Large area bulk superconductors

Superconductor technology: apparatus – material – process – High temperature devices – systems – apparatus – com- ponents,... – Substrate for supporting superconductor

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C505S471000, C505S450000

Reexamination Certificate

active

06410487

ABSTRACT:

FIELD OF THE INVENTION
The present invention relates to a method of producing superconductors with greater thicknesses or bulk compared to thin film superconductors and more particularly to textured, large-area bulk superconductors identified as high temperature superconductors. The invention also relates to the superconductor components or products.
BACKGROUND OF THE INVENTION
Bulk superconductors have increased current carrying capacities and are useful in certain product areas where thin film superconductors lack the required performance. The method employed to produce the bulk superconductors is preferably carried out by producing a biaxially textured sheet of a metal or oxide and using this sheet as a large scale seed in combination with superconductor material in a melt process where the melted superconductor material becomes textured as it solidifies by cooling from the region next to the seed through the thickness or bulk.
U.S. Pat. No. 5,869,431 discloses suitable materials for seeds and for superconductors. In addition to methods disclosed in the '431 patent, some processes in the past have used several individual seeds (spaced apart) with superconductor materials in an attempt to obtain growth of large area bulk material with appropriate texturing. However, uniformity of texturing and melting of the small seeds have been problems.
In this invention, a biaxially textured sheet of oxide or metal is used as a one-piece seed of a size generally that of the desired superconductor component and placed in contact with superconducting material. The superconducting material is melted and then solidified by cooling with solidification starting from a region adjacent to the seed. By this technique, texturing is extended through the bulk of the superconductor with uniformity.
Two techniques for producing the biaxially textured sheet or oxide may be carried out. With a metal such as nickel, the sheet could be rolled and annealed similar to the treatment described for the nickel wire in U.S. patent application Ser. No. 09/568,890 filed May 11, 2000, the disclosure of which is incorporated by reference. Although the metal sheet may have the desired texturing, it may be necessary to add a buffer layer such as an oxide like those disclosed in the '431 patent or other oxides such as MgO to preserve the texturing during the subsequent melt stage. Another process is to form a textured surface of a metal oxide such as MgO by using an inclined substrate deposition (ISD). The ISD or inclined substrate deposition method is disclosed in copending U.S. patent application entitled Method for Preparing High Temperature Superconductor, serial no. 09/621,272 filed on even date herewith by Uthamalingam Balachandran and Michael P. Chudzik, the disclosure of which is incorporated herein in its entirety.
OBJECTS OF THE INVENTION
Accordingly, it is an object of the present invention to provide a bulk superconductor having a thickness of not less than about 100 microns carried by a polycrystalline textured substrate having misorientation angles at the surface thereof not greater than about 15°.
Another object of the invention is to provide a bulk superconductor having a thickness of not less than about 100 microns and a surface area of not less than about 50 cm
2
carried by a polycrystalline textured layer or sheet having a thickness not less than about 10 microns and misorientation angles at the surface thereof not greater than about 15°.
Still another object of the invention is to provide a process of manufacturing a bulk superconductor having a thickness not less than about 100 microns, comprising providing a polycrystalline biaxially textured layer or sheet material having a thickness not less than about 10 microns and misorientation angles at the surface thereof not greater than about 15°, and providing a superconductor precursor powder in contact with the polycrystalline biaxially textured substrate material and melting the precursor powders and thereafter cooling the melted powders to grow superconductor material using substantially the entire polycrystalline textured substrate material as a seed to provide a superconductor having a thickness not less than about 100 microns carried by a polycrystalline biaxially textured substrate material.
A final object of the invention is to provide a superconductor having a thickness not less than 100 microns produced by the inventive methods.
SUMMARY OF THE INVENTION
The invention consists of certain novel features and a combination of parts hereinafter fully described, illustrated in the accompanying drawings, and particularly pointed out in the appended claims, it being understood that various changes in the details may be made without departing from the spirit, or sacrificing any of the advantages of the present invention.


REFERENCES:
patent: 4939120 (1990-07-01), Moon et al.
patent: 4956336 (1990-09-01), Salama et al.
patent: 5231076 (1993-07-01), Jeong et al.
patent: 5278137 (1994-01-01), Morita et al.
patent: 5292716 (1994-03-01), Sakai et al.
patent: 5395820 (1995-03-01), Murakami et al.
patent: 5739086 (1998-04-01), Goyal et al.
patent: 5741377 (1998-04-01), Goyal et al.
patent: 5846912 (1998-12-01), Selvamanickam et al.
patent: 5898020 (1999-04-01), Goyal et al.
patent: 5964966 (1999-10-01), Goyal et al.
patent: 5968877 (1999-10-01), Budai et al.
patent: 6008162 (1999-12-01), Miura et al.
patent: 6106615 (2000-08-01), Goyal et al.
patent: 6114287 (2000-09-01), Lee et al.
patent: 6256521 (2001-07-01), Lee et al.
patent: 6296701 (2001-10-01), Christen et al.
Garcia-Gonzalez et al., “Microstructural analysis of YBa2Cu3Oy thin films deposited on SrTiO3 and LaAIO3 substrates by offzxis magnetron sputtering,” Jul. 1995, J. Appl. Phys. 78(1) p. 353-359.*
King et al., “A geometrical rationalization of the special properties of the 14 degree [001] grain boundary in YBa2Cu3O7-b,” Oct. 1993, J. Appl. Phys. 74(7), p. 4627-4630.*
Heinig et al. “Strong to weak coupling transition in low misorientation angle thin film YBa2Cu3O7-x bicrystals,” Jul. 1999, Phys. Rev. B V60, No. 2, p. 1409-1417.*
Dimos et al., “Superconducting transport properties of gran boundaries in YBa2Cu3O7 bicrystals,” Mar. 1990, Phys. Rev. B V41, No. 7, p. 4038-4049.*
Critical Current Densities in Superconducting Y-Ba-Cu-O . . . ; Japanese Journal of Applied Physics, vol. 28, No. 9, Sep. 1989, pp. L 1545-L1548.
Superconductivity of YBa2Cu3O1-X by Addition of Reactive Fine Powders, Sakai et al. Superconductivity Research Laboratory Oct. 15, 1990.
Processing of Large YBa2Cu3OxDomains For Levitation Applications by a Nd1+xBa2−xCu3Oy-Seeded Melt-Growth Technique, Journal of Electronic Materials, vol. 23, No., 11 1994.
Extremely Fine Precipitate and Flux Pinning in Melt-Processed YBa2Cu3OxPhysica C 213 (1993) 179-184.

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Large area bulk superconductors does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Large area bulk superconductors, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Large area bulk superconductors will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2900857

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.