Laser segmented thick thermal barrier coatings for turbine...

Stock material or miscellaneous articles – Structurally defined web or sheet – Including variation in thickness

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C428S137000, C428S167000, C428S632000, C428S633000, C428S469000, C428S472000, C428S701000

Reexamination Certificate

active

06224963

ABSTRACT:

TECHNICAL FIELD
This invention relates to insulative and abradable ceramic coatings, and more particularly to ceramic turbine shroud coatings, and more particularly to a segmented ceramic coated turbine shroud and a method of making by laser cutting grooves through the ceramic coating in a grid pattern.
BACKGROUND OF THE INVENTION
Those skilled in the art know that the efficiency loss of a high pressure turbine increases rapidly as the blade tip-to-shroud clearance is increased, either as a result of blade tip wear resulting from contact with the turbine shroud or by design to avoid blade tip wear and abrading of the shroud. Any high pressure air that passes between the turbine blade tips and the turbine shroud does not do work and therefore is a system loss. Another loss is the use of compressor bleed air to cool the turbine shroud. If an insulative shroud technology could be provided which allows blade tip clearances to be small over the life of the turbine, there would be an increase in the overall turbine performance, including higher power output at a lower operating temperatures, better utilization of fuel, longer operating life, and reduced shroud cooling requirements.
To this end, efforts have been made in the gas turbine industry to develop abradable turbine shrouds to reduce clearance and associated leakage losses between the blade tips and the turbine shroud. Various techniques have been developed for coating turbine shrouds with ceramic materials such as, primarily, yttria stabilized zirconia. A disadvantage of these techniques is that the ceramic coating tends to spall off due to the steep thermal gradient across the thickness of the ceramic during engine operation. The spalling off severely reduces the sealing effectiveness and the insulative characteristics of the ceramic coating, causing shroud distortion, which results in a variation in the blade tip-to-shroud clearance, loss of performance, and expensive repairs.
Strangman, U.S. Pat. No. 4,914,794, entitled “Method of Making an Abradable Strain-Tolerant Ceramic coated Turbine Shroud”, which is assigned to the assignee of this application and incorporated by reference herein, provides a solution to the spalling off problem. Strangman discloses an abradable ceramic coated turbine shroud structure which includes a grid of slant-steps isolated by grooves in a superalloy metal shroud substrate. A thin bonding layer is applied to the slant-steps, followed by a stabilized zirconia layer that is plasma sprayed at a sufficiently large spray angle to cause formation of deep shadow gaps in the zirconia layer. The shadow gaps provide strain tolerance, avoiding spalling. However, the invention in Strangman requires that the substrate surface have sufficient thickness to accommodate the grooves formed therein. For thin metal turbine shrouds with a thick ceramic coating, it becomes impractical to have a deep enough groove in the metal substrate to cause adequate shadow gaps to form in the zirconia.
Schienle et al., U.S. Pat. No. 5,352,540, entitled “Strain-Tolerant Ceramic Coated Seal”, which is assigned to the assignee of this application and also incorporated by reference herein, provides a method of laser machining an array of grooves into a ceramic high temperature solid lubricant surface layer of a seal. When applied to a thin turbine shroud coated with a thick TBC layer, however, the results have not been satisfactory. Particularly with a thin substrate, the depth of the groove must be accurately controlled, so as to be deep enough to provide strain relief, but not touch the substrate. The laser machining method of Schienle does not provide the required level of control over the groove depth. Also, stabilized zirconia vapor produced by the laser machining process tends to fill in the groove behind the laser. To compensate for this back filling phenomenon, the grooves must made be excessively wide, which takes away from the sealing effectiveness of the shroud.
SUMMARY OF THE INVENTION
An object of the present invention is to provide a method for forming a segmented morphology in a thick ceramic thermal barrier coating on a thin metal turbine shroud.
Another object of the present invention is to provide a thin metal turbine shroud having a thick ceramic thermal barrier coating layer that is strain tolerant.
Yet still another object of the present invention is to provide a less expensive strain tolerant ceramic thermal barrier coating.
The present invention achieves these objects by providing a turbine shroud having a coating comprising a bond layer covering the shroud substrate, and a thick ceramic stabilized zirconia layer with a segmented morphology covering the bond coat. The segmented morphology is defined by an array of slots or grooves which extend from the outer surface of the ceramic layer inwards through almost the entire thickness of the coating but without piercing the underlying substrate. The segmented morphology comprises a plurality of grooves that are laser drilled into the ceramic layer. Each groove is formed by laser drilling a series of holes that are spaced from each other so that the groove has a fully segmented portion and a partially segmented portion.


REFERENCES:
patent: 3415672 (1968-12-01), Levinstein et al.
patent: 3489537 (1970-01-01), Cook
patent: 3849865 (1974-11-01), Gedwill et al.
patent: 3869779 (1975-03-01), Gedwill et al.
patent: 3955935 (1976-05-01), Shockley et al.
patent: 3978251 (1976-08-01), Stetson et al.
patent: 3979534 (1976-09-01), Rairden, III
patent: 3996021 (1976-12-01), Chang et al.
patent: 4005989 (1977-02-01), Preston
patent: 4080486 (1978-03-01), Walker et al.
patent: 4248940 (1981-02-01), Goward et al.
patent: 4298385 (1981-11-01), Claussen et al.
patent: 4321310 (1982-03-01), Ulion et al.
patent: 4321311 (1982-03-01), Strangman
patent: 4335190 (1982-06-01), Bill et al.
patent: 4374183 (1983-02-01), Deadmore et al.
patent: 4401697 (1983-08-01), Strangman
patent: 4405659 (1983-09-01), Strangman
patent: 4405660 (1983-09-01), Ulion et al.
patent: 4414249 (1983-11-01), Ulion et al.
patent: 4447503 (1984-05-01), Dardi et al.
patent: 4676994 (1987-06-01), Demaray
patent: 4880614 (1989-11-01), Strangman et al.
patent: 4916022 (1990-04-01), Solfest et al.
patent: 5015502 (1991-05-01), Strangman et al.
patent: 5059095 (1991-10-01), Kushner et al.
patent: 5073433 (1991-12-01), Taylor
patent: 5238752 (1993-08-01), Duderstadt et al.
patent: 5352540 (1994-10-01), Schienle et al.
patent: 5498484 (1996-03-01), Duderstadt
patent: 5562998 (1996-10-01), Strangman
patent: 5630314 (1997-05-01), Kojima et al.
patent: 0 609 795 A1 (1994-01-01), None
patent: 2 269 392 (1992-06-01), None
Article from Journal of Non-Crystalline Solids 147/148 (1992) Oct. 1, Amsterdam, NL entitled Corrosion resistant sol-gel ZrO2 coating on stainless steel by M. Atik and M.A. Aegerter.

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Laser segmented thick thermal barrier coatings for turbine... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Laser segmented thick thermal barrier coatings for turbine..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Laser segmented thick thermal barrier coatings for turbine... will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2454492

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.