ABSTRACT:
FIELD OF THE INVENTION
The present invention relates to laser welding, more particularly, welding with an oscillating laser beam to create a moving and refilling keyhole.
BACKGROUND OF THE INVENTION
Common welded joints include butt joints, lap-penetration joints, and lap-fillet joints. Laser welding is a method of joining metal components using a focused beam of coherent light to melt adjoining components and allowing the melt to solidify into a joint. While butt joints may be produced by laser welding, they are not always suitable in the aerospace, automotive, and marine industries. Laser welding of lap-penetration joints and lap-fillet joints is more difficult to accomplish.
FIGS. 1 and 2
depict the result of laser welding of a lap-penetration joint in which a laser beam is directed at the region of an interface
2
between components
4
and
6
. Relative movement is effected along the interface
2
between the laser beam and the assembly of components. The laser beam may cause a portion of metal in the interface to volatilize to produce a keyhole
8
bounded by molten metal
10
. The keyhole
8
advances with the movement of the laser beam in the direction of the arrow A. Molten metal
10
solidifies behind the advancing keyhole
8
to create a joint between the components.
In practice, production of lap-penetration joints and lap-fillet joints via laser welding is limited. For example, in a lap-penetration joint as shown in
FIGS. 1 and 2
, it is well established that the width W of the weld should be equal to or exceed the thickness t of the thinnest of the components being joined. The welding process must be controlled to minimize formation of voids in the welds that are caused by instabilities in the keyhole and/or volatilization of low melting constituents with high partial pressures (e.g., Mg). In addition, laser welding is relatively costly. The laser beam is generally operated at or above 10
6
W/cm
2
; efficiency dictates a need to weld at rates of at least 80 inches per minute (ipm) at this power level. When welding components up to 0.1 inch thick, it is possible to produce the required 0.1 inch weld width W at speeds exceeding 120 ipm. The formation of voids can be adequately controlled by use of defocused beams or bifocal optical systems. However, with thicker materials it is progressively more difficult to achieve the required weld width while still maintaining acceptable weld quality and speeds of travel.
When laser welding lap-fillet joints, the welding system must accommodate variations in lateral placement of the laser beam relative to the joint edge and gaps between the components to attain performance comparable to deposits made with gas metal arc welding (GMAW) at rates that justify using costlier laser welding systems.
One option for overcoming the challenges in laser welding lap-penetration and lap-fillet joints is to use beam integrators, focusing optics (mirrors or lenses) with longer focal length or defocused beams. However, to ensure reliable and consistent optical coupling between the laser and components to be joined and to achieve localized melting at the joint, the power output of the laser system must be increased to compensate for the reduction in power density. With sufficient power output, widened welds can be produced in the more placid conduction mode rather than the keyhole mode. Unlike the latter mode, which involves translation of a cavity (or keyhole) along the joining area, the conduction mode is achieved by translating a molten pool of metal along the joining area. By minimizing the violent volatilization of metal within the keyhole, the more placid conduction mode can eliminate the instabilities inherent with the keyhole mode. As a result, the conduction mode minimizes the formation of voids in the laser welds. However, to implement this approach necessitates using very powerful lasers (e.g. 18 KW to 25 KW, depending on the application) and costly laser generating systems, which makes the approach impractical for many industrial applications.
Another approach to increasing the effectiveness of laser welding is described in U.S. Pat. No. 4,369,348 by oscillating the laser beam at frequencies of over 1000 Hz. This very rapid movement of the laser is intended to distribute and time average the intensity of the laser at a frequency greater than the thermal response time of the metal. In this manner, the time averaged intensity of heat experienced by a particular location at the interface between the metal components being joined is greater than the intensity of heat experienced without oscillation. However, operation of a laser beam at oscillation frequencies of over 1000 Hz is difficult and costly. In addition, the only way to implement this approach is to weld in the conduction mode where a continuous molten pool is maintained.
Accordingly, a need remains for a low cost, effective method of laser welding.
SUMMARY OF THE INVENTION
This need is met by the method of the present invention which includes focusing a laser beam onto a joining region between a pair of metal components to form a continuous molten pool and establishing a keyhole therein. The molten pool is a mixture of metals from each of the components. By simultaneously translating the focused beam along the joining region in a first direction and oscillating the beam relative to the molten pool at a direction different from the first direction, the keyhole is continuously moved and immediately refilled by the adjoining molten metal. Welding takes place as the keyhole penetrates through the molten pool and melts the components being welded at the interface therebetween. In the vicinity of the focused laser beam, the molten pool is vaporized to produce a keyhole which is translated with the oscillating beam. As the beam oscillates in a direction different from the first direction (e.g. transverse to the first direction), the keyhole oscillates through the pool of molten metal and molten metal fills into the keyhole as the keyhole oscillates. In this manner, the keyhole continuously is produced and then is refilled with molten metal that solidifies to produce a weld.
The weld may be a lap-penetration weld, a butt weld, or a lap-fillet weld. Depending on the type of joint, thickness combination, and welding position, the laser beam oscillates at a frequency of about 5 to about 120 Hz and advances in the first direction at a rate of about 5 to about 400 ipm. When citing a range of frequency or dimension herein, the range includes all intermediate values, such as for the rate of the first direction, the rate would include 5, 6, 7, and on up through 400 ipm. The oscillations may be linear, circular, elliptical, or a combination thereof, or any other shape that accomplishes a moving keyhole. The thinner of the metal components may be over 0.1 inch thick. The present invention allows laser joining various types of joints with customized weld dimensions (e.g. 0.25 inch interfacial weld width between 0.25 inch thick components) up to about 0.50 inch wide.
REFERENCES:
patent: 4369348 (1983-01-01), Stetson et al.
patent: 4507540 (1985-03-01), Hamasaki
patent: 4794231 (1988-12-01), Banas et al.
patent: 4803334 (1989-02-01), Burke et al.
patent: 4857697 (1989-08-01), Melville
patent: 5591360 (1997-01-01), Mombo-Caristan
patent: 5595670 (1997-01-01), Mombo-Caristan
patent: 5603853 (1997-02-01), Mombo-Caristan
patent: 5841097 (1998-11-01), Esaka et al.
patent: 6087619 (2000-07-01), Berkmanns et al.
patent: 6410882 (2002-06-01), Okada
Martukanitz Richard P.
Stol Israel
Alcoa Inc.
Elve M. Alexandra
Meder Julie W.
LandOfFree
Laser welding with beam oscillation does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Laser welding with beam oscillation, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Laser welding with beam oscillation will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3239189