Active solid-state devices (e.g. – transistors – solid-state diode – Heterojunction device – Between different group iv-vi or ii-vi or iii-v compounds...
Reexamination Certificate
2001-04-24
2004-11-09
Jackson, Jerome (Department: 2815)
Active solid-state devices (e.g., transistors, solid-state diode
Heterojunction device
Between different group iv-vi or ii-vi or iii-v compounds...
C257S184000, C257S103000, C136S249000, C136S262000
Reexamination Certificate
active
06815736
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention is related generally to formulation and fabrication of doped semiconductor materials and more specifically to isoelectronic co-doping of semiconductor materials.
2. Description of the State of the Art
It is conventional to formulate and fabricate semiconductor materials by doping crystal lattice materials whereby a small amount of an element belonging to one column on the periodic table of the elements, i.e., one number of conduction or outer shell electrons, is replaced with a small amount of material from a different column or group on the periodic table, i.e., a different number of conduction or outer shell electrons, usually one column or group removed, i.e., one more or one fewer outer shell electrons. For example, silicon (a group IV material) is often doped with a small amount of boron (a group III material) to make electronic devices. It is also conventional to use various alloys to form the semiconductor material, i.e., substitutions on lattice sites by elements from the same group in the periodic table, to obtain whatever semiconductor characteristics are needed or desired, such as band gap, crystal lattice constant, mobility, and the like. Solar cells and light emitting semiconductors are usually made with semiconductor materials that have direct bandgaps (i.e., no change in momentum is required for an electron to cross the bandgap between the valence and the conduction energy bands). There have been, and still are, a number of attempts to fabricate solar cells, photodiodes, and light emitting semiconductors using silicon, which is an indirect bandgap material, to open the possibility of combining the benefits of silicon integrated circuits with the energy and communications capabilities of light, but such efforts have seen only limited success.
In the solar cell realm, there are many efforts to obtain a semiconductor material with a bandgap close to 1.0 eV and that is compatible with, i.e., lattice matched to, other semiconductor materials with higher and lower bandgaps to form an integral component of a monolithic quadruple junction solar cell. For example, it is known from mathematical modeling that, for optimum energy absorption from the solar spectrum using four discrete solar cells, the four discrete cells should have bandgaps in the sequence of 1.9 eV, 1.42 eV, 1.05 eV, and 0.67 eV, respectively. Such a monolithic, four-junction, 1.9 eV/1.42 eV/1.05 eV/0.67 eV solar cell structure could attain solar energy conversion efficiency of forty percent (40%) AM1. As mentioned above, solar cells are usually made of group III and group V semiconductor materials, such as gallium (Ga) and arsenic (As), which have direct bandgaps that facilitate absorption and conversion of light energy to electricity and because GaAs wafers for use as lattice matched substrates are readily available. Such group III and group V semiconductor materials with bandgaps at or near the 1.9 eV and 1.42 eV levels with good electric device qualities have been available for some time, e.g., InGaP (1.90 eV) and GaAs (1.42 eV). Germanium (Ge) with a bandgap of 0.67 eV, while it is a group IV material, can never-the-less be used for the substrate part of a monolithic, quadruple junction solar cell, because the substrate can be made thick enough to absorb light energy in spite of the indirect bandgap.
However, making a light absorbent, semiconductor material for the 1.05 eV bandgap cell has been an elusive goal. While 1.05 eV bandgap materials can be made, there have not been any suitable 1.05 eV bandgap materials that have acceptable carrier mobilities and other electronic properties and that can be lattice-matched to the other semiconductor materials for the other cell junctions, as discussed above, such as GaAs and Ge.
Among the semiconductor materials systems that have been investigate for a suitable 1.05 eV cell layer is GaInNAs. The interest in this system was sparked initially y the surprising observation by Weyers et al,
Jpn. J. Appl. Physics
31(1992) pp. L853, that the dilute alloy GaAs
1-x
N
x
has a giant conduction band bowing, Neugebauer, et al,
Phys. Rev. B
. 51(1995) pp. 10568, and then by the demonstration by Kondow et al., in 1996 that the quaternary alloy Ga
0.92
In
0.08
N
0.03
As
0.97
could be grown lattice matched to GaAs with a b gap of 1.0 eV
J Cryst. Growth
164 (1996) pp. 175. The 8% In was used by Kondow et al., al ng with the Ga, As, and N, to achieve lattice matching with a GaAs substrate. However, the photoluminescense of Ga
0.92
In
0.08
N
0.03
As
0.97
is poor. In spite of dilute GaAs
1-x
N
x
having the desired 1.0 eV bandgap and the ability to lattice match it to GaAs by the addition of In to the alloy, the very poor electron mobilities in such dilute GaAs
1-x
N
x
based alloys has inhibited an further significant progress toward using such an alloy in a photoelectric device, such a monolithic, quadruple junction, solar cell.
SUMMARY OF THE INVENTION
Accordingly, a specific object of this invention is to modify a dilute GaAs
1-x
N
x
alloy in a manner that not only maintains a bandgap close to 1.05 eV and is lattice matched to GaAs, but also that increases the electronic device quality of the alloy enough to make it not only useful, but also beneficial, as a solar cell semiconductor material.
A more general object of this invention is to expand the repertoire for available choices of semiconductor compounds and alloys that have bandgap/lattice constant paired values suited for expitaxial growth of device structures that implement design principles closest to the ideal.
Another specific object of this invention is to tailor semiconductor materials, such as GaP, to have bandgaps that are close to optimum solar radiation absorption for two junction and three junction tandem solar cells while also being lattice matched to silicon substrates.
Another specific object of this invention is to fabricate and tailor semiconductor materials for active layers of LED's and laser diodes with bandgaps that produce light in wavelengths that are particularly suitable for fiber optic transmission, such as 1.55 &mgr;m or 1.3 &mgr;m and which are lattice matched to common semiconductor substrate materials, such as Si or GaAs.
A further specific object of this invention is to fabricate and tailor semiconductor materials for LED's or laser diodes to have bandgaps that produce certain specific colors of light in the red and near infra-red wavelength regions and that are lattice matched to common semiconductor substrate materials, such as Si, GaAs, and GaP.
Yet another object of this invention is to fabricate and tailor semiconductor materials with bandgaps that absorb infrared radiation to produce electricity and that are lattice matched to desired substrate materials, such as InP.
Additional objects, advantages, and novel features of the invention are set forth in part in the description that follows and will become apparent to those skilled in the art upon examination of the following description and figures or may be learned by practicing the invention. Further, the objects and the advantages of the invention may be realized and attained by means of the instrumentalities and in combinations particularly pointed out in the appended claims.
To achieve the foregoing and other objects and in accordance with the purposes of the present invention, as embodied and broadly described herein, a method of this invention may comprise modifying a semiconductor compound or alloy comprising host atoms in a crystal lattice to have a lower bandgap than the bandgap of the semiconductor compound or alloy prior to such modification. Such bandgap lowering can be achieved by isoelectronically co-doping the semiconductor compound or alloy with a first isoelectronic dopant comprising atoms that form isoelectronic traps in the host crystal lattice, which behave as deep acceptors, and with a second isoelectronic dopant comprising atoms that form isoelectronic traps in the host crystal lattice, which behave as deep donors. For
Jackson Jerome
Midwest Research Institute
White Paul J.
LandOfFree
Isoelectronic co-doping does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Isoelectronic co-doping, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Isoelectronic co-doping will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3288089