Active solid-state devices (e.g. – transistors – solid-state diode – Non-single crystal – or recrystallized – semiconductor... – Amorphous semiconductor material
Reexamination Certificate
2002-12-30
2004-06-22
Nelms, David (Department: 2818)
Active solid-state devices (e.g., transistors, solid-state diode
Non-single crystal, or recrystallized, semiconductor...
Amorphous semiconductor material
C257S058000, C257S314000, C257S316000, C257S318000, C257S350000, C257S354000, C257S365000, C438S101000, C438S166000
Reexamination Certificate
active
06753550
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Technical Field
The present invention relates to a thin film transistor used for an active matrix liquid crystal display, a liquid crystal display device using the thin film transistor, and a method of fabricating the thin film transistor.
2. Prior Art
A liquid display device employing an active matrix system, which uses a thin film transistor, comprises a TFT array substrate in which gate electrodes (Y-electrode) and data electrodes (X-electrode) are arranged in the form of a matrix and thin film transistors (TFT) are disposed at intersceting points of the matrix, and an opposite substrate located so as face the TFT array substrate with a space therebetween. By the thin film transistor, the liquid display device controls a voltage applied to a liquid crystal which is sealed between the TFT array substrate and the opposite substrate, and can performs a displaying utilizing an electro-optic effect of the liquid crystal.
Here, as a structure of the thin film transistor (TFT), a top gate type (positive stagger type) thin film transistor (TET) and a bottom gate type (reverse stagger type) thin film transistor have heretofore been known. In the top gate type thin film transistor, a light shield film is formed on an insulating substrate formed of glass and the like, and an insulating film formed of silicon oxide SiO
x
, silicon nitride SiN
x
and the like is formed on the light shield film. On the insulating film, source electrode and source electrodes formed of an ITO (indium tin oxide) film are formed so as to be apart from each other by a predetermined distance. An amorphous silicon film (a-Si film) is formed so as to cover the source and drain electrodes. A gate insulating film formed of SiO
x
, SiN
x
and the like is formed on the amorphous silicon film. A gate electrode is formed on the gate insulating film. On the other hand, in the bottom gate type thin film transistor, a gate electrode is formed by patterning a metal film deposited on an insulating substrate formed of glass and the like. A gate insulating film formed of SiN
x
and the like is formed on the gate electrode. An amorphous silicon film (a-Si film) is grown on the gate insulating film by a CVD method. Thereafter, an a-Si film doped with phosohorus (n
+
) is grown in a way that phosphine (PH
3
) is continuously supplied during the growth of the film, and then patterned. Moreover, a film for source and drain electrodes is formed on the a-Si film, and patterned. Thus, the source and drain electrodes are formed.
Here, since a growth rate of the amorphous silicon (a-Si) film is as slow as 500 Å/min in forming the thin film transistor (TFT), acquisition of a sufficient TFT characteristic with an a-Si film of a thickness which is as thin as possible is effective to increase a productivity and to minimize a capital investment.
As prior arts paying attention to the length of a manufacturing time in forming such a-Si film, there exist Japanese Patent Laid-Open No. Hei 6(1994)-77483, No. Hei 7(1995)-45833, No. Hei 7(1995)-135319 and. No. Hei 8(1996)-255917. In these gazettes, an a-Si film formed of a low deposition rate film, which takes a long film growth time for growing it, is grown in combination with an a-Si film formed of a high deposition rate film, which takes a short film growth time. More specifically, in the thin film transistors (TFT) taking a bottom gate type structure and a top gate type structure, a good a-Si film (fine a-Si film/low defect-density a-Si film) formed of a low deposition rate film is grown on so-called a channel interface side (gate insulating film side), and a bad a-Si film (coarse a-Si film/high defect-density a-Si film) is grown close to the source and drain electrode side that is a contact portion. According to these films, a tact time can be reduced to half, compared to a length of a general manufacturing time at the time when the a-Si film is formed at a single low deposition rate by a chemical vapor deposition method. In addition, it is possible to prevent deterioration of the a-Si film on the channel interface side which has an effect on electric characteristics and physical and mechanical characteristic, thus preventing deterioration of characteristics of the thin film transistor (TFT).
However, according to these background arts, although the film growth time can surely be shortened, the prior arts are nothing else more than preventing the deterioration of the TFT characteristic such as an electrical characteristic, and the prior arts do not aim at increasing the TFT characteristic. In other words, the object of these prior arts is to shorten a working time for growing the film under a situation where the deterioration of the TFT characteristic is prevented, and disclose nothing than increasing no deposition rate of the a-Si film on the channel interface side in both of the bottom gate and top gate type TFTs.
As described above, it is required to obtain a sufficient TFT characteristic with an a-Si film of a thickness which is as thin as possible in fabricating the thin film transistor (TFT). On the other hand, in the top gate type TFT, when source and drain electrodes are formed by plasma doping technique, the a-Si film is grown on the SiO
x
film formed on the substrate. Accordingly, the a-Si film has a tendency to have a large defect-density due to a lattice mismatching of the a-Si film with the SiO
x
film. In order to acquire a sufficient ON characteristic of the thin film transistor (TFT), an a-Si film having a sufficiently thick thickness must be formed so that its film quality is further improved as a distance from the SiO
x
film becomes larger. In other words, as the thickness of the deposited a-Si film increases, a lower part of amorphous silicon is annealed in eventually H
2
atmosphere and the film quality is improved as the dangling bond of amorphous silicon is terminated by H
2
. (as the thickness of the deposited a-Si film increases, an influence of lattice mismatching of the amorphous silicon with the silicon oxide on an upper part of the amorphous silicon is reduced, and so-called a hydrogen annealing effect further improving the film quality of the amorphous silicon as the deposition of the amorphous silicon is progressed is exhibited, thus tending to increase an ON current.)
FIG. 6
is a graph showing a dependency of the film thickness on the ON current in the conventional TFT structure. In
FIG. 6
, the axis of abscissa shows the film thickness of the a-Si film, and the axis of ordinates shows the ON current. In the case where the a-Si film formed at a high deposition rate is particularly used, the ON current increases approximately in proportion to the film thickness in a practical use as shown in
FIG. 6
, so that a thick thickness is required for the a-Si film to obtain a sufficient ON current to drive a liquid crystal device (LCD) including the thin film transistor.
This tendency is shown in the case where a low defect-density amorphous silicon formed at a low deposition rate is used.
However, as a result of investigations by the inventors, the inventors came to recognize the existence of the fact that the ON current decreases as the film thickness of the a-Si film becomes larger. Specifically, although the ON current tends generally to increase as the film thickness of the a-Si film becomes larger, on the contrary the ON current decreases as the film thickness of the a-Si film becomes larger depending on a position of the a-Si film formed and its state. The reason is that as the film thickness of the a-Si film becomes larger, a distance between the channel interface (the upper part of the a-Si film in the case of the top gate type thin film transistor TFT) and the source/drain electrode becomes larger, thus increasing a parasitic capacitance. Furthermore, as another reason, the following reason is given. When the Debye length defined by the depth in which electric field has effect on the amorphous silicon is nearly equal to the thickness of the amorphous silicon, the current conduction is dominated by the contact cond
Morooka Mitsuo
Tokuhiro Osamu
Tsujimura Takatoshi
Nelms David
Scully Scott Murphy & Presser
Tran Mai-Huong
Trepp, Esq. Robert M.
LandOfFree
Liquid crystal display device having a thin film transistor... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Liquid crystal display device having a thin film transistor..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Liquid crystal display device having a thin film transistor... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3357939