encountered is that the solution of the 2,5-diamino-1,4-benz
REFERENCES:
patent: 2904537 (1959-09-01), Brinker et al.
patent: 3286992 (1966-11-01), Armeniades et al.
patent: 3424720 (1969-01-01), Rudner et al.
patent: 3620999 (1971-11-01), Marvel
patent: 3632414 (1972-01-01), Arnold et al.
patent: 3642696 (1972-02-01), Rabilloud et al.
patent: 3644288 (1972-02-01), Odier et al.
patent: 3661849 (1972-05-01), Culbertson
patent: 3681297 (1972-08-01), D'Alelio
patent: 3691136 (1972-09-01), Serres, Jr. et al.
patent: 3800985 (1974-04-01), Grout et al.
patent: 3804791 (1974-04-01), Morgan
patent: 3836500 (1974-09-01), Calundann et al.
patent: 3864310 (1975-02-01), Saferstein
patent: 3873497 (1975-03-01), Jackson
patent: 4051108 (1977-09-01), Helminiak et al.
patent: 4054633 (1977-10-01), Richardson
patent: 4108835 (1978-08-01), Arnold et al.
patent: 4131748 (1978-12-01), Arnold et al.
patent: 4207407 (1980-06-01), Helminiak et al.
patent: 4225700 (1980-09-01), Wolfe et al.
patent: 4229566 (1980-10-01), Helminiak et al.
patent: 4233434 (1980-11-01), Kraus et al.
patent: 4263245 (1981-04-01), Tan
patent: 4312976 (1982-01-01), Choe
patent: 4342862 (1982-08-01), Jackson, Jr. et al.
patent: 4351917 (1982-09-01), Caludann et al.
patent: 4351918 (1982-09-01), Charbonneau et al.
patent: 4355132 (1982-10-01), East et al.
patent: 4359567 (1982-11-01), Evers
patent: 4377546 (1983-03-01), Helminiak et al.
patent: 4423202 (1983-12-01), Choe
Synthesis and Thermal Properties of Para-Aromatic Polymers with 2,6,Benzobisoxazole Units-Macromolecules, 14, 909 (1981) by Wolfe.
Macromolecules, 14, 925 (1981) by Robert C. Evers et al.
Macromolecules, 14, 915 (1981) by Wolfe et al.
Am. Chem. Soc. Polymer Preprints, 23, 3 (1982)-Sybert et al.
Am. Chem. Soc. Polymer Preprints, 23, 2 (1982) Wolfe.
FY80, AFOSR-TR-81-0448, p. 217 (Mar. '81) Wolfe.
"Mechanical Properties vs. Morphology of Ordered Polymers", vol. II, Report 1, Sep. '79-30 Aug. '80, AFWAL-TR-80-4045 (Jul. 1981) Thomas et al.
Processing of Rodlike Polymers, Final Report Jun. '79-Jul. '80, AFWAL-TR-80-4142 (Oct. '80) Chenevy et al.
Final Report Mar. '80-Feb. 81, AFWAL-TR-81-4092 (Oct. '81)-Berry.
"Synthesis of Pararordered Aromatic Polymers", Interim Report Feb. '77-Feb. '78, AFML-TR-78-32 (Apr. 1978) Wolfe.
Polybenzazoles, Makromol. Chem., 83, 179 (1965) Imai et al.
Polyphenylenebenzimidazoles-Polymer Sci. A, 2, 2605 (1964) Iwakura et al.
Thermally Stable Polymers Derived from 2,3,5,6-Tetraaminopyridine, 11, 1703, (1973) Gerber.
J. Polymer Sci. A-1, 6, 1777 (1968) Deusen et al.
J. Polymer Sci. A-1, 6, 2939 (1968) Hergenrother et al.
J. Polymer Sci., 1, 511 (1961), Vogel et al, A. 1, 1531 (1963), Vogel et al.
II, J. Polymer Sci., Polymer Chem. Ed., 17, 163 (1979), Varma et al.
J. Polymer Sci., Polymer Symp., 65, 173 (1978) Wong.
J. of Polymer Science: Part A, vol. 2, pp. 2559-2569 (1964) Plummer et al.
Tech. Report, 15 May 1965-15 Jul. 1966, NTIS No. AD-815-332/7ST (Dec. 1966) Mecum et al.
Mechanical Properties vs. Morphology of Ordered Polymers, 1 Sep. 1978-30 Aug. 1979, Thomas.
Schubert, M., Liebigs Ann. Chem., 1947, 558, 29.
Macromolecules, 14, 1135 (1981) Allen et al.
Macromolecules, 14, 930 (1981) Berry et al.
AFWAL-TR-80-4099 (Aug. 1980) Berry et al.
AFWAL-TR-80-4142 (Jul. 1980), Chenevey.
AFWAL-TR-80-4142 (Oct. 1981) Chenevey.
AFWAL-TR-80-4142 (Dec. 1982) Chenevey.
Macromolecules, 14, 920 (Aug. 1981) Choe et al.
Macromolecules, vol. 14, 4, 925 (1981), Evers et al.
Polymer Preprint, 21(1) 88 (1980), Evers et al.
Pol
Sybert Joanne R.
Sybert Paul D.
Wolfe James F.
Chen John Y.
Michl Paul R.
Sarofim N.
SRI - International
LandOfFree
Liquid crystalline polymer compositions, process, and products does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Liquid crystalline polymer compositions, process, and products, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Liquid crystalline polymer compositions, process, and products will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-513161