ABSTRACT:
BACKGROUND OF THE INVENTION
Marine propellers, particularly those used for high performance marine engines, are usually formed of stainless steel. The traditional method of producing a stainless steel propeller is to cast the propeller by a conventional lost wax casting procedure using a 15-5 stainless steel which contains approximately 15% chromium and 5% nickel. After casting, the outer diameter of the propeller hub is machined, and the outer surface of the propeller is then ground to eliminate any pin holes or microporosity. Following the grinding, the propeller is then polished to a high luster. If the cast propeller contains larger casting defects, such as gas holes, it is necessary to repair the larger defects through welding and the welded areas are then ground before the propeller is polished to its final condition.
The grinding and welding operations require considerable time and labor and, therefore, constitute a substantial portion of the overall cost of the stainless steel propeller.
SUMMARY OF THE INVENTION
The invention is based on the discovery that by employing a stainless steel containing in excess of 1% silicon, and preferably a silicon content in the range of 1.0% to 1.5% by weight, pin hole and porosity casting defects can be considerably reduced, thereby reducing the time and labor required in the welding, grinding and polishing operations for the propeller.
In general, pin holes and the larger defect form, gas porosity, traditionally result from the carbon dissolved in the metal reacting with oxygen either dissolved in the metal or blown into the metal. The resulting carbon dioxide gas is trapped under the solidified skin and is visible as gas porosity. For low carbon ferrous alloys, like 15-5 pH, stainless steel, that are well deoxidized inherently by their high levels of chromium, pin holes and gas porosity are not expected to be a problem. However, in an investment or lost wax casting process in which the molten stainless steel is fed into a silica mold or shell, metal/mold reactions can occur that result in gas porosity and thereby increase the manufacturing cost of primary and secondary cleaning operations and/or that can compromise the quality of the cast metal. This invention specifically addresses the pin hole and porosity problem that occurs in the near surface regions (e.g. approximately 0.050 inches below the surface) of investment cast martensitic and of martensitic precipitation hardened stainless steel that use a silica shell. Porosity can be eliminated by deep grinding or by changing the shell system to alumina shells, but both of these solutions have an adverse economic impact on the overall process. Instead it has been unexpectedly found that by raising the silicon level of the stainless steel about 50%, from under 0.8% by weight in the conventional practice, to 1.2% and above, the reaction between the molten steel and the silica shell substantially stops or is dramatically reduced, and thus the more economical process of light grinding of propellers can be used.
It is believed that the increased silicon dissolved in the molten steel thermodynamically lowers the driving force for the silica shell from reacting with the molten metal, much like the mechanism in die casting where dissolving iron in a molten aluminum alloy decreases “die sticking” or the tendency of the steel die from reacting with an iron-free aluminum alloy.
The increased silicon content also increases the fluidity of the alloy during casting, resulting in a reduction in non-fill defects, as well as a reduction in cold lap defects in the cast article.
The increased silicon content also reduces the hardness of the cast article, which correspondingly facilitates the grinding operation on the cast propeller.
Other features, objects and advantages will appear in the course following description.
DESCRIPTION OF THE PREFERRED EMBODIMENT
The invention is directed to a cast stainless steel article, such as a marine propeller, having reduced casting defects and improved mechanical properties. The stainless steel to be used is a variation of a conventional 15-5 stainless steel (15% chromium, 5% nickel) containing in excess of 1% silicon and preferably from 1.0% to 1.5% by weight of silicon.
In general, the stainless steel has the following composition in weight percent:
Chromium
14.5% to 15.2%
Nickel
5.35% to 6.05%
Silicon
1.0% to 1.5%
Copper
2.8% to 3.5%
Niobium
0.15% to 0.45%
Tantalum
0.15% to 0.45%
Carbon
0.05% max
Sulfur
0.025% max
Iron
Balance
The marine propeller is cast using a conventional investment or lost wax casting procedure to obtain close tolerances. In a lost wax casting procedure, a pattern is initially formed of wax having a shape and size identical to the propeller to be ultimrately cast. The wax pattern is then dipped or otherwise coated with a thin aqueous slurry of silica, and the slurry is subsequently dried to provide a thin dry silica coating on the wax pattern. Several additional silica coats are applied in the same manner to produce an outer silica shell on the wax pattern. The resulting composite structure is then heated, preferably in an autoclave, to melt the wax, leaving a hollow silica shell into which the molten stainless steel is fed to produce a cast article identical in size and shape to the original wax pattern.
In the past when casting propellers using a conventional 15-5 stainless steel, the cast article may contain some surface and sub-surface defects, such as microporosity or pinholes, which are removed from the pattern by grinding. Quite often the cast propeller will also include larger defects, such as gas holes or voids, which require repair by welding. The welded areas must be subsequently ground and polished. The after-casting procedures, such as welding, grinding and polishing, require substantial time and labor which contribute greatly to the overall cost of the propeller.
It has unexpectedly been found that by increasing the silicon content of the stainless steel to a value in excess of 1.0% by weight, reaction between the silica mold and the molten stainless steel is favorably controlled and, as a result, the surface and sub-surface defects of the casting are reduced. It is believed that the increased silicon in the molten stainless steel thermodynamically reduces the driving force for the silica shell from reacting with the molten metal, thus reducing gas-formed defects. By reducing the defects, such as pinholes, gas holes and the like, the amount of labor required for grinding of the propeller is correspondingly reduced. Further, the increased silicon content also increases the fluidity of the stainless steel during casting. The increased fluidity serves to reduce non-fill defects in the casting, as well as cold-lap defects. Non-fill defects are areas of the casting which are not properly filled with the molten metal, while cold-lap defects are areas where two molten metal fronts met but did not properly fuse.
REFERENCES:
patent: 3661658 (1972-05-01), Oda et al.
patent: 3915756 (1975-10-01), Oda et al.
patent: 3925064 (1975-12-01), Takamura et al.
patent: 4975041 (1990-12-01), Fries et al.
patent: 4981167 (1991-01-01), Anderson
patent: 5089067 (1992-02-01), Schumacher
patent: 60-029451 (1985-02-01), None
Anderson Kevin R.
Bauer Richard S.
Cleary Terrance M.
Donahue Raymond J.
Riutta Barry L.
Andrus Sceales Starke & Sawall LLP
Brunswick Corporation
Elve M. Alexandra
Kerns Kevin P.
LandOfFree
Investment cast stainless steel marine propeller does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Investment cast stainless steel marine propeller, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Investment cast stainless steel marine propeller will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2940349