ABSTRACT:

BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a joint body of a ceramic member and a metal member and a method of producing the same.
2. Description of Related Art
A method of directly connecting substrates made of aluminum nitride sintered body is known. For example, in Japanese Patent Laid-Open Publication No. 2-124778 (JP-A-2-124778), aluminum nitride substrates were heated to a temperature of 1800° C.-1900° C., and connected integrally by means of a diffusion connection. Moreover, in Japanese Patent Laid-Open Publication No. 8-13280 (JP-A-8-13280), an aluminum nitride joint body having a relatively high strength is disclosed.
Moreover, a method of brazing one nitride ceramic member to another nitride ceramic member is also known. For example, in Japanese Patent Laid-Open Publication No. 8-277171 (JP-A-8-277171), a joint body having a high anti-corrosive property with respect to halogen series corrosive gas such as CIF
3
and so on is obtained by connecting aluminum nitride members by using a brazing material consisting of aluminum, copper or nickel as a main ingredient and an active metal such as titanium as an additive. Such a brazing material is hard to corrode by halogen series corrosive gases and easily wets the surface of aluminum nitride.
However, when a cylindrical metal member is brazed to a flat or a plate-like ceramic member, the following problems were found. For example, in the field of semiconductor manufacturing, the present inventors tried to connect a ring-shaped support member made of KOVAR (Fe—Ni—Co alloy) to a rear surface of a suscepter for supporting a semiconductor wafer made of aluminum nitride sintered body. However, since the area of the suscepter becomes larger corresponding to an increase of silicon wafer diameter, it is extremely difficult to connect the ring-shaped support member to the suscepter under such a condition that they are correctly aligned. Particularly, when the rear surface of the suscepter is not sufficiently flat, or when the rear surface of the suscepter is not parallel, i.e., slightly aligned, to an end surface of the ring-shaped support member, the distance between the rear surface of the suscepter and the end surface of the ring-shaped support member is locally very small. Therefore, there is a tendency such that the thickness of the brazing layer between the suscepter and the ring-shaped support member becomes smaller. In this manner, if the thickness of the brazing layer between the rear surface of the suscepter and the end surface of the ring-shaped support member becomes locally thin, a thermal strain generated between the suscepter and the ring-shaped support member cannot be absorbed, so that it causes local crack generation.
Moreover, when the ring-shaped support member is an iron based metal, such as KOVAR, stainless steel and so on, a reaction layer such as an intermetallic compound is precipitated due to a reaction between the brazing member and the ring-shaped support member, and the durability and the hardness of the brazing member are increased. As a result, the remaining stress generated in the suscepter and the ring-shaped support member becomes larger.
SUMMARY OF THE INVENTION
An object of the invention is to provide a joint body of a ceramic member and a cylindrical metal member in which a metal connection portion having a predetermined thickness along all connection regions between an end portion of the metal member and the ceramic member can be formed. Moreover, an object is also to prevent the deterioration of a portion of the metal connection portion which is particularly contacted to the ceramic member and to prevent an increase of a durability or a hardness of the metal connection portion.
Further, another object of the invention is to provide a joint body of a ceramic member and a cylindrical metal member, which is strong for a heat cycle and is hardly to generate a local crack.
According to the invention, a joint body of a ceramic member and a cylindrical metal member, comprises a structure such that:
(1) an end portion of the metal member and the ceramic member are connected via a metal connection portion;
(2) the metal connection portion has a metallized layer formed on the ceramic member and a brazing connection portion interposing at least between the metallized layer and an end portion of the metal member; and
(3) a melt point of a brazing member constructing the brazing connection portion is lower than that of a brazing member constructing the metallized layer.
The inventors thought a method of forming at first a metallized layer on the ceramic member, interposing a brazing member for connection between the metallized layer and an end portion of the metal member, melting the brazing member for connection at a temperature lower than a melt point of a brazing member for metallizing, generating a brazing connection portion at least between the metallized layer and an end portion of the metal member. In the joint body thus obtained, when an end portion of the metal member and a connection surface of the ceramic member are inclined with respect to predetermined relative positions, or even when the distance between the ceramic member and the metal member becomes locally small during brazing (since the flatness of an end portion of the metal member and the flatness of the connection surface of the ceramic member are low), it is possible to keep the metal connection portion having a predetermined thickness by means of the metallized layer.
Further, since the melt point of the brazing connection portion is low, it is possible to prevent the reaction of the metallized layer and the metal member, and to suppress the increase of the durability or the hardness of the metallized layer after connection.
Moreover, in the present invention, since a metal plate made of a low durability metal or a low thermal expansion metal is interposed between the end portion of the cylindrical metal member and the connection surface of the ceramic member, it is possible to obtain a metal connection portion having a predetermined thickness along all the connection regions.


REFERENCES:
patent: 4624897 (1986-11-01), Ito
patent: 4634638 (1987-01-01), Ainsalie et al.
patent: 5043229 (1991-08-01), Mizuhara
patent: 2-124778 (1990-05-01), None
patent: 8-13280 (1996-01-01), None
patent: 8-277171 (1996-10-01), None

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Joint body of ceramic member and metal member and method of... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Joint body of ceramic member and metal member and method of..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Joint body of ceramic member and metal member and method of... will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2973332

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.