Large forging manufacturing process

Metal treatment – Process of modifying or maintaining internal physical... – Heating or cooling of solid metal

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C148S410000, C148S428000, C148S676000

Reexamination Certificate

active

06409853

ABSTRACT:

BACKGROUND OF THE INVENTION
This invention relates to forgings used for large land-based gas turbines, and particularly to large Alloy 718 forgings that are prone to a problem known as abnormal grain growth.
The forging of Alloy 718 involves heating a billet and forging it in one or many steps (also referred to as upsets) to the final required shape. The billet must be reheated before each upset. After forging, the shaped parts are solution treated at a high temperature (1700-1825F), and then aged at a lower temperature (1325-1150F) to develop strength. Under certain process conditions, Alloy 718 forgings develop abnormal grain growth when heated to the solution temperature. This has not been a serious problem for small forgings (as discussed below), but it has been a serious problem for large forgings which, for purposes of this invention, are those over 10,000 pounds in weight.
Abnormal grain growth, also referred to as secondary grain growth or critical grain growth, occurs when a few grains in the material grow to a very large size compared to neighboring grains. This occurrence alters the mechanical properties of the material. Specifically, not only does abnormal grain growth reduce fatigue resistance and yield strength of the material, it also impairs the ability to detect small defects by ultrasonic testing. Abnormal grain growth does however, improve creep resistance at high temperatures, and may therefore be desirable in certain instances.
The possibility of developing abnormal grain growth in Alloy 718 forgings has been known for some time. A prior document which describes abnormal grain growth in Alloy 718 and conditions which promote abnormal grain growth is the “Study of Secondary Grain Growth on 781 Alloy” by J. F. Uginet and B. Pieraggi; The Minerals, Metals and Materials Society, 1997. Abnormal grain growth was not regarded as a serious problem in that process modifications were available that minimized or eliminated its occurrence. These process modifications, however, work well with small forgings but not with large forgings as defined above. More specifically, with small parts, one could:
1. Avoid low strains (amount of upsets in a forging step). There are some difficulties in doing this for large parts because the press capacity may allow only small upsets each time.
2. Use higher strain rates (related to the speed at which the top dies move). This again will not work for very large parts because the higher strain rates require higher press loads that would exceed the capacity of the largest presses in the world.
3. Avoid doing a solution treatment and do a direct age instead. This works out well for small parts because the cooling rate in air after completion of forging is adequate to ensure a fully solutioned structure for a small part. If air cooled after forging, the cooling rate at the center of very large parts will be very slow and will not have a fully solutioned structure. The absence of a fully solutioned structure means that the part will not develop high strength after the aging heat treatment. Therefore, after the solution treatment, the parts must be quenched in oil/water to retain a fully solutioned structure.
BRIEF SUMMARY OF THE INVENTION
This invention involves the identification of a unique processing window for large Alloy 718 forgings which causes abnormal grain growth. By then avoiding this window, abnormal grain growth can be eliminated, thereby permitting large forgings that have a uniform grain structure. Alternatively, the process permits the formation of abnormal grain growth in selected areas when considered desirable.
Initially, a study on the effect of forging parameters was carried out using small specimens, but the process was made to simulate the processing of large forgings. It was observed that abnormal grain growth occurs under specific conditions of:
(a) starting grain size;
(b) forging temperatures;
(c) forging strains;
(d) forging strain rates;
(e) number of upsets; and
(f) solution treatment temperature.
In one embodiment of this invention, abnormal grain growth can be avoided by a forging process which takes into account the above factors, within the parameters disclosed herein.
In an alternative embodiment of the invention, where there is a need to intentionally create abnormal grain growth in any areas of a forging, items (c) and (f) are altered, as also described further herein.
More specifically, the present invention relates generally to a process for forging large components of Alloy 718 material comprising:
a) providing a billet with an average grain size between ASTM 0 and ASTM 3;
b) heating the billet to a temperature of between 1750° F. and 1800° F.;
c) upsetting the billet to obtain a component part with a minimum strain of 0.125 in at least selected areas of the part;
d) reheating the component part to a temperature between 1750° F. and 1800° F.;
e) upsetting the component part to a final configuration such that the selected areas receive no strains between 0.01 and 0.125;
f) solution treating the component part at a temperature of between 1725° F. and 1750° F.; and
g) aging the component part over predetermined times at different temperatures.
When there is a need to intentionally create abnormal grain growth in any areas of a forging, then steps e) and f) are changed only as follows.
e) finish forge the part to intentionally create strains of 0.01 to 0.125 in the required areas.
f) solution treat the component part at 1825-1850° F.
The process in accordance with the invention has advantages over the prior art. Specifically, one can develop a control process which can eliminate abnormal grain growth and have a uniform grain structure specifically for large 718 alloy forgings. Alternatively, one can develop a control process which does produce abnormal grain growth intentionally in specific areas to meet specific property needs. This aspect can be used in both large and small forgings.


