ABSTRACT:
CROSS REFERENCE TO RELATED APPLICATION
The present application claims priority to Hungarian Patent Application 0205406, filed Feb. 7, 2002.
BACKGROUND OF THE INVENTION
1. Field of the Invention
The invention relates to a lightweight concrete composition containing foamed plastic balls or particles obtained by grinding foamed plastic waste material. The invention also relates to a method for the production of lightweight concrete composition wherein foamed plastic balls or particles obtained by grinding foamed plastic waste material are mixed with cement.
2. Description of the Related Art
The Hungarian Patent No. 181180 prepares polystyrofoam (PSF) concrete by using polystyrofoam beads mounting up to 60-70% of the volume of crude concrete. The polystyrofoam beads are mixed with water or with the water content of the sand, and then the mix is compacted (by vibrating press) after being poured into formwork. The concrete produced in this way—as a consequence of volumetric proportions—has the disadvantage of high gravimetric density, and, as a consequence, reduced heat-insulating capacity. At the same time, the bond of concrete and PSF in not ensured. (Generally lightweight concrete not reaching the value of 350-400 kg/m3 cannot be vibrated).
The process in Patent No. 213905 B applies soda soluble glass (15-18 l/m3) to treat PSF—to increase bonding—and, in this manner, manufactures building-block elements, and different materials for construction industry application.
The process in Hungarian Patent No. 174868 provides for bonding of PSF and cement by adding aluminum hydro-silicate to the mix, and, thus renders it thixotrope. The prepared mix is worked in a mold or framework. This process does not activate the surface of the PSF aggregate, but pulps the cement (using bentonite) to create better bonding.
The U.S. Pat. No. 5,639,297 aims for an increase in strength of PSF concrete in such a way that heat treats the PSF granules before being added, so that it shrinks them and hardens their surface. The disadvantage of the process is the fact that the increase of strength requires significant expenditure of energy, which involves cost increment.
These processes offer solutions to two problem ranges: on the one hand, to enhance problematic bonding capacity of PSF and cement slurry, and, on the other hand, to increase the strength of lightweight concrete. The goal is only reached by deteriorating advantageous properties (181180) or by significant cost increment (5,639,297), and the compositions prepared with the applied bonding additives, in many of the cases, do not meet the required or necessary strength values, and, consequently, have limited application.
SUMMARY OF THE INVENTION
The main objective of the present invention is to provide a lightweight concrete composition that preserves the advantageous properties (good heat-insulating capacity, low gravimetric density, good water vapor permeation capability, etc.) of the conventional lightweight—primarily polystyrofoam—concrete. Nevertheless, by virtue of its increased strength, it can be used in even more complex situations and in a wider range of application fields of the construction industry than conventional concrete.
The basic idea of this invention is to add a polymer dispersion to lightweight concrete composition because, with this, the properties of lightweight concrete, in fresh and also in solid state (after having set and hardened), improve considerably. The appropriate polymer dispersion also improves the homogeneity, stability and workability of the mix.
By dosing the polymer dispersion properly, a further bond system is introduced in the mix, which also modifies the water relations of the composition: while the cement is setting during water absorption, the polymer dispersion hardens when the water has left (drying). Therefore, during the application of the process it must be taken into consideration that the state when the load can be applied sets in later—in fact, after drying.
Simultaneously, as a new effect, the dispersed polymer particles also tie the components of the mix with adhesive bonding.
The invention is based on the additional idea that, after having improved the plasticity and compactibility of lightweight concrete with the above stated process, the prepared mix is to a large extent compressible. This increases further the strength improved by adhesive bonding.
The invention is also based on the idea that any profiled shape can be sawn out of the increased strength lightweight concrete block by moving an endless coarse steel wire in longitudinal and transverse direction.
The method of this invention enables the forming of more favorable and up-to-date lightweight concrete form blocks for concrete-filled masonry than the currently used ones. The currently produced form blocks have grooves at their edges, and, thus, the narrowed edges easily damage whilst transported and assembled. The form blocks butt with their plane surface so they can shift along this surface when the concrete is poured. Usually, manufacturing such form blocks requires expensive press dies, and, consequently, the blocks have a minimal size choice. The dimension of the houses constructed with them is limited by the form block types.
The basis of the invention is constituted by the perception that, in case we create increased strength lightweight concrete masonry to fill with concrete by sawing the form blocks, we can choose the block dimensions at discretion, prevent block movement by tongue-and-groove joint, and create the cavity inside the blocks. Then these blocks permit freer dimensioning, reduced risk of damage and more secure concrete filling. Due to the applied technology, the cavities do not need to be formed centrally. Therefore, the constructed masonry can have a thicker and more efficient heat-insulating layer on its exterior.
Various optional or preferred features are set out in the detailed description forming part of this specification.
REFERENCES:
patent: 5639297 (1997-06-01), Stracke et al.
patent: 5737896 (1998-04-01), Rodgers
patent: 5974762 (1999-11-01), Rodgers
patent: 6290769 (2001-09-01), Carkner
“Perform Wall Panel System,”Internet, Copyright© 2001 by Perform Wall, LLC, http://www.performwall.com/disc.htm.
“Guild Members Use Rastra,” EcoBuilding Times, vol. 6.2,Internet, Copyright© 2001 by Northwest EcoBuilding Guild, Http://www.ecobuilding.org/lib/ebt/2000/userasta.htm.
Timmons, “Alternative Building System Saves Energy,” EDC,Internet, Feb. 22, 2001, http://www.edcmag.com/CDA/ArticleInformation/features/BNP.
“Rastra, The Environmentally Friendly Solution,”Internet, Copyright © 1999 by Rastra Found, Liechtenstein, http://www.rastra.com/wi_ra.htm.
Klarquist & Sparkman, LLP
Wood Elizabeth D.
LandOfFree
Lightweight concrete with increased strength and method for... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Lightweight concrete with increased strength and method for..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Lightweight concrete with increased strength and method for... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3357045