REFERENCES:
patent: 4793868 (1988-12-01), Chang
patent: 4957567 (1990-09-01), Kruegar et al.
patent: 5120373 (1992-06-01), Miller et al.
patent: 5360496 (1994-11-01), Kuhlman et al.
patent: 5374323 (1994-12-01), Kuhlman et al.
patent: 6193823 (2001-02-01), Morra
“Study of Secondary Grain Growth on 718 Alloy, ” JF Uginet et al., The Minerals, Metals & Materials Society, 1997, pp. 343-351.
“39thGE Turbine State-of-the-Art Technology Seminar”, Tab 1, ““F” Technology—the First Half-Million Operating Hours”, H.E. Miller, Aug. 1996.
“39th GE Turbine State-of-the-Art Technology Seminar”, Tab 2, “GE Heavy-Duty Gas Turbine Performance Characteristics”, F. J. Brooks, Aug. 1996.
“39th GE Turbine State-of-the-Art Technology Seminar”, Tab 3, “9EC 50Hz 170-MW Class Gas Turbine”, A. S. Arrao, Aug. 1996.
“39th GE Turbine State-of-the-Art Technology Seminar”, Tab 4, “MWS6001FA—An Advanced-Technology 70-MW Class 50/60 Hz Gas Turbine”, Ramachandran et al., Aug. 1996.
“39th GE Turbine State-of-the-Art Technology Seminar”, Tab 5, “Turbomachinery Technology Advances at Nuovo Pignone”, Benvenuti et al., Aug. 1996.
“39th GE Turbine State-of-the-Art Technology Seminar”, Tab 6, “GE Aeroderivative Gas Turbines—Design and Operating Features”, M.W. Horner, Aug. 1996.
“39th GE Turbine State-of-the-Art Technology Seminar”, Tab 7, “Advance Gas Turbine Materials and Coatings”, P.W. Schilke, Aug. 1996.
“39th GE Turbine State-of-the-Art Technology Seminar”, Tab 8, “Dry Low NOxCombustion Systems for GE Heavy-Duty Turbines”, L. B. Davis, Aug. 1996.
“39th GE Turbine State-of-the-Art Technology Seminar”, Tab 9, “GE Gas Turbine Combustion Flexibility”, M. A. Davi, Aug. 1996.
“39th GE Turbine State-of-the-Art Technology Seminar”, Tab 10, “Gas Fuel Clean-Up System Design Considerations fo GE Heavy-Duty Gas Turbines”, C. Wilkes, Aug. 1996.
“39th GE Turbine State-of-the-Art Technology Seminar”, Tab 11, “Integrated Control Systems for Advanced Combined Cycles”, Chu et al., Aug. 1996.
“39th GE Turbine State-of-the-Art Technology Seminar”, Tab 12, “Power Systems for the 21st Century “H” Gas Combined Cycles”, Paul et al., Aug. 1996.
“39th GE Turbine State-of-the-Art T

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Large forging manufacturing process does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Large forging manufacturing process, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Large forging manufacturing process will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2958771

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.